High-temperature wear-resistant and corrosion-resistant steel powder for additive manufacturing and additive manufacturing method

A technology for additive manufacturing and corrosion-resistant steel, which is applied in the field of additive manufacturing to achieve the effects of higher hardness, good tempering stability, and significant thermal fatigue resistance

Active Publication Date: 2017-10-13
XIAN BRIGHT ADDTIVE TECH CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the high-temperature wear-resistant and corrosion-resistant steels used for additive manufacturing mainly include 316L, H13 and 17-4PH, etc., and almost no steel has the characteristics of wear resistance, impact resistance, high hardness and thermal fatigue resistance at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature wear-resistant and corrosion-resistant steel powder for additive manufacturing and additive manufacturing method
  • High-temperature wear-resistant and corrosion-resistant steel powder for additive manufacturing and additive manufacturing method
  • High-temperature wear-resistant and corrosion-resistant steel powder for additive manufacturing and additive manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Prepare high-performance high-temperature wear-resistant and corrosion-resistant steel powder for additive manufacturing, the mass percentage content of each element in the powder material is:

[0045] element

C

mn

Si

Cr

Ni

Mo

V

Nb

Fe

Wt.%

0.2

1.5

0.6

9.0

6.0

1.0

0.2

0.3

margin

[0046] Additive manufacturing methods are:

[0047] Steel powder materials with a particle size of 15-53 μm and a purity of ≥99.99% were kept at 120°C for 4 hours, and then put into the powder cylinder of the additive manufacturing equipment. Mill the surface of the H13 steel substrate with a size of 250mm (length) × 250mm (width) × 20mm (thickness) with a milling machine until the surface roughness is not greater than Ra6.3, and clean the surface of the substrate with acetone, and install it after drying. Into the additive manufacturing equipment fixed. Use the subsection software to obtain slices of each layer...

Embodiment 2

[0049] The steel powder in the above-mentioned embodiment 1 was replaced with the steel powder having the following component contents, and the parts were formed, and the other processes were the same.

[0050] element

Embodiment 3

[0052]The steel powder in the above-mentioned embodiment 1 was replaced with the steel powder having the following component contents, and the parts were formed, and the other processes were the same.

[0053] element

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
purityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature wear-resistant and corrosion-resistant steel powder for additive manufacturing, which contains the following elements in mass percent: C 0.1-0.3% Wt., Mn 1.0-1.5% Wt., Si 0.2-0.6% Wt ., Cr 5~9%Wt., Ni 2.0~6.0%Wt., Mo 1.0~1.5%Wt., V 0.2~0.4%Wt., Nb 0.3~0.7%Wt., the balance is Fe, the above elements The sum of the mass percentages is 100%. The method of using the steel powder for additive manufacturing is: put the above steel powder into the additive manufacturing equipment; divide the parts to be manufactured and set the laser process parameters as follows: output power 200-400W, spot diameter 0.06-0.1 mm, scanning speed 960-1500mm / s, track spacing 0.06-1.2mm; then import the subdivided program into the additive manufacturing equipment; fill the additive manufacturing equipment with high-purity argon, and finally print layer by layer, Finally, high-temperature wear-resistant and corrosion-resistant steel parts are obtained.

Description

technical field [0001] The invention belongs to the technical field of additive manufacturing, and in particular relates to a high-temperature wear-resistant and corrosion-resistant steel powder for additive manufacturing, and also relates to an additive manufacturing method using the powder material. Background technique [0002] High-temperature, wear-resistant and corrosion-resistant steel is a commonly used ferrous metal material with excellent physical, chemical and mechanical properties, and is widely used in construction, medical, national defense, mold and other fields. The traditional processing method of high-temperature wear-resistant and corrosion-resistant steel parts is mainly mechanical processing, which is a typical subtractive manufacturing process. The part preparation cycle is long and the material utilization rate is low. Especially because it has high hardness and high strength, traditional processing methods are difficult to process. , which greatly lim...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/18C22C38/08C22C38/12C22C38/44C22C38/46C22C38/48B22F3/105B22F1/00B33Y10/00B33Y70/00
CPCB22F1/0003C22C38/02C22C38/04C22C38/08C22C38/12C22C38/18C22C38/44C22C38/46C22C38/48B33Y10/00B33Y70/00B22F10/00B22F10/34B22F10/28B22F10/36B22F10/366B22F10/32Y02P10/25
Inventor 熊嘉锋赵晓明
Owner XIAN BRIGHT ADDTIVE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com