A kind of preparation method of self-lubricating anti-friction and wear-resisting coating for suspension clamp of transmission line

A technology for hanging wire clamps and transmission lines, which is applied in coating, metal material coating technology, fusion spraying, etc., which can solve problems such as wire wear and tear, and achieve the effects of improving service life, reducing rapid wear, and ensuring safe operation

Active Publication Date: 2018-09-28
ELECTRIC POWER RESEARCH INSTITUTE OF STATE GRID SHANDONG ELECTRIC POWER COMPANY +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the hard coating has high hardness and high wear resistance, it is easy to cause more serious wear to the wire while being wear-resistant.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A self-lubricating composite coating for electric hardware, the composition mass percentage of the coating is: tin (Sn) 5%, antimony (Sb) 1.5%, silicon (Si) 2.0%, boron (B) 0.8%, carbon (C ) <0.01%, the rest of the total impurities <1.0%, and the balance is copper (Cu).

[0037] Copper-based alloy powders for self-lubricating coatings: the raw materials used are commercially available: CuSi 16 Master alloy, CuSb 50 Master alloy, CuSn 16 master alloy, CuB 3 Master alloy, T1 oxygen-free copper (copper content ≥ 99.98wt.%). According to the formula ratio, put the raw materials into the crucible of high-frequency induction vacuum melting equipment, fully melt each alloy raw material at 1100℃~1150℃ and keep it warm for 10min, then release it from the furnace, and then use atomization powder making method in the pulverizer under high-purity argon gas The powder was prepared in a protective atmosphere, sieved, and the powder with a particle size range of 10 μm to 60 μm was...

Embodiment 2

[0043] A self-lubricating composite coating for electric power fittings, the composition mass percentage of the coating is: tin (Sn) 18.0%, antimony (Sb) 8.0%, silicon (Si) 5.0%, boron (B) 1.5%, carbon (C ) <0.01%, the rest of the total impurities <1.0%, and the balance is copper (Cu).

[0044] Copper-based alloy powders for self-lubricating coatings: the raw materials used are commercially available: CuSi 16 Master alloy, CuSb 50 Master alloy, CuSn 16 master alloy, CuB 3 Master alloy, T1 oxygen-free copper (copper content ≥ 99.98wt.%). According to the formula ratio, put the raw materials into the crucible of high-frequency induction vacuum melting equipment, fully melt each alloy raw material at 1100℃~1150℃ and keep it warm for 10min, then release it from the furnace, and then use atomization powder making method in the pulverizer under high-purity argon gas The powder was prepared in a protective atmosphere, sieved, and the powder with a particle size range of 10 μm to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
surfaceaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for a self-lubricating antifriction wear-resistant coating of a suspension clamp of a transmission line. The preparation method comprises the following steps: by taking copper-based self-melting alloy powder as a coating raw material, spraying a porous coating, the porosity of which is 5-25%, to the surface of a clamp part through surface pre-treatment by adopting flame spraying; then infiltrating a carbon source to the porous coating through a solvent method; and then performing curing and polishing to prepare the self-lubricating antifriction wear-resistant coating, wherein the copper-based self-melting alloy respectively comprises the following components in percentages by mass: 5-25% of stannum (Sn), 0.5-10.0% of stibium (Sb), 0.5-5.0% of silicon (Si), 0.5-2.0% of boron (B), less than 0.01% of carbon (C), less than 1.0% of other impurities in total and the balance of copper (Cu). The coating prepared by the method can alleviate rapid wear of members of the suspension clamp of the transmission line and that among wires to a great extent, so that the service life of the suspension clamp of the transmission line is prolonged, and meanwhile, hard-wear damage to the wires caused by the clamp is prevented.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and relates to a method for manufacturing electric fittings and a surface coating. Background technique [0002] The transmission line clamp is one of the main components for connecting, fixing and supporting overhead conductors. Under the action of the environment (wind force, icing, rainfall, temperature changes, etc.), fixed-frequency vibration of towers, wire vibration, etc., the wire clip and the wire are in a permanent relative motion state. Over time, the wire and the wire clip are worn and damaged Deplete both or clamp components to failure. [0003] The clamps used in overhead transmission lines are mostly made of steel materials with surface hot-dip galvanized. The hot-dip galvanized layer on the surface is relatively soft, and it will be transformed into wear between the steel substrate and the aluminum conductor or the steel substrate and the steel substrate after the co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C4/06C23C4/129C23C4/18C22C9/02C22C9/00
CPCC22C9/00C22C9/02C23C4/06C23C4/18
Inventor 李辛庚苏建军李勇岳增武张振岳李文静陈素红傅敏
Owner ELECTRIC POWER RESEARCH INSTITUTE OF STATE GRID SHANDONG ELECTRIC POWER COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap