Low-temperature resistance and high-compatibility mixed material and preparation method thereof

A mixed material and low-temperature resistant technology, which is applied in the field of low-temperature-resistant and highly compatible mixed materials and their preparation, can solve the problems of low-temperature resistance and limited PE content, and achieve low cost, good compatibility, and material compatibility Good results

Active Publication Date: 2016-08-31
WEIDIYA CHANGTAI TECH CO LTD
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent uses carbon fiber and polytetrafluoroethylene as corrosion-resistant modifiers to optimize the performance of PP materials. At the same time, maleic anhydride grafted polypropylene is used as a compatibilizer. The added PE content is limited and does not have low-temperature resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature resistance and high-compatibility mixed material and preparation method thereof
  • Low-temperature resistance and high-compatibility mixed material and preparation method thereof
  • Low-temperature resistance and high-compatibility mixed material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Prepare the raw materials for each component according to the table below:

[0030] Table 1 Composition list of mixed materials

[0031] raw material name

[0032] The steps to make the mixed material are as follows:

[0033] Weigh a certain amount of copolymerized PP and pour it into a mixing bucket, add white mineral oil (the amount added is 1% of the total weight of each component) and stir for 5 minutes, then add an appropriate amount of lubricant and antioxidant and stir for 5 minutes, add low-density PE Stir with the compatibilizer INTUNE for 10 minutes, and finally the mixture is obtained.

[0034] The compound is extruded, the extruding equipment is parallel extruding granulator in the same direction, the extruding temperature is 185-220°C, the screw speed is 280 rpm, then cooled, and finally pelletized to obtain a low temperature resistant and highly compatible compound Material.

[0035] Use the prepared low-temperature-resistant and high-compatib...

Embodiment 2

[0040] Prepare the raw materials for each component according to the table below:

[0041] Table 3 Composition list of mixed materials

[0042]

[0043]

[0044] The steps to make the mixed material are as follows:

[0045] Weigh a certain amount of copolymerized PP and pour it into a mixing bucket, add white mineral oil (the amount added is 2% of the total weight of each component) and stir for 5 minutes, then add an appropriate amount of lubricant and antioxidant and stir for 5 minutes, add low-density PE Stir with the compatibilizer INTUNE for 10 minutes, and finally the mixture is obtained.

[0046] The compound is extruded, the extruding equipment is parallel extruding granulator in the same direction, the extruding temperature is 185-220°C, the screw speed is 290 rpm, then cooled, and finally pelletized to obtain a low temperature resistant and high compatible compound Material.

[0047] Use the prepared low-temperature-resistant and high-compatible mixed materi...

Embodiment 3

[0052] Prepare the raw materials for each component according to the table below:

[0053]Table 5 Composition list of mixed materials

[0054] raw material name

Parts by mass (%)

Copolymerized PP

43

low density PE

53

Compatibilizer INTUNE

3

Lubricant PP Wax / PE Wax

0.25 / 0.25

Antioxidant 168 / 1010

0.25 / 0.25

[0055] The steps to make the mixed material are as follows:

[0056] Weigh a certain amount of copolymerized PP and pour it into the mixing tank, add white mineral oil and stir for 5 minutes (the amount of white mineral oil is 1% of the total weight of each component), then add an appropriate amount of lubricant and antioxidant and stir for 5 minutes, add low Density PE and compatibilizer INTUNE were stirred for 10 minutes, and finally the mixture was obtained.

[0057] The compound is extruded, and the extruding equipment is parallel extrusion granulator in the same direction, the extrusion temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-temperature resistance and high-compatibility mixed material. The mixed material is prepared from the following components in percentage by mass: 40-50% of copolymer PP, 40-55% of PE, 3-15% of compatilizer INTUNE, 0.5-2% of lubricant and 0.5-1.5% of antioxidant. The mixed material provided by the invention perfectly integrates the advantages of PP and PE, and has good compatibility, high low-temperature impact resistance and good performance in rigidity, toughness, chemical resistance, high-temperature resistance and processability; and a preparation method of the mixed material provided by the invention has the advantages of easiness in operation, low cost and good material performance and has an economic value.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a low-temperature resistant and highly compatible mixed material and a preparation method thereof. Background technique [0002] PP is one of the most widely used varieties of general-purpose thermoplastic resins, and is widely used in various fields of industrial production. PP is cheap and has excellent comprehensive properties, but the most prominent shortcoming that needs to be overcome is the low low-temperature impact strength, and it is prone to cracking under force when used in cold regions. [0003] At present, the common method is to add a toughening agent to PP. This method has no obvious improvement effect on low-temperature impact, and the cost is high, and the rigidity of the material decreases greatly. Adding PE to PP can also be used to improve low-temperature impact resistance. This method is the most simple and effective, and the cost is also low. How...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L23/06C08L23/12C08L53/00
CPCC08L23/06C08L23/14C08L2201/08C08L2205/025C08L2205/035C08L2205/08C08L2207/066C08L23/12C08L53/00
Inventor 连荣炳徐名智
Owner WEIDIYA CHANGTAI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap