A kind of honeycomb ceramic plate load tio 2 ——Preparation process of ncp immobilized photocatalyst

A honeycomb ceramic plate, photocatalyst technology, applied in physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, chemical instruments and methods, etc., to achieve easy recovery and reuse, stable performance and low price Effect

Active Publication Date: 2017-10-10
NATURE ENVIRONMENTAL PROTECTION TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There is no literature report on the photocatalyst of multi-element co-doped TiO2 loaded on the honeycomb ceramic plate, and its application in the deep treatment of water health and environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of honeycomb ceramic plate load tio <sub>2</sub> ——Preparation process of ncp immobilized photocatalyst
  • A kind of honeycomb ceramic plate load tio <sub>2</sub> ——Preparation process of ncp immobilized photocatalyst
  • A kind of honeycomb ceramic plate load tio <sub>2</sub> ——Preparation process of ncp immobilized photocatalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The honeycomb ceramic plate loaded with TiO 2 -The preparation technology of NCP immobilized photocatalyst comprises the following steps:

[0036] 1) Preparation of honeycomb ceramic plate:

[0037] Silicon oxide, aluminum oxide, magnesium oxide, iron oxide, titanium dioxide, K 2 O and Na 2 O and CaO are wet-milled in a ball mill to less than 320 mesh powder, silicon oxide, aluminum oxide, magnesium oxide, iron oxide, titanium dioxide, K 2 O and Na 2 The mass percentage of O and CaO components is 39% of silicon oxide, 52% of aluminum oxide, 6% of magnesium oxide, 0.8% of iron oxide, 1.0% of titanium dioxide, K 2 O and Na 2 O and CaO 1.2%, the powder after ball milling becomes mud block after pressure filtration and vacuum refining, and the green body is synthesized in a downdraft kiln to become cordierite material; then the synthesized cordierite is finely ground again to the required Granularity is required; then the finely ground cordierite powder is added to th...

Embodiment 2

[0049] The honeycomb ceramic plate loaded with TiO 2 -The preparation technology of NCP immobilized photocatalyst comprises the following steps:

[0050] 1) Preparation of honeycomb ceramic plate:

[0051] Silicon oxide, aluminum oxide, magnesium oxide, iron oxide, titanium dioxide, K 2 O and Na 2 O and CaO are wet-milled in a ball mill to less than 320 mesh powder, silicon oxide, aluminum oxide, magnesium oxide, iron oxide, titanium dioxide, K 2 O and Na 2 The mass percentages of O and CaO components are silicon oxide 44%, aluminum oxide 47%, magnesium oxide 5%, iron oxide 0.5%, titanium dioxide 1.9%, K 2 O and Na 2 O and CaO 1.6%, the powder after ball milling becomes mud block after pressure filtration and vacuum refining, and the green body is synthesized in a downdraft kiln to become cordierite material; then the synthesized cordierite is finely ground again to the required Granularity is required; then the finely ground cordierite powder is added to the binder with...

Embodiment 3

[0063] The honeycomb ceramic plate loaded with TiO 2 -The preparation technology of NCP immobilized photocatalyst comprises the following steps:

[0064] 1) Preparation of honeycomb ceramic plate:

[0065] Silicon oxide, aluminum oxide, magnesium oxide, iron oxide, titanium dioxide, K 2 O and Na 2 O and CaO are wet-milled in a ball mill to less than 320 mesh powder, silicon oxide, aluminum oxide, magnesium oxide, iron oxide, titanium dioxide, K 2 O and Na 2 The mass percentage of each component of O and CaO is 42% of silicon oxide, 50% of aluminum oxide, 5% of magnesium oxide, 0.5% of iron oxide, 1% of titanium dioxide, K 2 O and Na 2 O and CaO 1.5%, the powder after ball milling becomes mud block after pressure filtration and vacuum refining, and the green body is synthesized in a downdraft kiln to become cordierite material; then the synthesized cordierite is finely ground again to the required Granularity is required; then the finely ground cordierite powder is added ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation process of a honeycomb ceramic plate loaded TiO2-NCP immobilized photocatalyst, and belongs to the field of air purifying agent processing. The preparation process of the honeycomb ceramic plate loaded TiO2-NCP immobilized photocatalyst includes the first step of preparing honeycomb ceramic plates, the second step of preparing a TiO2-NCP composite photocatalyst, and the third step of preparing the honeycomb ceramic plate loaded TiO2-NCP immobilized photocatalyst. By means of the multielement-doped TiO2-NCP / Honeycomb cerami composite photocatalyst and the multielement-codoped TiO2-NCP / Honeycomb cerami composite photocatalyst prepared through the honeycomb ceramic plates, advanced treatment can be carried out on pollutants and VOCs in air under natural conditions, no waste is generated, and the composite photocatalyst is an environment-friendly product.

Description

technical field [0001] The invention belongs to the field of air purifier processing, in particular, relates to a honeycomb ceramic plate loaded TiO 2 —The preparation process of NCP immobilized photocatalyst. Background technique [0002] Photocatalytic environmental protection technology is a new purification technology produced by applying photocatalytic method to environmental pollution control. It is based on the super strong redox ability of photocatalyst under the irradiation of light, which can almost decompose various organic pollutants into CO 2 and H 2 O, can almost kill biological pollutants such as various bacteria and viruses. Moreover, it has the characteristics of high efficiency, low operating cost, and can be operated under normal temperature and pressure. It has been one of the research hotspots in the field of cutting-edge science and technology for more than 20 years, and it has developed rapidly in the past ten years. It has become a The new technol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/89
CPCB01J23/8946B01J35/004B01J35/04
Inventor 冯泽云韩延昆
Owner NATURE ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com