Polymer composition for manufacturing high-elasticity table tennis ball

A table tennis and polymer technology, which is applied in the field of polymer compositions for making high elastic table tennis balls, can solve the problems of flammability, environmental hazards, flammability and explosion, and achieve excellent elastic modulus, good eccentricity and hardness. high effect

Inactive Publication Date: 2017-02-01
YANCHENG AST SPORTING GOODS
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But adopting celluloid to be raw material to make highly elastic table tennis has following drawbacks: celluloid material is to be main raw material with the nitrocellulose of dehydration, and it is inflammable and explosive, and there is bigger safety in its storage in raw material stage, production stage, transportation process hidden dangers, and after being made into table tennis products, there are also hidden dangers of flammability during storage and transportation; and for safety, nitrocellulose needs to be added with water during transportation, and needs to be dehydrated during use. There is a large amount of waste liquid discharged, which will It brings harm to the environment and is not environmentally friendly; in addition, its production process is complicated and the production cycle is long

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present embodiment provides a kind of macromolecule composition that is used to make high elasticity table tennis, and it comprises the component of following parts by weight:

[0022] High-density polyethylene (PE-EA-57D003, molecular weight 10000): 110g;

[0023] Vinylimidazole-acrylonitrile copolymer (obtained by conventional free radical polymerization after mixing vinylimidazole and acrylonitrile at a mass ratio of 1:1, with a number average molecular weight of 10,000): 20g;

[0024] Heat stabilizer (calcium zinc composite stabilizer, TF-790GX-6B): 2.5 g;

[0025] Lubricant (zinc stearate): 5 g;

[0026] Strengthening and toughening agent (ABS, Japan Toray 100-X01): 8 g;

[0027] Titanium dioxide (Ti-Pure R-103): 0.2 g;

[0028] Antioxidant (phosphite): 0.2g.

Embodiment 2

[0030] The present embodiment provides a kind of macromolecule composition that is used to make high elasticity table tennis, and it comprises the component of following parts by weight:

[0031] High-density polyethylene (Shanghai Petrochemical MH602, molecular weight 100000): 150g;

[0032] Vinylimidazole-acrylonitrile copolymer (obtained by conventional free radical polymerization after mixing vinylimidazole and acrylonitrile at a mass ratio of 5:1, with a molecular weight of 100,000): 10g;

[0033] Heat stabilizer (laurate type organotin heat stabilizer): 0.5g;

[0034] Lubricant (calcium stearate): 1g;

[0035] Reinforcement and toughening agent (thermoplastic polyurethane, TPU, Dongguan Detron): 5g;

[0036] Titanium dioxide (Ti-Pure R-104): 0.1g;

[0037] Antioxidant (2,5-Di-tert-butylhydroquinone): 0.1g.

Embodiment 3

[0039] The present embodiment provides a kind of macromolecule composition that is used to make high elasticity table tennis, and it comprises the component of following parts by weight:

[0040] Polyethylene (Shanghai Petrochemical MH602, molecular weight 80000): 120g;

[0041] Vinylimidazole-acrylonitrile copolymer (obtained by conventional free radical polymerization after mixing vinylimidazole and acrylonitrile at a mass ratio of 4:1, with a molecular weight of 80,000): 18g;

[0042] Heat stabilizer (maleic acid ester organotin heat stabilizer): 2.2g;

[0043] Lubricant (magnesium stearate): 4g;

[0044] Reinforcing and toughening agent (thermoplastic polyolefin, HP162): 7g;

[0045] Titanium dioxide (Ti-Pure R-104): 0.18g;

[0046] Antioxidant (2,6-di-tert-butyl-p-cresol): 0.18g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a polymer composition for manufacturing a high-elasticity table tennis ball. The polymer composition is prepared from the following components in parts by weight: 110-150 parts of polyethylene, 10-20 parts of vinyl imidazole-acrylonitrile copolymer, 0.5-2.5 parts of a heat stabilizer, 1-5 parts of a lubricant, 5-8 parts of a strengthening and toughening agent, 0.1-0.2 part of titanium dioxide powder and 0.1-0.2 part of an antioxidant. According to the polymer composition, by adopting the raw materials including the vinyl imidazole-acrylonitrile copolymer, the heat stabilizer, the lubricant, the strengthening and toughening agent, the titanium dioxide powder, the antioxidant and the like according to the ratio, celluloid is prevented from being used, and the polymer composition is low in cost, high in hardness, excellent in elastic modulus and good in eccentricity and can meet environment-friendly table tennis ball used materials needed by a table tennis official ball.

Description

technical field [0001] The invention belongs to the field of polymer materials, in particular to a polymer composition used for making high-elastic table tennis balls. Background technique [0002] Since the 1930s, celluloid has been used as a raw material to prepare table tennis balls. Due to its high hardness and elastic modulus, the table tennis balls produced have the advantages of uniform thickness and long service life, and this material has been used until now. . But adopting celluloid to be raw material to make highly elastic table tennis has following drawbacks: celluloid material is to be main raw material with the nitrocellulose of dehydration, and it is inflammable and explosive, and there is bigger safety in its storage in raw material stage, production stage, transportation process hidden dangers, and after being made into table tennis products, there are also hidden dangers of flammability during storage and transportation; and for safety, nitrocellulose need...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L39/04C08L33/20C08K13/02C08K5/098C08K3/22C08K5/524C08K5/13
CPCC08L23/06C08L2205/03C08L2205/035C08L2207/062C08L39/04C08K13/02C08K2003/2241C08K5/098C08K5/524C08L33/20C08K5/13C08K5/37C08K5/1345
Inventor 王旭升高焱汤小庆刘宗英黄田富
Owner YANCHENG AST SPORTING GOODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap