Polyester fiber reinforced anti-cracking diatom ooze material, and preparation method thereof

A polyester fiber and diatom mud technology, applied in the field of building materials, can solve the problems of loss of diatom mud's respiration and filtering effect, poor adhesion performance of inorganic materials, affecting the use performance of diatom mud, etc., to achieve enhanced water retention and moisturizing effect, Good anti-aging effect and easy mass production

Inactive Publication Date: 2017-03-29
东莞市爱乐居环保科技有限公司
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the redispersible rubber powder used in this patent belongs to organic latex powder. Although it can make the bonding stronger, it is easy to block the micropores and lose the breathing and filtering effect of diatom mud. In addition, the materials used are easy to release VOC substances such as formaldehyde. , unable to be truly green
[0005] The Chinese patent literature with the publication number CN101700965A discloses a kind of environment-friendly diatom mud wall material powder, wall material and preparation method thereof, the wall material mainly adopts inorganic materials such as diatomite, kaolin, sepiolite, vermiculite powder, etc. The effect of heat preservation and adsorption purification is better, but the adhesion performance of inorganic materials is poor, and it is easy to drop powder and fall off
[0006] In the prior art, the inorganic adhesives used in diatom mud are generally low in strength, poor in water retention, easy to remove powder, and cannot be used alone; and the disadvantages of wood fiber species are single, easy to absorb water and corrode, and the reinforcement effect is not high enough, which seriously affects the quality of diatom mud. performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester fiber reinforced anti-cracking diatom ooze material, and preparation method thereof
  • Polyester fiber reinforced anti-cracking diatom ooze material, and preparation method thereof
  • Polyester fiber reinforced anti-cracking diatom ooze material, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The preparation method of the polyester fiber reinforced crack-resistant diatom ooze material of this embodiment is prepared according to the following steps:

[0032] Step 1, preparation of mixed powder: 30 parts of diatomite with a silicon content of 95%, 22 parts of ground calcium carbonate with a particle size of 80 μm, 20 parts of ash calcium powder with a particle size of 60 μm, 8 parts of quartz sand with a particle size of 600 μm, 4 parts of negative ion powder with a particle size of 3.3 μm, 0.8 parts of sodium carboxymethyl cellulose with a viscosity of 20,000 and 1 part of potato starch with a particle size of 130 μm are sufficiently uniform to obtain a mixed powder;

[0033] Step 2. Preparation of nano-titanium dioxide mixed solution: after mixing 4 parts of rutile nano-titanium dioxide powder with water, ultrasonically disperse at 50KHz until uniform;

[0034] Step 3, preparing mixed slurry: adding the mixed powder in step 1 to the nano-titanium dioxide mix...

Embodiment 2

[0038] The preparation method of the polyester fiber reinforced crack-resistant diatom ooze material of this embodiment is prepared according to the following steps:

[0039] Step 1, preparation of mixed powder: 28 parts of diatomite with a silicon content of 90%, 30 parts of heavy calcium carbonate with a particle size of 45 μm, 18 parts of ash calcium powder with a particle size of 23 μm, 16 parts of quartz sand with a particle size of 450 μm, 3 Anion powder with a particle size of 12 μm, 0.5 part of sodium carboxymethyl starch with a viscosity of 80000, 1 part with a viscosity of 200000 hydroxypropyl methylcellulose and 0.3 part of cornstarch with a particle size of 150 μm are fully uniform to obtain a mixed powder;

[0040] Step 2. Preparation of nano-titanium dioxide mixed solution: after mixing 3 parts of anatase nano-titanium dioxide powder with water, ultrasonically disperse at 60KHz until uniform;

[0041] Step 3, preparing mixed slurry: adding the mixed powder in ste...

Embodiment 3

[0045] The preparation method of the polyester fiber reinforced crack-resistant diatom ooze material of this embodiment is prepared according to the following steps:

[0046] Step 1. Preparation of mixed powder: 15 parts of diatomite with a silicon content of 93%, 35 parts of heavy calcium carbonate with a particle size of 23 μm, 16 parts of ash calcium powder with a particle size of 150 μm, 20 parts of quartz sand with a particle size of 800 μm, 2 parts of negative ion powder with a particle size of 8 μm, 1 part of sodium carboxymethyl starch with a viscosity of 60000, 0.5 part of sodium carboxymethylcellulose with a viscosity of 120000, 0.5 part of hydroxypropyl methylcellulose with a viscosity of 100000 and 0.5 part The cassava pregelatinized starch with a particle size of 120 μm is sufficiently uniform to obtain a mixed powder;

[0047] Step 2. Preparation of nano-titanium dioxide mixed solution: after mixing 3 parts of rutile nano-titanium dioxide powder with water, ultra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyester fiber reinforced anti-cracking diatom ooze material, and a preparation method thereof. The polyester fiber reinforced anti-cracking diatom ooze material comprises, by mass, 15 to 35 parts of diatomite, 20 to 40 parts of heavy calcium carbonate, 8 to 20 parts of ash calcium powder, 8 to 20 parts of quartz sand, 2 to 5 parts of nanometer titanium dioxide, 1 to 4 parts of tourmaline, 0.5 to 2.5 parts of cellulose ether, 0.1 to 0.5 part of pregelatinized starch, and 0.1 to 2 parts of polyester fiber. According to the preparation method, diatomite, heavy calcium carbonate, ash calcium powder, quartz sand, nanometer titanium dioxide, tourmaline, and polyester fiber are taken as the raw materials, nontoxic and renewable adhesives cellulose ether and pregelatinized starch are also added, so that the obtained polyester fiber reinforced anti-cracking diatom ooze material possesses excellent cracking resistance and anti-pulverization ability; the preparation method is safe, and is friendly to the environment; production cost is low; and large-scale production can be realized easily.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a polyester fiber reinforced crack-resistant diatom mud material and a preparation method thereof. Background technique [0002] Diatom mud is a natural environmental protection interior wall decoration material, which is used to replace wallpaper and latex paint, and plays the role of interior wall decoration and indoor air purification. Its main raw materials are diatomite and amorphous silica. Since the surface of diatomite is rich in fine pores and a small amount of mesopores and micropores in the interior, it has a unique multi-level channel structure. The specific surface area of ​​diatomite can reach 65m 2 / g, light and non-toxic, powder bulk density is only 0.34-0.65g / m 3 , so it has strong adsorption, and can be used as filter aid, adsorption, thermal insulation and catalytic carrier materials, etc.; because its main component is amorphous silica (SiO 2 .nH...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/28C04B111/28C04B111/52
CPCC04B26/285C04B2111/00025C04B2111/28C04B2111/52C04B14/08C04B14/28C04B22/064C04B14/06C04B14/305C04B16/0683C04B20/008
Inventor 李绍龙唐世家吴沁
Owner 东莞市爱乐居环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap