Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Compound concrete expanding agent

A technology of expansion agent and concrete, which is applied in the field of building material concrete admixture, can solve unsatisfactory problems, and achieve the effect of increasing market value, improving early strength, and having more pores

Active Publication Date: 2017-01-25
GUILIN HUAYUE ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it can obtain a certain strength and the ability to compensate for shrinkage, it is still unsatisfactory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound concrete expanding agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A composite concrete expansion agent, which is made of the following components in parts by weight: 18 parts of calcium aluminosilicate, 28 parts of calcium sulfoaluminate, 25 parts of solid sulfur waste residue, 15 parts of red mud, 12 parts of lithium slag, 6 parts of modified calcium oxide, 5 parts of magnesium oxide, 7 parts of sodium methyl silicate, 0.2 parts of azodicarbonamide, 0.6 parts of sodium tripolyphosphate, 3 parts of sodium lauryl sulfate, 0.4 parts of ethylene-acrylic acid copolymer Parts, 0.8 parts of polycarboxylic acid water reducing agent, 0.6 parts of nano calcium carbonate.

Embodiment 2

[0029] A composite concrete expansion agent, which is made of the following components in parts by weight: 15 parts of calcium aluminosilicate, 25 parts of calcium sulfoaluminate, 20 parts of solid sulfur waste residue, 10 parts of red mud, 10 parts of lithium slag, 4 parts of modified calcium oxide, 3 parts of magnesium oxide, 5 parts of sodium methyl silicate, 0.1 parts of azodicarbonamide, 0.4 parts of sodium tripolyphosphate, 2 parts of sodium lauryl sulfate, 0.3 parts of ethylene-acrylic acid copolymer Parts, 0.7 parts of polycarboxylic acid water reducing agent, 0.5 parts of nano calcium carbonate.

Embodiment 3

[0031] A composite concrete expansion agent, which is made of the following components in parts by weight: 20 parts of calcium aluminosilicate, 30 parts of calcium sulfoaluminate, 30 parts of solid sulfur waste residue, 20 parts of red mud, 15 parts of lithium slag, 8 parts of modified calcium oxide, 6 parts of magnesium oxide, 8 parts of sodium methyl silicate, 0.3 parts of azodicarbonamide, 0.7 parts of sodium tripolyphosphate, 4 parts of sodium lauryl sulfate, 0.6 parts of ethylene-acrylic acid copolymer Parts, 0.9 parts of polycarboxylic acid water reducing agent, 0.7 parts of nano calcium carbonate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a compound concrete expanding agent. The compound concrete expanding agent is prepared by using the following components in parts by weight: 15 to 20 parts of calcium aluminosilicate, 25 to 30 parts of calcium sulphoaluminate, 20 to 30 parts of sulfur fixation waste residue, 10 to 20 parts of red mud, 10 to 15 parts of lithium slag, 4 to 8 parts of modified calcium oxide, 3 to 6 parts of magnesium oxide, 5 to 8 parts of methyl sodium silicate, 0.1 to 0.3 part of azodicarbonamide, 0.4 to 0.7 part of sodium tripolyphosphate, 2 to 4 parts of lauryl sodium sulfate, 0.3 to 0.6 part of ethylene-acrylic acid copolymer, 0.7 to 0.9 part of polycarboxylate superplasticizer and 0.5 to 0.7 part of nano calcium carbonate. The compound concrete expanding agent has the advantages of high strength, good compensation capability, calcium oxide reaction regulation and the like, and is a concrete additive which has a great development prospect.

Description

Technical field [0001] The invention relates to a composite concrete expansion agent and belongs to the technical field of building material concrete admixtures. Background technique [0002] Concrete is the most widely used building material. With the development of science and technology, it is constantly being studied in depth and its performance is improved and developed. In recent years, the problem of concrete shrinkage and cracking has become a research hotspot. This is because in the initial stage of cement hardening, water loss and changes in temperature and humidity can easily cause volume shrinkage. When the shrinkage is limited, the tensile stress generated exceeds the concrete itself. At the time of tensile strength, cement concrete is prone to cracking; at the same time, the load-bearing capacity of the cracked concrete is drastically reduced; in addition, the infiltration of water will further deteriorate the durability of the concrete, causing corrosion of steel b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/42
CPCC04B40/0039C04B22/08C04B22/0093C04B18/0427C04B18/0409C04B18/141C04B22/064C04B22/066C04B24/42C04B24/129C04B22/16C04B24/16C04B24/26C04B22/10C04B2103/302
Inventor 陈威黄煌王恒尹丹阮长泰谢体云欧鹏
Owner GUILIN HUAYUE ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com