Nickel-based molybdenum disulfide powder for laser cladding, its preparation method and use method

A molybdenum disulfide and laser cladding technology, applied in the field of powder materials, can solve the problems of limited application scope and application value, long time required for pre-melting layer, low production efficiency, etc. The effect of flatness

Active Publication Date: 2019-04-23
FUZHOU UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the time required for the preparation of the premelted layer by electroplating involved in this scheme is too long, the production efficiency is low, and it is not suitable for industrialization, which limits its application range and application value.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel-based molybdenum disulfide powder for laser cladding, its preparation method and use method
  • Nickel-based molybdenum disulfide powder for laser cladding, its preparation method and use method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The nickel-based molybdenum disulfide powder for laser cladding includes the following components:

[0035] Molybdenum disulfide: 3%wt, particle size 200 microns;

[0036] Aluminum: 2%wt, particle size 0.1 micron;

[0037] The balance is nickel with a particle size of 50 microns.

[0038] Its preparation process includes the following steps:

[0039] (1) Add the molybdenum disulfide powder, aluminum powder, and nickel powder that have been confirmed in particle size to the ethanol solution, stir it into a paste, then add it to the mixed solution of 80% ethanol and 20% methanol, soak for 10-30min, Remove the dirt on the surface of molybdenum disulfide powder, aluminum powder and nickel powder;

[0040] (2) Select quantitative filter paper to filter separately, and place them in a drying oven at 120°C for drying treatment for 30-60 minutes to remove residual ethanol and methanol;

[0041] (3) Mix powder, weigh molybdenum disulfide powder and aluminum powder in proport...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nickel-based molybdenum disulfide powder for laser cladding, a preparation method and a use method thereof, comprising the following components: molybdenum disulfide powder: 3-8%wt, particle size 0.1-2 microns; aluminum powder : 2~5%wt, particle size 200~300 microns; the balance is nickel powder, particle size 50~100 microns. The nickel-based molybdenum disulfide powder involved in the invention can effectively control the thermal decomposition of the molybdenum disulfide during the laser cladding process, thereby reducing the vulcanization effect of the decomposition on the obtained cladding layer, and improving the oxidation resistance of the cladding layer.

Description

technical field [0001] The invention relates to the field of powder materials, in particular to nickel-based molybdenum disulfide powder for laser cladding, a preparation method and a use method thereof. Background technique [0002] Laser cladding refers to placing the selected coating material on the surface of the substrate to be clad in different ways, and then irradiating it with laser to melt it and a thin layer on the surface of the substrate at the same time, and form a very low dilution after rapid solidification. The surface coating that is metallurgically combined with the substrate is a process method that significantly improves the wear resistance, corrosion resistance, heat resistance, oxidation resistance and electrical properties of the base surface, so as to achieve the purpose of surface modification or repair, which not only satisfies the specific needs of the material surface Performance requirements, but also save a lot of precious elements. Compared wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C24/10C22C32/00C22C19/03B22F1/00
CPCC22C19/03C22C32/0089C23C24/103B22F1/105
Inventor 戴品强徐临超
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com