A kind of ultra-low temperature metal passivation phosphating solution and preparation method thereof

A technology of metal passivation and phosphating solution, applied in the direction of metal material coating process, etc., can solve the problems of few breakthrough progress in phosphating technology, and achieve the effect of shortening production cycle, improving working environment and easy production.

Active Publication Date: 2018-10-19
安徽子西环保科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the end of World War II, there were few breakthroughs in phosphating technology, but steady development and improvement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An ultra-low temperature metal passivation phosphating solution, the components and the mass concentration of each component are as follows: phosphoric acid 100g / L, tartaric acid 2g / L, sodium chlorate 2g / L, sodium dihydrogen phosphate 3g / L, fluotitanic acid 6g / L L, ammonium citrate 8g / L, triethanolamine 6g / L, tannic acid 2g / L, sodium molybdate 3g / L, water-based polyurethane 8g / L, m-xylylenediamine 5g / L.

[0018] Weigh phosphoric acid, tartaric acid, sodium chlorate, dihydrogen phosphate, fluotitanic acid, ammonium citrate, triethanolamine, molybdate, water-based polyurethane and m-xylylenediamine according to the mass concentration, mix well, add water to 1L, Raise the temperature to 60°C and stir for 40 minutes, then add a surfactant and stir to obtain an ultra-low temperature metal passivation phosphating solution.

Embodiment 2

[0020] An ultra-low temperature metal passivation phosphating solution, the components and the mass concentration of each component are as follows: phosphoric acid 300g / L, tartaric acid 18g / L, sodium chlorate 10g / L, zinc dihydrogen phosphate 10g / L, fluotitanic acid 1g / L L, ammonium citrate 2g / L, triethanolamine 1g / L, dodecyltrimethylammonium bromide 10g / L, ammonium molybdate 12g / L, water-based polyurethane 8g / L, m-xylylenediamine 2g / L .

[0021] Weigh phosphoric acid, tartaric acid, sodium chlorate, dihydrogen phosphate, fluotitanic acid, ammonium citrate, triethanolamine, molybdate, water-based polyurethane and m-xylylenediamine according to the mass concentration, mix well, add water to 1L, Raise the temperature to 60°C and stir for 40 minutes, then add a surfactant and stir to obtain an ultra-low temperature metal passivation phosphating solution.

Embodiment 3

[0023] An ultra-low temperature metal passivation phosphating solution, the components and the mass concentration of each component are as follows: phosphoric acid 150g / L, tartaric acid 6g / L, sodium chlorate 4g / L, sodium dihydrogen phosphate 8g / L, fluotitanic acid 5g / L L, ammonium citrate 6g / L, triethanolamine 2g / L, dodecyltrimethylammonium bromide 4g / L, sodium molybdate 5g / L, water-based polyurethane 18g / L, m-xylylenediamine 3g / L .

[0024] Weigh phosphoric acid, tartaric acid, sodium chlorate, dihydrogen phosphate, fluotitanic acid, ammonium citrate, triethanolamine, molybdate, water-based polyurethane and m-xylylenediamine according to the mass concentration, mix well, add water to 1L, Raise the temperature to 60°C and stir for 40 minutes, then add a surfactant and stir to obtain an ultra-low temperature metal passivation phosphating solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses ultralow-temperature metal passivation phosphorizing liquid and a preparation method thereof. The ultralow-temperature metal passivation phosphorizing liquid comprises the following components in concentration by mass: 100-300 g / L of phosphoric acid, 2-18 g / L of tartaric acid, 2-10 g / L of sodium chlorate, 3-10 g / L of dihydric phosphate, 1-6 g / L of hexafluorotitanic acid, 2-8 g / L of ammonium citrate, 1-6 g / L of triethanolamine, 2-10 g / L of surface active agent, 3-12 g / L of molybdate, 8-20 g / L of waterborne polyurethane, and 2-5 g / L of m-xylylenediamine. The phosphorizing liquid contains no such harmful substances as chromate and nitrite, can reduce the working temperature of high-acidity phosphorizing liquid to 0-20 DEG C, needs no heating, saves a lot of energy, simplifies procedures, and shortens the production period. The phosphorizing liquid has special advantages on metal surface phosphorizing below 10 DEG C, is excellent in film forming performance, and reaches indoor rust preventing period of not less than one year.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment chemicals, and in particular relates to an ultra-low temperature metal passivation phosphating solution and a preparation method thereof. Background technique [0002] Passivation is a method to transform the metal surface into a state that is not easily oxidized, and to delay the corrosion rate of the metal. Corrosion is an electrochemical change process. There are a small amount of electric ions on the untreated metal surface. These electric ions will move from the high potential area (cathode) to the low potential area (anode), thus generating an electric current. Under the action of this current, it will accelerate the destructive attack on the metal and cause corrosion in the weak part of the metal potential. In layman's terms, it is rust. The mechanism of passivation can be explained by thin film theory, that is, passivation is considered to be due to the interaction between...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/44
CPCC23C22/44
Inventor 尤为
Owner 安徽子西环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com