Environment friendly aluminum electrode anticorrosive paint and preparation method thereof

A technology for anti-corrosion coatings and aluminum electrodes, which is applied in the direction of anti-corrosion coatings, coatings, and devices for coating liquids on the surface. It can solve the problems of complex modification methods and difficult industrial production, and achieve improved anti-corrosion performance and easy operation. Effect

Inactive Publication Date: 2016-08-03
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Regarding the functional modification of mesoporous SiO2 microspheres, some studies have used the method of layer-by-layer self-assembly to form multi-layer polyelectrolytes on the surface of mesoporous SiO2 microspheres. The purpose of controlled release of corrosion agent; but because this modification method is more complicated, it is not easy for industrial production, so the development of simple and novel method of surface modification of mesoporous SiO2 microspheres has become the research direction of people

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] A kind of environment-friendly aluminum electrode anticorrosion paint, it is made up of the raw material of following weight part:

[0026] Beeswax 2, cetyltrimethylammonium bromide 0.7, magnesium sulfate 0.05, benzotriazole 0.06, octylphenol polyoxyethylene ether 1.7, dodecylamine 0.3, ethyl orthosilicate 46, dodecyl Alkyl trichlorosilane 0.3, zirconium n-propoxide 13, ethyl acetoacetate 7, isopropanol 57, silane coupling agent kh56010, glyceryl carboxylate 0.1, calcium palmitate 0.6, sodium fluorosilicate 1, zinc acetylacetonate 0.2, lauryl dimethyl amine oxide 0.2.

[0027] A kind of preparation method of described environment-friendly aluminum electrode anticorrosion coating comprises the following steps:

[0028] (1) Mix the above cetyltrimethylammonium bromide and sodium fluorosilicate, add it to deionized water 37 times the weight of the mixture, stir evenly, add 3mol / l sulfuric acid dropwise, adjust the pH to 2, Insulated and stirred at 60°C for 4 minutes, mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly aluminum electrode anticorrosion coating, which is composed of the following raw materials in parts by weight: beeswax 2-3, hexadecyltrimethylammonium bromide 0.7-1, magnesium sulfate 0.05-0.06, benzene Triazole 0.06‑0.07, octylphenol polyoxyethylene ether 1.7‑2, dodecylamine 0.3‑0.5, tetraethyl orthosilicate 46‑50, n-dodecyltrichlorosilane 0.3‑0.4, n-propanol Zirconium 13‑20, ethyl acetoacetate 7‑10, isopropanol 57‑60, silane coupling agent kh56010‑13, carboxyglycerin 0.1‑0.2, calcium palmitate 0.6‑2, sodium fluorosilicate 1‑2 , Zinc acetylacetonate 0.2‑0.3, lauryl dimethylamine oxide 0.2‑0.4. The paint of the invention does not contain volatilization of toxic and harmful substances, and has good safety and environmental protection.

Description

technical field [0001] The invention relates to the technical field of electrode anticorrosion, in particular to an environment-friendly aluminum electrode anticorrosion coating and a preparation method thereof. Background technique [0002] The anti-corrosion of metal coating is one of the important methods of metal anti-corrosion, and the coating itself only plays a passive physical isolation role, that is, to prevent the direct contact between the metal surface and the environmental medium, because there may be some defects (such as micropores) inside the coating ), so the metal cannot be adequately protected. In order to improve its active corrosion resistance, inorganic or organic corrosion inhibitors are added directly or indirectly. The corrosion inhibitor added directly may interact with the coating, reducing the strength of the coating and causing unnecessary waste. The indirect method is mainly to load the corrosion inhibitor through the carrier material to preven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/08C09D7/12B05D1/18B05D7/14
CPCC09D1/00B05D1/18B05D7/14C09D5/08C09D7/40
Inventor 王和山
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products