Heat-resistant sintered material excellent in oxidation resistance, high-temperature wear resistance, and salt corrosion resistance, and production method thereof

A wear resistance and oxidation resistance technology, applied in turbines, mechanical equipment, etc., can solve the problems of wear resistance deterioration, powder compressibility deterioration, oxidation resistance, salt corrosion resistance problems, etc. Effects of excellent corrosion and heat resistance, and excellent wear resistance

Active Publication Date: 2020-01-14
DIAMET CORP
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] However, if the precipitation of high-Cr carbide particles is given priority, the amount of Cr in the parent phase will decrease, so there will be problems in oxidation resistance and salt corrosion resistance. If the number of high-Cr carbide particles is reduced, there will be wear resistance Deterioration problem
[0017] In addition, if the amount of Cr in the entire alloy is increased in the sintered material, the compressibility of the powder will deteriorate, and there is a problem that it cannot be molded into the desired shape.
[0018] In addition, in the structure in which high-Cr carbide particles are precipitated in the parent phase, if the amount of high-Cr carbide particles precipitated is increased, the wear resistance of the sintered material itself is good, but the loss of the counterpart material due to sliding increases. The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resistant sintered material excellent in oxidation resistance, high-temperature wear resistance, and salt corrosion resistance, and production method thereof
  • Heat-resistant sintered material excellent in oxidation resistance, high-temperature wear resistance, and salt corrosion resistance, and production method thereof
  • Heat-resistant sintered material excellent in oxidation resistance, high-temperature wear resistance, and salt corrosion resistance, and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0110] "Example 1"

[0111] As raw material powder, Fe-25Cr-20Ni alloy powder, Cr-40Fe alloy powder, Ni-12P alloy powder are prepared, and these raw material alloy powders are blended to make it into the final composition shown in the following tables 1-3, and V After mixing in a type mixer for 30 minutes, press molding was performed at a molding pressure of 588 MPa to produce a cylindrical green compact.

[0112] Next, this green compact was sintered at a temperature of 1250 to 1280° C. for 1.5 hours in a vacuum atmosphere to obtain heat-resistant sliding materials (sample Nos. 1 to 29).

[0113] In addition, Fe-25Cr-2Mo alloy powder, Cr-40Fe alloy powder, and Fe-27P alloy powder were prepared as raw material powders, and these raw material alloy powders were blended to obtain the final composition shown in Table 4 below, so as to be compatible with Heat-resistant sliding materials (sample Nos. 30 to 35) were obtained in the same manner as in sample Nos. 1 to 29.

[0114] A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
Login to View More

Abstract

In this heat-resistant sintered material and its manufacturing method, it is an object to obtain a heat-resistant sintered material excellent in oxidation resistance, high-temperature wear resistance, and salt erosion resistance. The heat-resistant sintered material is characterized in that it has a composition containing Cr: 25-50%, Ni: 2-25%, P: 0.2-1.2% in mass%, and the balance is composed of Fe and unavoidable impurities; and Has a structure with a Fe-Cr parent phase and a hard phase composed of Cr-Fe alloy grains dispersed in the Fe-Cr parent phase; the amount of Cr in the Fe-Cr parent phase is expressed in mass % 24-41%, the amount of Cr in the hard phase is 30-61% by mass %; and the effective porosity is 2% or less.

Description

technical field [0001] The present invention relates to a heat-resistant sintered material excellent in oxidation resistance, high-temperature wear resistance, and salt corrosion resistance, and a method for producing the same. [0002] This application claims priority based on Japanese Patent Application No. 2015-066748 for which it applied in Japan on March 27, 2015, and uses the content here. Background technique [0003] Among internal combustion engines, there is known a turbocharger that utilizes the energy of exhaust gas to rotate a turbine at a high speed, drives a centrifugal compressor with the rotational force, and sends compressed air into the engine to improve the performance of the internal combustion engine. Thermal efficiency. [0004] A turbocharger attached to an internal combustion engine is provided with a nozzle mechanism and a valve mechanism that divide a part of the exhaust gas to adjust the inflow amount of the exhaust gas to the turbine. [0005] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C22C30/00C22C33/02B22F1/00
CPCC22C30/00C22C38/00B22F5/009C22C1/045C22C33/0214C22C33/0285B22F2998/10C22C27/06C22C38/22C22C38/44C22C38/002C22C38/40B22F1/00B22F1/09B22F3/02B22F3/10B22F3/16B22F2301/35
Inventor 加藤健一水野达规宫原正久
Owner DIAMET CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com