A kind of p-type crmcuo amorphous oxide semiconductor thin film and preparation method thereof

A technology of amorphous oxide and amorphous thin film, which is applied in semiconductor/solid-state device manufacturing, semiconductor devices, transistors, etc., to achieve the effect of large-area deposition, good material properties, and low cost

Active Publication Date: 2020-01-17
ZHEJIANG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the currently reported AOS TFTs are all n-type channel, lack of p-type channel AOS TFT, which greatly restricts the application of AOS TFT in new generation display, transparent electronics and many other fields.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) with high purity Cr 2 o 3 , MgO and Cu 2 O powder is used as the raw material, mixed, ground, and sintered in an Ar atmosphere at 1150°C to make CrMgCuO ceramic sheets as the target, where the atomic ratio of Cr, Mg, and Cu is 2:1:0.8;

[0026] (2) Using the radio frequency magnetron sputtering method, install the substrate and target in the sputtering reaction chamber, and evacuate to a vacuum degree of 9×10 -4 Pa;

[0027] (3) Passing Ar-O 2 For the working gas, gas pressure 2Pa, Ar-O 2 The flow volume ratio is 10:2, the sputtering power is 140W, and the substrate temperature is 200°C. 2 Under the bombardment of ions, the atoms and molecules on the surface of the target are sputtered out, and a thin film is deposited on the substrate. 2 Naturally cooled to room temperature under atmosphere to obtain p-type Cr 2 MgCu 0.8 o 4.4 Amorphous thin film.

[0028] Using quartz as the substrate, p-type Cr was prepared according to the above growth steps 2 MgCu 0...

Embodiment 2

[0030] (1) with high purity Cr 2 o 3 , MgO and Cu 2 O powder is used as the raw material, mixed, ground, and sintered in an Ar atmosphere at 1150°C to make CrMgCuO ceramic sheets as the target, where the atomic ratio of Cr, Mg, and Cu is 2:1:1;

[0031] (2) Using the radio frequency magnetron sputtering method, install the substrate and target in the sputtering reaction chamber, and evacuate to a vacuum degree of 9×10 -4 Pa;

[0032] (3) Passing Ar-O 2 For the working gas, the gas pressure is 3Pa, Ar-O 2 The flow volume ratio is 10:1, the sputtering power is 140W, and the substrate temperature is 300°C. 2 Under the bombardment of ions, the atoms and molecules on the surface of the target are sputtered out and deposited on the substrate to form a thin film.2 Naturally cooled to room temperature under atmosphere to obtain p-type Cr 2 MgCuO 4.5 Amorphous thin film.

[0033] Using quartz as the substrate, p-type Cr was prepared according to the above growth steps 2 MgCuO ...

Embodiment 3

[0035] (1) with high purity Cr 2 o 3 , MgO and Cu 2 O powder is used as the raw material, mixed, ground, and sintered in an Ar atmosphere at 1150°C to make CrMgCuO ceramic sheets as the target material, in which the atomic ratio of Cr, Mg, and Cu is 2:1:1.2;

[0036] (2) Using the radio frequency magnetron sputtering method, install the substrate and target in the sputtering reaction chamber, and evacuate to a vacuum degree of 9×10 -4 Pa;

[0037] (3) Passing Ar-O 2 For the working gas, the gas pressure is 4Pa, Ar-O 2 The flow volume ratio is 10:2, the sputtering power is 150W, and the substrate temperature is 400°C. 2 Under the bombardment of ions, the atoms and molecules on the surface of the target are sputtered out, and a thin film is deposited on the substrate. 2 Naturally cooled to room temperature under atmosphere to obtain p-type Cr 2 MgCu 1.2 o 4.6 Amorphous thin film.

[0038] Using quartz as the substrate, p-type Cr was prepared according to the above grow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a p-type amorphous oxide semiconductor thin film. The p-type amorphous oxide semiconductor thin film is CrMCuO, and the thin film is amorphous and has p-type conductivity, wherein Cr is of +3 valence; M is one of Zn, Mg and Mn elements and is of +2 valence, and Cr and M are jointly combined with O to form a p-type conductive matrix of the CrMcuO thin film; Cu is of +1 valence, Cu, Cr and M co-act to form spatial network structures, and the spatial network structures are connected with each other in an amorphous state to achieve the effect of a hole transport channel. The invention further provides a preparation method of the p-type CrMgCuO amorphous oxide semiconductor thin film. The p-type CrMgCuO amorphous thin film is prepared by using a CrMgCuO ceramic chip as the target, adopting a radio-frequency magnetron sputtering method and using Ar-O2 as a working gas. The prepared thin film can be used for p-type amorphous thin film transistor.

Description

technical field [0001] The invention relates to an amorphous oxide semiconductor thin film, in particular to a p-type amorphous oxide semiconductor thin film and a preparation method thereof. Background technique [0002] Thin film transistor (TFT) is one of the core technologies in the field of microelectronics, especially display engineering. At present, TFT is mainly based on amorphous silicon (a-Si) technology, but a-Si TFT is opaque, has strong photosensitivity, and needs to add a mask layer. The pixel aperture ratio of the display screen is low, which limits the display performance. And the mobility of a-Si is low (~2 cm 2 / Vs), cannot meet some application requirements. Although TFT based on polysilicon (p-Si) technology has high mobility, its device uniformity is poor and its fabrication cost is high, which limits its application. In addition, organic semiconductor thin-film transistors (OTFT) have also been studied a lot, but the stability of OTFT is not high, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01L29/24H01L21/02H01L29/786H01L29/10
CPCH01L21/02631H01L29/1025H01L29/247H01L29/78693
Inventor 吕建国岳士录叶志镇
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap