Eucalyptus wood board processing technique
A processing technology and wood board technology, applied in wood processing appliances, wood heating, wood treatment and other directions, can solve the problems of cracking, wood bursting, easy powdering of wood boards, etc., and achieve the effects of good toughness, no powdering, and low cost.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] A kind of eucalyptus board processing technology, operation steps are as follows:
[0016] (1) Put the eucalyptus board into the drying machine, the thickness of each eucalyptus board is 0.5cm, the length and width are cut according to the size of the drying machine space, and the temperature is kept at 75°C, the pressure is 0.25Mpa, and the time is 40s for drying; wherein, Put a layer of quartz sand with a thickness of 0.05mm on the bottom layer of the eucalyptus, as the quartz sand layer, spread the eucalyptus board on the quartz sand layer, place gauze on the eucalyptus board, place 0.2mm wood bran on the gauze, as the wood bran layer, gauze The eucalyptus board is separated from the eucalyptus board by a layer of chaff;
[0017] (2) Take out the eucalyptus board obtained after drying in step (1) for dehydration, and dry it during the whole dehydration process. The drying temperature for the first time is 60°C, cool to room temperature after 55 minutes, and keep the ...
Embodiment 2
[0019] A kind of eucalyptus board processing technology, operation steps are as follows:
[0020] (1) Put the eucalyptus board into the drying machine, the thickness of each eucalyptus board is 1cm, the length and width are cut according to the size of the drying machine space, and the temperature is kept at 85°C, the pressure is 0.30Mpa, and the time is 30s for drying; among them, place The bottom layer of the eucalyptus wood is first covered with quartz sand with a thickness of 0.1mm as the quartz sand layer, and the eucalyptus board is placed on the quartz sand layer, and gauze is placed on the eucalyptus board, and 0.5mm of wood chaff is placed on the gauze, as the wood chaff layer, gauze and The bran layer separates the eucalyptus boards from the eucalyptus boards;
[0021] (2) Take out the eucalyptus board obtained after drying in step (1) for dehydration, and dry it during the whole dehydration process. The drying temperature for the first time is 65°C, cool to room tem...
Embodiment 3
[0023] A kind of eucalyptus board processing technology, operation steps are as follows:
[0024] (1) Put the eucalyptus board into the drying machine, the thickness of each eucalyptus board is 0.7cm, the length and width are cut according to the size of the drying machine space, and the temperature is kept at 80°C, the pressure is 0.27Mpa, and the time is 35s for drying; wherein, Place a layer of quartz sand with a thickness of 0.08mm on the bottom layer of the eucalyptus wood as the quartz sand layer. On the quartz sand layer, lay a eucalyptus board. The eucalyptus board is separated from the eucalyptus board by a layer of chaff;
[0025] (2) Take out the eucalyptus board obtained after drying in step (1) for dehydration, and dry it during the whole dehydration process. The drying temperature for the first time is 63°C, cool to room temperature after 55 minutes, and keep the room temperature for 20 minutes; then carry out the second time Drying, the drying temperature is 55...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com