Edible oil high-temperature swelling-resistant modified polypropylene material applied to household appliances and preparation method thereof

A polypropylene material and edible oil technology, which is applied in the field of polymer materials, can solve problems such as difficult cleaning and swelling of edible oil, and achieve the effects of low oil absorption rate, easy molding, and simple processing procedures

Inactive Publication Date: 2017-05-10
GUANGDONG ALDEX NEW MATERIAL CO LTD
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The polarity of edible oil and PP material is similar, so it is difficult to clean at room temperature, and the surface temperature can reach as high as 80-100°C under the working condition of household appliances, which can easily cause swelling of edible oil on the PP surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Edible oil high-temperature swelling-resistant modified polypropylene material applied to household appliances and preparation method thereof
  • Edible oil high-temperature swelling-resistant modified polypropylene material applied to household appliances and preparation method thereof
  • Edible oil high-temperature swelling-resistant modified polypropylene material applied to household appliances and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Prepare edible oil high temperature swelling resistant polypropylene material according to the raw materials in parts by weight shown in Table 1:

[0027] Table 1 The formula composition of high temperature swelling resistant edible oil polypropylene material

[0028] raw material Parts by weight (parts) Homo-PP 65 Anti-swelling modified masterbatch 18 heavy calcium 12 Compatibilizer 5 Antioxidant 1010 0.1 Antioxidant 168 0.2 sodium benzoate 0.2 Calcium stearate 0.2

Embodiment 2

[0030] Prepare edible oil high-temperature swelling-resistant polypropylene material according to the raw materials in parts by weight shown in Table 2:

[0031] Table 2 The formula composition of high temperature swelling resistant edible oil polypropylene material

[0032]

[0033]

Embodiment 3

[0035] Prepare edible oil high-temperature swelling-resistant polypropylene material according to the raw materials in parts by weight shown in Table 3:

[0036] Table 3 The composition of the high temperature swelling resistant edible oil polypropylene material

[0037] raw material Parts by weight (parts) Copolymerized PP 65 Anti-swelling modified masterbatch 18 heavy calcium 12 Compatibilizer 5 Antioxidant 1010 0.1 Antioxidant 168 0.2 sodium benzoate 0.2 Calcium stearate 0.2

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of high-molecular materials and discloses an edible oil high-temperature swelling-resistant modified polypropylene material applied to household appliances. The modified polypropylene material comprises the following components in parts by weight: 50-70 parts of polypropylene resin, 15-30 parts of swelling-resistant modified masterbatch, 7-15 parts of inorganic filler, 3-8 parts of a compatilizer, 0.1-0.3 part of a nucleating agent, 0.1-1.0 part of an antioxidant and 0.1-1.0 part of a processing aid. The invention also discloses a preparation method of the edible oil high-temperature swelling-resistant modified polypropylene material applied to the household appliances. The method comprises the following steps: uniformly mixing the polypropylene resin, the swelling-resistant modified masterbatch and the compatilizer, then adding the nucleating agent, the antioxidant and the processing aid, then continuing to stir, then adding the inorganic filler, uniformly stirring, finally adding the mixed materials in an extruder for extruding and granulating to obtain the polypropylene material. The polypropylene material prepared by the invention has high resistance to edible oil high-temperature swelling, high gloss, good scratch resistance, good heat resistance and good rigid-tough balance.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a modified polypropylene material for household appliances resistant to high-temperature swelling of cooking oil and a preparation method thereof. Background technique [0002] Polypropylene (PP) is a crystalline polymer with a regular structure. It is a white pellet, odorless, non-toxic, and light-weight thermoplastic resin. It has easy processing, impact resistance, flex resistance, and good electrical insulation. It has a wide range of applications in the automotive industry, household appliances, electronics, packaging and building materials and furniture. [0003] However, with the rapid development of my country's household electrical appliance industry in recent years, the use effect of PP in some household electrical appliances is not satisfactory, such as the application of the appearance parts of household appliances in the kitchen. Appearance parts will inevitably come...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L51/06C08L27/18C08L77/02C08L77/06C08K13/02C08K3/36C08K5/54C08K3/26C08K5/098C08K3/30
CPCC08L23/12C08K2201/014C08L23/14C08L2201/08C08L2203/20C08L2205/02C08L2205/035C08L2205/08C08L2205/24C08L51/06C08L27/18C08L77/02C08L77/06C08K13/02C08K3/36C08K5/54C08K2003/265C08K5/098C08K2003/3045C08K5/20
Inventor 于海鸥王灿耀易庆锋桑杰李白羽
Owner GUANGDONG ALDEX NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products