Water-based plastic product label adhesive

A technology for pasting plastic products and labels, which is applied in the field of plastic product processing, can solve the problems of blackening of adhesives, inability to remove labels, inability to remove, etc., and achieve the effects of recycling, easy separation, and strong adhesion

Inactive Publication Date: 2017-02-08
肇庆高新区飞越信息科技有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most plastic products cannot completely remove their labels when they are used. Even after removal, some adhesives will adhere to the plastic products, and these adhesives are easy to absorb dust and turn black, and cannot be removed by washing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Add 10 parts of polyvinyl alcohol resin and 1 part of polyoxyethylene rosin acid ester to 100 parts of water, heat to reflux state and mix for 15 minutes, then add 8 parts of hydrogenated rosin pentaerythritol ester and 2 parts of polytetrahydrofuran ether glycol, continue Reflux heat preservation and mixing for 15min to obtain material I;

[0023] (2) Add 5 parts of sodium bentonite and 3 parts of water-soluble chitosan to 6 parts of hydroxyethyl methacrylate, heat to 110-120°C and mix for 10 minutes, then add 3 parts of flexibility additive and 1 part of tea seed powder, 1 part of diisooctyl maleate and 0.5 part of sodium pyrophosphate, and continue to mix at 110-120 ° C for 10 minutes to obtain material II;

[0024] (3) Add 2 parts of polymaleic anhydride and 1 part of polyaluminum chloride to material I, mix well and let stand for 30 minutes, then add material II, 1 part of polyquaternium-7 and 0.5 part of sodium glycinate, and heat to Heat and mix for 10 minut...

Embodiment 2

[0028] (1) Add 15 parts of polyvinyl alcohol resin and 0.5 part of polyoxyethylene rosin acid ester to 100 parts of water, heat to reflux state and mix for 15 minutes, then add 8 parts of hydrogenated rosin pentaerythritol ester and 3 parts of polytetrahydrofuran ether glycol, continue Reflux heat preservation and mixing for 15min to obtain material I;

[0029] (2) Add 5 parts of sodium bentonite and 5 parts of water-soluble chitosan to 8 parts of hydroxyethyl methacrylate, heat to 110-120°C and mix for 10 minutes, then add 3 parts of flexibility aid and 1 part of tea seed powder, 1 part of diisooctyl maleate and 0.5 part of sodium pyrophosphate, and continue to mix at 110-120 ° C for 10 minutes to obtain material II;

[0030] (3) Add 3 parts of polymaleic anhydride and 1 part of polyaluminum chloride to the material I, and let it stand for 30 minutes after fully mixing, then add material II, 0.5 part of polyquaternium-7 and 0.5 part of sodium glycinate, and heat to Heat and ...

Embodiment 3

[0034] The adhesives prepared in Examples 1 and 2 are used for pasting labels of plastic products. It is found through actual production that the adhesive can make the label sticking success rate reach 100%, and the pasted labels will not be misplaced due to friction. There is no peeling of the label during transportation, sales and use. After the label is removed, the adhesive remaining on the plastic product can be completely removed by washing it with water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based plastic product label adhesive, relating to the technical field of plastic product processing. The water-based plastic product label adhesive is prepared from the following raw materials in parts by weight: 10-15 parts of polyvinyl alcohol resin, 8-12 parts of hydrogenated rosin pentaerythritol ester, 4-8 parts of hydroxyethyl methacrylate, 3-6 parts of sodium bentonite, 3-6 parts of water-soluble chitosan, 2-4 parts of polymaliec acid anhydride, 2-4 parts of polyoxytetramethylene glycol, 2-4 parts of aid, 1-2 parts of tea seed powder, 1-2 parts of polyaluminum chloride, 1-2 parts of diisooctyl maleate, 0.5-1 part of polyoxyethylene abietate, 0.5-1 part of polyquaternary amine salt-7, 0.5-1 part of sodium glycinate, 0.5-1 part of sodium pyrophosphate and 100-150 parts of water. The adhesive has high binding property, and can firmly attach the label to the plastic product, thereby achieving the goal of identifying the product information. The label can be easily peeled off, and the residual adhesive on the plastic product after the label is peeled off can be washed off by water.

Description

[0001] Technical field: [0002] The invention relates to the technical field of plastic product processing, in particular to a water-based plastic product label adhesive. [0003] Background technique: [0004] Plastic products are a general term for household and industrial products processed from plastic as the main raw material. Including plastic as raw material for injection molding, blister and other products of all processes. The label is the carrier used to mark the product name, manufacturer, production address, production time and barcode of the plastic product, which is convenient for consumers to identify the relevant information of the purchased plastic products and facilitate the sale of plastic products in supermarkets and stores. To attach labels to plastic products, label adhesives are usually used. At present, most plastic products cannot completely remove their labels during use. Even after removal, some adhesives will adhere to the plastic products, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J129/04C09J105/08C09J133/14C09J157/02C09J129/14C09J11/08C09J11/06C09J11/04
CPCC09J129/04C08L2205/02C08L2205/035C09J11/04C09J11/06C09J11/08
Inventor 曾诗敏
Owner 肇庆高新区飞越信息科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products