Water turbine blade modified epoxy resin multi-coating anti-corrosion anti-abrasion method

An epoxy resin, multi-coating technology, applied in the field of materials, can solve problems such as material damage of hydraulic turbine impellers, and achieve the effects of high bonding performance, high flexibility, and improved compatibility

Inactive Publication Date: 2017-05-31
WUXI MINGSHENG TEXTILE MACHINERY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, in the hydropower stations in Central South and East China, although the water turbine components suffer from little sand wear and loss due to the low sand content of the river, the cavitation phenomenon of water flow can seriously damage the material of the water turbine impeller in deep water.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water turbine blade modified epoxy resin multi-coating anti-corrosion anti-abrasion method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A method for preventing corrosion and abrasion of water turbine blades, comprising:

[0032] (1) Carry out sandblasting roughening on blade surface;

[0033] (2) cleaning the roughened blade surface with acetone and ethanol and drying;

[0034] (3) according to the proportioning of hard graphene fiber 2wt% and hydroxyl-terminated liquid rubber-modified epoxy resin surplus, make slurry and mix homogeneously;

[0035] (4) the slurry is uniformly applied on the surface of the blade, and dried at 90° C. to obtain a wear-resistant and corrosion-resistant coating of hydroxyl-terminated liquid rubber-modified epoxy resin doped with graphene fibers cladding on the surface of the blade;

[0036] (5) According to the proportion of hard WC ceramic particles accounting for 20wt%, high-density polyethylene fiber 2wt%, and hydroxyl-terminated liquid rubber-modified epoxy resin balance, make a slurry and mix it uniformly;

[0037] (6) Apply the slurry evenly on the surface of the hy...

Embodiment 2

[0039] A method for preventing corrosion and abrasion of water turbine blades, comprising:

[0040] (1) Carry out sandblasting roughening on blade surface;

[0041] (2) cleaning the roughened blade surface with acetone and ethanol and drying;

[0042] (3) according to the proportioning of hard graphene fiber 10wt% and hydroxyl-terminated liquid rubber modified epoxy resin surplus, make slurry and mix homogeneously;

[0043] (4) Apply the slurry evenly on the surface of the blade and dry at 130° C. to obtain a wear-resistant and corrosion-resistant coating of hydroxyl-terminated liquid rubber-modified epoxy resin doped with graphene fibers cladding on the surface of the blade;

[0044] (5) According to the ratio of 65wt% of hard WC ceramic particles, 10wt% of high-density polyethylene fiber and the remainder of hydroxyl-terminated liquid rubber modified epoxy resin, slurry is made and mixed uniformly;

[0045] (6) Apply the slurry evenly on the surface of the hydroxyl-termina...

Embodiment 3

[0047] A method for preventing corrosion and abrasion of water turbine blades, comprising:

[0048] (1) Carry out sandblasting roughening on blade surface;

[0049] (2) cleaning the roughened blade surface with acetone and ethanol and drying;

[0050] (3) according to the proportioning of hard graphene fiber 5wt% and hydroxyl-terminated liquid rubber modified epoxy resin surplus, make slurry and mix homogeneously;

[0051] (4) Apply the slurry evenly on the surface of the blade and dry at 100° C. to obtain a wear-resistant and corrosion-resistant coating of hydroxyl-terminated liquid rubber-modified epoxy resin doped with graphene fibers cladding on the surface of the blade;

[0052](5) According to the proportion of hard WC ceramic particles accounting for 50wt%, high-density polyethylene fiber 5wt%, and hydroxyl-terminated liquid rubber-modified epoxy resin balance, make slurry and mix uniformly;

[0053] (6) Apply the slurry evenly on the surface of the hydroxyl-terminate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water turbine blade modified epoxy resin anti-corrosion anti-abrasion method, which comprises the following steps of (1) performing sand-blasting roughening on the surface of a blade; (2) cleaning and roughening the surface of the blade by acetone and ethyl alcohol; performing drying; (3) preparing the materials into slurry according to the proportion ratio of 2 to 10 weight percent of hard graphene fiber and the balance hydroxy-terminated liquid rubber modified epoxy resin; uniformly mixing the materials; (4) uniformly smearing the slurry onto the surface of the blade; obtaining a graphene fiber doping hydroxy-terminated liquid rubber modified epoxy resin wear-resistant and anti-corrosion coating molten covering on the blade surface; (5) preparing the materials into slurry according to the proportioning ratio of hard WC ceramic particles, high-density polyethylene fiber and hydroxy-terminated liquid rubber modified epoxy resin; uniformly mixing the raw materials; (6) uniformly smearing the slurry onto the surface of the graphene fiber doping hydroxy-terminated liquid rubber modified epoxy resin wear-resistant and anti-corrosion coating to obtain the multi-coating anti-corrosion layer. Through the trail use for one month in sand river, no obvious ablation and corrosion marks are found.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to a multi-coating anti-corrosion and anti-abrasion method of water turbine blade modified epoxy resin. Background technique [0002] Wear and tear is common in many industries such as water conservancy, hydropower, machinery, textile and metallurgy, and it is very serious, and the economic loss caused thereby is quite visible. my country's expenditure in this area is very large, especially in the water conservancy and hydropower sectors. This is because my country's rivers have a high sediment content, and there are 115 rivers that transport more than 10 million tons of sand each year, ranking first in the world. Relevant statistical data in 2001 showed that the total installed capacity of hydropower stations nationwide was 80.05GW, and the total power generation was 218.45 billion kW / h, of which 105.6 billion kW h was located in areas with high sediment concentration in rivers ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D115/00C09D123/06C09D5/08C09D7/12
CPCC09D163/00C08L2203/16C08L2205/03C08L2207/062C09D5/08C09D7/61C09D7/65C09D7/70C08L15/00C08K7/06C08L23/06C08K3/16
Inventor 张达明
Owner WUXI MINGSHENG TEXTILE MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com