Flame-retardant resin composition, adhesive and laminated busbar insulating adhesive film prepared from same, and preparation method for insulating adhesive film

A flame-retardant resin and insulating film technology, applied in adhesives, insulators, adhesive additives, etc., can solve problems such as failure to meet the application requirements of working temperature laminated busbars, high-temperature bonding strength reduction, etc., and achieve excellent high-temperature peeling Effects of strength, heat resistance improvement, and compatibility improvement

Inactive Publication Date: 2017-05-31
GUANGDONG SHENGYI SCI TECH
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this modified saturated polyester adhesive can only be used for laminated busbars with an operating temperature of 105°C. As the temperature rises, the high-temperature bonding strength of the saturated polyester adhesive decreases rapidly, which cannot meet the requirements for higher operating temperature lamination. Application requirements for busbars

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant resin composition, adhesive and laminated busbar insulating adhesive film prepared from same, and preparation method for insulating adhesive film
  • Flame-retardant resin composition, adhesive and laminated busbar insulating adhesive film prepared from same, and preparation method for insulating adhesive film
  • Flame-retardant resin composition, adhesive and laminated busbar insulating adhesive film prepared from same, and preparation method for insulating adhesive film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A flame retardant resin composition, comprising 110 parts of saturated polyester resin (ES600) calculated in parts by mass, 15 parts of polyester polyurethane resin, 8 parts of aliphatic isocyanate curing agent, 10 parts of antimony trioxide, bromine 20 parts of styrene, 10 parts of magnesium hydroxide, 0.2 parts of antioxidant (1010), 0.08 parts of coupling agent (KH570).

[0033] The flame-retardant resin composition is applied to the laminated busbar insulation adhesive film.

[0034] The preparation method of the laminated busbar insulating adhesive film containing the flame-retardant resin composition: first use cyclohexanone to adjust the composition of the saturated polyester resin, polyester polyurethane resin, aliphatic isocyanate curing agent, antimony trioxide, A liquid dispersion (solid content 35%) composed of brominated styrene, magnesium hydroxide, antioxidant, and coupling agent is mixed to make a flame-retardant adhesive.

[0035] like figure 1 As sh...

Embodiment 2

[0039] A flame retardant resin composition, comprising 50 parts of saturated polyester resin (L952) calculated in parts by mass, 25 parts of polyether polyurethane resin, 12 parts of aromatic isocyanate curing agent, 40 parts of antimony pentoxide, ten parts 100 parts of brominated diphenylethane, 0.1 part of antioxidant (168), 0.1 part of coupling agent (KH172).

[0040] The flame-retardant resin composition is applied to the laminated busbar insulation adhesive film.

[0041] The preparation method of the laminated busbar insulating adhesive film containing the flame-retardant resin composition: first use acetone to adjust the composition of the saturated polyester resin, polyether polyurethane resin, aromatic isocyanate curing agent, antimony pentoxide, decabromine A liquid dispersion (solid content 45%) composed of diphenylethane, antioxidant and coupling agent is mixed to make a flame-retardant adhesive.

[0042] like figure 2 As shown, the flame-retardant adhesive is ...

Embodiment 3

[0046] A flame retardant resin composition, comprising 75 parts by mass of saturated polyester resin, 38 parts of polyether polyurethane resin, 18 parts of alicyclic isocyanate curing agent, 50 parts of antimony trioxide, ethylene bismuth 120 parts of tetrabromophthalimide, 8 parts of aluminum hydroxide, 0.1 part of antioxidant (168), 0.1 part of coupling agent (TMC-201).

[0047] The flame retardant resin composition is used for laminated busbar insulation film.

[0048] The preparation method of the laminated busbar insulating adhesive film containing the flame-retardant resin composition: first use methyl ethyl ketone to adjust the composition of the saturated polyester resin, polyether polyurethane resin, alicyclic isocyanate curing agent, antimony trioxide, A liquid dispersion (solid content: 40%) composed of ethylene bis-tetrabromophthalimide, aluminum hydroxide, antioxidant, and coupling agent is mixed to make a flame-retardant adhesive.

[0049] Then use a coating mac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention provides a flame-retardant resin composition, which comprises the following components in parts by mass: 50 to 110 parts of a saturated polyester resin, 15 to 40 parts of a polyurethane resin, 5 to 20 parts of a curing agent, 30 to 200 parts of a flame retardant, 0.01 to 1 part of an antioxidant and 0.01 to 5 parts of a coupling agent. A small amount of polyurethane resin is added into the flame-retardant resin composition, and then carboxy groups can be introduced into the flame-retardant resin composition to increase functional groups capable of performing a crosslinking reaction with the curing agent in the flame-retardant resin composition and improve the crosslinking density of the flame-retardant resin composition, so that the heat resistance of the flame-retardant resin composition is improved. Moreover, the carboxy groups in the polyurethane resin and hydroxyl groups in the saturated polyester resin can both perform a crosslinking reaction with the curing agent, and an interpenetrating polymer network can be formed after curing, so that the compatibility of the polyurethane resin and the saturated polyester resin is improved. The invention also provides an adhesive and laminated busbar insulating adhesive film prepared from the flame-retardant resin composition, and a preparation method for the laminated busbar insulating adhesive film.

Description

technical field [0001] The invention relates to the field of laminated busbar insulating adhesive films, in particular to a flame-retardant resin composition and an adhesive prepared therefrom, a laminated busbar insulating adhesive film, and a method for preparing the insulating adhesive film. Background technique [0002] Laminated busbars are also called composite busbars, composite busbars, laminated busbars, composite copper bars, low-inductance busbars, etc., and their English name is called Laminatd Busbar. As a connection bar with a multi-level composite structure, the laminated busbar can be regarded as the expressway of the power distribution system. Compared with the traditional complex, bulky, time-consuming and labor-intensive wiring methods, laminated busbars can provide a high-tech and easy-to-design power distribution system with a clear structure. It has the characteristics of repeatable electrical performance, low inductive impedance, strong anti-interfere...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/00C08L75/06C08L75/08C08L63/00C08K13/02C08K5/03C08K5/136C08K5/02C08K3/22C08K5/3415C09J167/00C09J175/06C09J175/08C09J11/06C09J11/04C09J11/08C09J7/02H01B17/62
CPCC08L67/00C08L2201/02C08L2201/08C08L2203/20C08L2205/03C09J7/22C09J7/30C09J11/04C09J11/06C09J11/08C09J167/00C09J2203/326C09J2301/122C09J2301/30C09J2301/408H01B17/62C08L75/06C08K13/02C08K3/2279C08K5/03C08K2003/2224C08L75/08C08K5/3415C08K2003/2227
Inventor 左陈茹敬宏伍宏奎蒋媚媚
Owner GUANGDONG SHENGYI SCI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com