Corrosion-resistant long-acting antirust liquid

A rust-proof and corrosion-resistant technology, applied in the direction of metal material coating process, etc., can solve the problems of metal rust, water-based rust-proof solution for a short period of time, and troublesome follow-up procedures.

Inactive Publication Date: 2016-11-09
TIANCHANG RUNDA METAL ANTIRUST AUX
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Metals are easily corroded by the surrounding environment
People usually choose anti-rust oil or water-based anti-rust liquid for metal surface treatment, but anti-rust oil is not easy to remove, which will bring trouble t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of anti-corrosion long-acting anti-rust liquid, its raw material comprises by weight: 35 parts of composite corrosion inhibitors, 0.3 parts of sodium dodecylbenzene sulfonate, 0.2 parts of hydroxypropyl cellulose, 0.5 parts of polyethylene glycol, 0.1 part of emulsified silicone oil, 3 parts of sodium gluconate, 0.2 part of benzisothiazolinone, 54 parts of water;

[0016] Among them, the raw materials of the composite corrosion inhibitor include: phytic acid, sodium molybdate, diethanolamine, monoethanolamine borate, 2-methylbenzimidazoline, phytic acid, sodium molybdate, diethanolamine, monoethanolamine borate , The weight ratio of 2-methylbenzimidazoline is 1:0.8:1:4:4.

Embodiment 2

[0018] A corrosion-resistant and long-lasting antirust solution, its raw materials include by weight: 45 parts of composite corrosion inhibitor, 0.1 part of sodium lauryl sulfate, 0.4 part of hydroxypropyl cellulose, 0.3 part of polyethylene glycol, polyoxygen 0.3 part of propylene glyceryl ether, 1 part of sodium gluconate, 0.3 part of benzisothiazolinone, 50 parts of water;

[0019] Among them, the raw materials of the composite corrosion inhibitor include: phytic acid, sodium molybdate, diethanolamine, monoethanolamine borate, 2-methylbenzimidazoline, phytic acid, sodium molybdate, diethanolamine, monoethanolamine borate , The weight ratio of 2-methylbenzimidazoline is 2:0.6:2:2:6.

Embodiment 3

[0021] A kind of anti-corrosion long-term anti-rust liquid, its raw material comprises by weight: 38 parts of composite corrosion inhibitors, 0.25 parts of sodium dodecylbenzene sulfonate, 0.25 parts of hydroxypropyl cellulose, 0.45 parts of polyethylene glycol, 0.15 parts of polyoxypropylene glyceryl ether, 2.5 parts of sodium gluconate, 0.22 parts of benzisothiazolinone, 53 parts of water;

[0022] Among them, the raw materials of the composite corrosion inhibitor include: phytic acid, sodium molybdate, diethanolamine, monoethanolamine borate, 2-methylbenzimidazoline, phytic acid, sodium molybdate, diethanolamine, monoethanolamine borate , The weight ratio of 2-methylbenzimidazoline is 1.2:0.75:1.3:3.5:4.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses corrosion-resistant long-acting antirust liquid. Raw materials of the corrosion-resistant long-acting antirust liquid comprise, by weight, 35-45 parts of compound corrosion inhibitor, 0.1-0.3 parts of a surface active agent, 0.2-0.4 part of hydroxy propyl cellulose, 0.3-0.5 part of polyethylene glycol, 0.1-0.3 part of a defoaming agent, 1-3 parts of sodium gluconate, 0.2-0.3 part of benzisothiazolones and 50-54 parts of water, wherein raw materials of the compound corrosion inhibitor comprise phytic acid, sodium molybdate, diethanol amine, monoethanolamine borate and 2-methyl benzimidazoline. According to the corrosion-resistant long-acting antirust liquid, by means of cooperation of the phytic acid, the sodium molybdate, the diethanol amine, the monoethanolamine borate and the 2-methyl benzimidazoline, the film forming speed of a protective film is increased, the corrosion speed is decreased, the thickness of the protective film is increased, corrosion media are prevented from making contact with metal, and the corrosion-resistant long-acting antirust liquid is made to have good corrosion-resistant performance and long-acting antirust performance.

Description

technical field [0001] The invention relates to the technical field of antirust liquid, in particular to a corrosion-resistant long-term antirust liquid. Background technique [0002] Metals are easily corroded by the surrounding environment. People usually choose anti-rust oil or water-based anti-rust liquid for metal surface treatment, but anti-rust oil is not easy to remove, which will bring trouble to the subsequent process; water-based anti-rust liquid will not affect the subsequent process and is easy to clean, so it is widely used , but the anti-rust time of water-based anti-rust liquid is not long, which limits its use. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a corrosion-resistant long-acting anti-rust liquid, the present invention interacts with phytic acid, sodium molybdate, diethanolamine, monoethanolamine borate, and 2-methylbenzimidazoline Cooperate to increase t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/40
CPCC23C22/40
Inventor 林伟江海涛江海波江浩
Owner TIANCHANG RUNDA METAL ANTIRUST AUX
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap