Geopolymer-based light wallboard and preparation method

A geopolymer, lightweight wallboard technology, used in clay preparation devices, chemical instruments and methods, ceramic products, etc., to achieve the effects of excellent sound insulation, small voids, and good resistance to tensile deformation

Inactive Publication Date: 2017-01-04
MAANSHAN MCC17 ENG TECH CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the technical problems existing in the existing lightweight wallboards, the present invention provides a geopolymer-based lightweight wallboard and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The invention provides a geopolymer-based lightweight wallboard. The raw materials are weighed according to the following parts by weight:

[0035] Bentonite powder 26, iron tailings slag powder 20, vermiculite powder 10, alkaline activator 22, ecological fiber 0.2, foaming agent 0.5, thickener 0.3, water 21.

[0036] (1) Mix and stir the caustic soda and liquid water glass until the caustic is completely dissolved to obtain an alkaline activator;

[0037] (2) Put the bentonite powder, iron tailings powder, expanded vermiculite powder, thickener, and ecological fiber required for batching together for 10 to 15 minutes, and then mix according to the required water, The foaming agent and the alkaline activator are added in sequence, and the stirring is continued for 30 to 45 minutes to obtain geopolymer foam concrete;

[0038] (3) Inject the geopolymer foam concrete into the wall panel molding machine through the grouting pump, and then demould after the concrete is soli...

Embodiment 2

[0040] The invention provides a geopolymer-based lightweight wallboard. The raw materials are weighed according to the following parts by weight:

[0041] Bentonite powder 20, iron tailings slag powder 32, vermiculite powder 12, alkaline activator 18, ecological fiber 0.1, foaming agent 0.8, thickener 0.1, water 17.

[0042] (1) Mix and stir the caustic soda and liquid water glass until the caustic is completely dissolved to obtain an alkaline activator;

[0043] (2) Put the bentonite powder, iron tailings powder, expanded vermiculite powder, thickener, and ecological fiber required for batching together for 10 to 15 minutes, and then mix according to the required water, The foaming agent and the alkaline activator are added in sequence, and the stirring is continued for 30 to 45 minutes to obtain geopolymer foam concrete;

[0044] (3) Inject the geopolymer foam concrete into the wall panel molding machine through the grouting pump, and then demould after the concrete is soli...

Embodiment 3

[0046] The invention provides a geopolymer-based lightweight wallboard. The raw materials are weighed according to the following parts by weight:

[0047] Bentonite powder 15, iron tailings slag powder 40, vermiculite powder 18, alkaline activator 10, ecological fiber 0.4, foaming agent 0.1, thickener 0.5, water 16.

[0048] (1) Mix and stir the caustic soda and liquid water glass until the caustic is completely dissolved to obtain an alkaline activator;

[0049] (2) Put the bentonite powder, iron tailings powder, expanded vermiculite powder, thickener, and ecological fiber required for batching together for 10 to 15 minutes, and then mix according to the required water, The foaming agent and the alkaline activator are added in sequence, and the stirring is continued for 30 to 45 minutes to obtain geopolymer foam concrete;

[0050] (3) Inject the geopolymer foam concrete into the wall panel molding machine through the grouting pump, and then demould after the concrete is soli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a geopolymer-based light wallboard and a preparation method. The geopolymer-based light wallboard is composed of high-strength asbestos-fiber-free cement plates on two sides and geopolymer-based foamed concrete in the middle. The geopolymer-based foamed concrete is prepared from, by mass, 5-32 parts of bentonite fine powder, 3-28 parts of iron tailings slag fine powder, 5-17 parts of expanded vermiculite powder, 5-25 parts of alkaline activator, 0.05-0.8 part of ecological fiber, 0.05-1.0 part of foaming agent, 0.2-1.0 part of thickener and 10-30 parts of water. The bentonite fine powder is formed by smashing and grinding bentonite raw ore, particle size is 1.2-5.8 micrometers, density is 1.7-2.5 g / cm<2>, pores are thin, small and uniform and not connected mutually, the bentonite fine powder is excellent in sound-isolation, heat-insulation and flame-retardant properties, and the service life of the bentonite fine powder is the same to that of a body structure. Low weight and high strength are achieved, and the specific gravity is low, so that the foamed concrete is tough. Besides, China has rich ecological plant resources, a lot of resources can be saved, the survival environment of human is benefited, and the strength and the durability of the light wallboard are improved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a geopolymer-based lightweight wallboard and a preparation method thereof. Background technique [0002] With the improvement of people's awareness of environmental protection and energy conservation and the regulations of national policies, various industries have increased their research and development efforts in environmental protection and energy conservation to better protect the environment in which human beings live. [0003] Geopolymer is one of the non-metallic materials that has been studied very actively in the world in recent years. It is a new type of inorganic polymer material obtained by chemical reaction at a lower temperature with silicon-containing solid materials such as clay, industrial waste or slag as the main raw material. It can replace cement for construction, Roads, artificial islands, prefabricated components, refractory materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04C2/288C04B38/10C04B28/00C04B18/24B28B1/00B28B1/52B28C5/00B28B11/24B28B13/06
CPCB28B1/00B28B1/52B28B11/243B28B13/06B28C5/003C04B28/006C04B38/10C04B2201/32C04B2201/50E04C2/288C04B38/0067C04B14/104C04B18/12C04B14/204C04B22/062C04B22/08C04B18/245C04B18/248C04B24/32C04B24/383C04B22/002Y02P40/10Y02W30/91
Inventor 钱元弟柯能好雷团结过前红王孝平李亚辉陈贺王慧
Owner MAANSHAN MCC17 ENG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com