Environment-friendly seal ring material used for respirator and preparing method thereof

A sealing ring and respirator technology, applied in the field of sealing ring materials, can solve the problems of short service life, easy aging, poor environmental protection, etc., and achieve the effects of good environmental protection, strong aging resistance, and high tensile strength

Inactive Publication Date: 2017-02-01
NINGBO TONGGUAN ELECTRIC AUTOMATION EQUIP
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional silicone rubber mostly contains toxic plasticizers, which has poor environmental protection, is easy to age, and has a short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A kind of respirator is used environment-friendly sealing ring material, and it is made up of the raw material of following weight part:

[0018] Methyl vinyl phenyl silicone rubber 120, antioxidant MB1, zinc oxide 1, sulfur 0.9, dodecyl mercaptan 4, zinc hydroxystannate 1, dibutyl maleate 10, dimethyl diallyl Ammonium chloride 0.8, casein 0.5, bark powder 6, triethanolamine 1, calcium palmitate 3, polyacrylamide 2, polyethylene wax 4, sodium lauryl sulfate 1, carbon fiber 3, trimethylolpropane 0.4, horse Toric anhydride 5, antioxidant AW1, potassium persulfate 0.1, diatomaceous earth 16.

[0019] A kind of preparation method of described respirator with environment-friendly sealing ring material comprises the following steps:

[0020] (1) Add the above bark powder to 7mol / l hydrochloric acid, soak at 50°C for 1 hour, discharge and cool, add to 10mol / l sodium hydroxide, soak at 70°C for 1 hour, filter , sending the precipitate into an oven at 50°C, drying for 2 hours,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly seal ring material used for a respirator. The environment-friendly seal ring material is prepared from, by weight, 120-140 parts of methyl vinyl phenyl siloxane rubber, 1-2 parts of anti-aging agent MB, 1-2 parts of zinc oxide, 0.9-1 part of sulfur, 4-5 parts of lauryl mercaptan, 1-2 parts of hydroxy zinc stannate, 10-14 parts of dibutyl maleate, 0.8-1 part of dimethyl diallyl ammonia chloride, 0.5-1 part of casein, 6-7 parts of powdered bark, 1-2 parts of triethanolamine, 3-4 parts of calcium palmitate, 2-4 parts of polyacrylamide, 4-5 parts of polyethylene wax, 1-2 parts of sodium laurylsulfate, 3-4 parts of carbon fiber, 0.4-1 part of trimethylolpropane, 5-7 parts of maleic anhydride, 1-2 parts of anti-ageing agent AW, 0.1-0.2 part of potassium peroxodisulfate and 16-20 parts of kieselguhr. The rubber material is high in elongation at break and tensile strength, high in tenacity and water resistance, high in acid and alkali corrosion, high in storage stability and ageing resistance, free of poisonous and harmful substance volatilization, high in environment-friendly performance and excellent in comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of sealing ring materials, in particular to an environment-friendly sealing ring material for a respirator and a preparation method thereof. Background technique [0002] The remarkable feature of silicone rubber is high temperature stability. Although the strength of silicone rubber at room temperature is only half that of natural rubber or some synthetic rubber, it can still maintain a certain degree of flexibility and resilience in high temperature environments above 200°C. Elasticity and surface hardness, and no significant change in mechanical properties. Low temperature performance The glass transition temperature of silicone rubber is generally -70~-50°C, and the special formula can reach -100°C, which shows that it has excellent low temperature performance. This is of great significance to the aviation and aerospace industries. The Si-O-Si bond in weather-resistant silicone rubber is very stable to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L51/10C08L33/26C08L23/06C08L97/02C08K13/06C08K9/04C08K3/34C08K3/22C08K7/06C08K5/098C08F292/00C08F222/06
CPCC08L83/04C08F292/00C08L2203/20C08L2205/035C08L51/10C08L33/26C08L23/06C08L97/02C08K13/06C08K9/04C08K3/346C08K2003/2296C08K7/06C08K5/098C08F222/06
Inventor 张立
Owner NINGBO TONGGUAN ELECTRIC AUTOMATION EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap