Preparation and application of novel environmental-friendly cyanuric acid compound stabilizer special for PVC profile

A composite stabilizer and special-shaped material technology, which is applied in the field of organic compound synthesis, can solve problems such as application restrictions and high prices

Inactive Publication Date: 2017-02-01
SHENZHEN AIMSEA IND
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The price of organotin is high, considering the economic cost-effectiveness, its application is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and application of novel environmental-friendly cyanuric acid compound stabilizer special for PVC profile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Step 1, the preparation of zinc cyanurate;

[0031] Take the quality of total reactant as benchmark, prepare zinc cyanurate stabilizer according to following formula:

[0032] Cyanuric acid 62-67 parts

[0033] Zinc oxide 60-65 parts

[0034] Silane coupling agent 0.1-0.3 parts

[0035] 3-5 parts of acetic acid

[0036] Add cyanuric acid, zinc oxide, and silane coupling agent into a mechanical cyclone mill according to the above ratio, and grind and blend for 60 minutes under the specific conditions of microwave radiation and acetic acid as a catalyst to obtain a zinc cyanurate stabilizer.

[0037] Step two, compounding;

[0038] Taking the quality of the total reactant as a benchmark, compound the cyanuric acid stabilizer according to the following formula:

[0039] Zinc cyanurate 20 parts

[0040] Auxiliary stabilizer 5 parts

[0041] Lubricant 20 parts

[0042] Antioxidant 5 parts

[0043] Zinc stearate 20 parts

[0044] Calcium stearate 10 parts

[0045] ...

Embodiment 2

[0056] Step 1, the preparation of zinc cyanurate;

[0057] Take the quality of total reactant as benchmark, prepare zinc cyanurate stabilizer according to following formula:

[0058] Cyanuric acid 62-67 parts

[0059] Zinc oxide 60-65 parts

[0060] Silane coupling agent 0.1-0.3 parts

[0061] 3-5 parts of acetic acid

[0062] Add cyanuric acid, zinc oxide, and silane coupling agent into a mechanical cyclone mill according to the above ratio, and grind and blend for 60 minutes under the specific conditions of microwave radiation and acetic acid as a catalyst to obtain a zinc cyanurate stabilizer.

[0063] Step two, compounding;

[0064] Taking the quality of the total reactant as a benchmark, compound the cyanuric acid stabilizer according to the following formula:

[0065] Zinc cyanurate 19 parts

[0066] Auxiliary stabilizer 4.5 parts

[0067] Lubricant 16 parts

[0068] Antioxidant 4.5 parts

[0069] Zinc stearate 16 parts

[0070] 7 parts calcium stearate

[007...

Embodiment 3

[0082] Step 1, the preparation of zinc cyanurate;

[0083] Take the quality of total reactant as benchmark, prepare zinc cyanurate stabilizer according to following formula:

[0084] Cyanuric acid 62-67 parts

[0085] Zinc oxide 60-65 parts

[0086] Silane coupling agent 0.1-0.3 parts

[0087] 3-5 parts of acetic acid

[0088] Add cyanuric acid, zinc oxide, and silane coupling agent into a mechanical cyclone mill according to the above ratio, and grind and blend for 60 minutes under the specific conditions of microwave radiation and acetic acid as a catalyst to obtain a zinc cyanurate stabilizer.

[0089] Step two, compounding;

[0090] Taking the quality of the total reactant as a benchmark, compound the cyanuric acid stabilizer according to the following formula:

[0091] Zinc cyanurate 17 parts

[0092] Auxiliary stabilizer 3.5 parts

[0093] Lubricant 13 parts

[0094] Antioxidant 4 parts

[0095] Zinc stearate 14 parts

[0096] 4 parts calcium stearate

[0097]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of chemical stabilizers and in particular to preparation and application of a novel environmental-friendly cyanuric acid compound stabilizer special for a PVC profile. The preparation comprises the following steps: forming a basic catalyst by adopting caustic soda (sodium hydroxide), taking zinc oxide as a raw material, and directly reacting to produce cyanuric acid; neutralizing the basic catalyst by utilizing industrial stearic acid, taking the produced sodium stearate as a surfactant of zinc cyanurate; compounding an auxiliary stabilizer, a lubricating agent, an antioxidant, zinc stearate, calcium stearate and zinc cyanurate according to a set formula. Compared with the traditional heat stabilizer, the cyanuric acid is capable of improving the plasticizing quality of the PVC profile; due to the added lubricating agent, a phenomenon of flow velocity disorder occurring in material processing and production is avoided, so that production and processing can be normally performed, and the inherent quality and appearance quality are improved. Moreover, the stabilizer is environmental-friendly and non-toxic, has high heat stability and processability as well as wide application prospects in the PVC profile industry.

Description

technical field [0001] The invention relates to the technical field of organic compound synthesis, and specifically designs the preparation and application of a novel cyanuric acid composite stabilizer specially used for environment-friendly PVC profiled materials. Background technique [0002] Polyvinyl chloride [poly (vinyl choride), PVC] is one of the five largest synthetic resins in the world. It is a thermoplastic linear polymer produced by free radical polymerization of vinyl chloride monomer. PVC material has the advantages of high strength, low price, good chemical corrosion resistance, good electrical insulation and difficult to burn, and is easy to process. It can be processed by molding, lamination, injection molding and other methods. It is widely used in engineering construction, Hard and soft products in food packaging, electrical and other industries. With the further expansion of application fields, the demand for PVC will continue to increase. PVC profiles...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K13/02C08K5/098C08K3/22C08K3/26C08K5/3492
CPCC08K13/02C08K3/22C08K3/26C08K5/098C08K5/34924C08K2003/2241C08K2003/2296C08K2003/265C08K2201/014C08L2201/08C08L27/06
Inventor 严一丰严晴周国庆张显蒋设高金奎杨光翟华伟
Owner SHENZHEN AIMSEA IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com