Guar gum modified vinyl acetate low-solid and high-viscosity pressing plate adhesive and preparation method thereof

A vinyl acetate, guar gum technology, applied in the direction of adhesives, non-polymer adhesive additives, non-polymer organic compound adhesives, etc., can solve the problem of prolonged production process time, low solid content, and easy starch mold. and other problems, to achieve the effect of accelerating the water solubility, increasing the dispersion force, and improving the hydrophilicity.

Inactive Publication Date: 2016-10-12
顶立新材料科技股份有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To obtain products with low solid content and high viscosity, starch is usually added at the late stage of polymerization and then gelatinized, which prolongs the production process of the adhesive and causes unnecessary waste of energy. Starch is a physical change process in this process, and there is no interaction with acetic acid. Vinyl ester undergoes graft polymerization reaction, and there is a risk of delamination of the glue during storage
At the same time, because starch is easy to mold, a large amount of anti-mold agent needs to be added later, which increases a certain amount of cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Guar gum modified vinyl acetate low-solid and high-viscosity pressing plate adhesive and preparation method thereof
  • Guar gum modified vinyl acetate low-solid and high-viscosity pressing plate adhesive and preparation method thereof
  • Guar gum modified vinyl acetate low-solid and high-viscosity pressing plate adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Formula: total amount = 1000kg

[0020]

[0021]

[0022] Production Process:

[0023] a. Dissolve 0.3kg of ammonium persulfate in 9.7kg of water to obtain 10kg of ammonium persulfate solution; disperse 12kg of NMA-48% in 12kg of water to obtain 24kg of NMA aqueous solution; add 210kg of vinyl acetate and 12kg of methacrylic acid to the monomer tank The tank is mixed and stirred evenly to make 222kg mixed monomer;

[0024] b. Add the remaining 709.5kg of water into the reactor, start stirring, add 1kg BYK024, 1kgCO436, 1kg sodium acetate, 18kg hydroxypropyl guar gum, heat up to 60°C, stir and disperse for 90 minutes to fully dissolve the hydroxypropyl guar gum ;

[0025] c. Warm up to 72°C, add 4kg of ammonium persulfate solution prepared in step a, then add dropwise 222kg of mixed monomer prepared in step a and the remaining 6kg of ammonium persulfate solution at the same time, control the mixed monomer to drop in 3.0 hours, and persulfate The ammonium solutio...

Embodiment 2

[0027] Embodiment two formula: total amount=1000kg

[0028] Hydroxypropyl Guar Gum 19kg NMA - 48% 13kg BYK024 1.1kg Aluminum nitrate 3kg CO436 1.1kg citric acid 1.8kg Sodium acetate 1.1kg urea 6kg Ammonium persulfate 0.3kg TXIB 5kg vinyl acetate 220kg LEX fungicide 2kg Methacrylate 13kg water 713.6kg

[0029] Production Process:

[0030] a. Dissolve 0.3kg of ammonium persulfate in 9.7kg of water to obtain 10kg of ammonium persulfate solution; disperse 13kg of NMA-48% in 13kg of water to obtain 26kg of NMA aqueous solution; add 220kg of vinyl acetate and 13kg of methacrylic acid to the monomer tank The tank is mixed and stirred evenly to make 233kg mixed monomer;

[0031] b. Add the remaining 690.9kg of water into the reaction kettle, start stirring, add 1.1kg BYK024, 1.1kgCO436, 1.1kg sodium acetate, 19kg hydroxypropyl guar gum, heat up to 60°C, stir and disperse for 90 minutes to make hydrox...

Embodiment 3

[0034] Embodiment three formula: total amount=1000kg

[0035] Hydroxypropyl Guar Gum 20kg NMA - 48% 14kg BYK024 1.2kg Aluminum nitrate 4kg CO436 1.2kg citric acid 2kg Sodium acetate 1.2kg urea 8kg Ammonium persulfate 0.4kg TXIB 6kg vinyl acetate 230kg LEX fungicide 3kg Methacrylate 14kg water 695kg

[0036] Production Process:

[0037] a. Dissolve 0.4kg of ammonium persulfate in 13kg of water to obtain 13.4kg of ammonium persulfate solution; disperse 14kg of NMA-48% in 14kg of water to obtain 28kg of NMA aqueous solution; add 230kg of vinyl acetate and 14kg of methacrylic acid into the monomer tank The tank is mixed and stirred evenly to make 244kg mixed monomer;

[0038]b. Add the remaining 668kg of water into the reaction kettle, start stirring, add 1.2kg BYK024, 1.2kgCO436, 1.2kg sodium acetate, 20kg hydroxypropyl guar gum, heat up to 60°C, stir and disperse for 90 minutes to make hydroxyp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a guar gum modified vinyl acetate low-solid and high-viscosity pressing plate adhesive and a preparation method thereof. Main components of the guar gum modified vinyl acetate low-solid and high-viscosity pressing plate adhesive comprise tap water, modified guar gum, a de-foaming agent, a buffering agent, an emulsifier, an initiator, methacrylic acid, vinyl acetate, a self-cross-linking monomer, a plasticizer, a catalyst and a preservative. The modified guar gum is used as protective colloid; almost primary hydroxyl and secondary hydroxyl on a straight chain in a guar gum molecular structure are located at the outer side so that a hydrogen bond combining area is the largest; a process of increasing the amount of the polymerization initiator at an initial period and directly dropwise adding the monomer to polymerize is adopted and the homogeneous nucleation quantity is increased, so that the quantity of latex particles in a system is increased and a low-solid and high-viscosity adhesive product is prepared.

Description

technical field [0001] The invention relates to an adhesive preparation technology, in particular to a preparation method of a guar gum modified vinyl acetate low-solid and high-viscosity adhesive. Background technique [0002] Guar gum is a kind of vegetable gum extracted from leguminous plants, and its chemical composition is polygalactomannose. Guar gum is a macromolecular natural hydrophilic colloid, which belongs to natural galactomannan and is a natural thickener. Appearance is white to yellowish free-flowing powder, can be dissolved in cold water or hot water, and will form a jelly-like substance after contact with water to achieve the effect of rapid thickening. Guar gum is the most potent and water-soluble natural polymer known. At low concentrations, it can form highly viscous solutions; exhibits non-Newtonian rheological properties and forms acid-reversible gels with borax. Due to its unique properties, it is used in industries such as food, pharmaceuticals, pe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/02C09J4/00C09J4/06C09J11/04C09J11/06
CPCC09J4/00C09J4/06C09J11/04C09J11/06C08F251/00
Inventor 刘维均章勇生罗平徐建宋志强牟海燕
Owner 顶立新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More