Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Pure-white modal wide pile fabric and production method thereof

A production method and fabric technology, applied in the direction of fabric, liquid/gas/steam open fabric treatment, fabric elongation, etc., can solve the problems of morphological stability decline, high shrinkage, affecting the performance of modal fabrics, etc., to achieve The product has excellent performance, easy operation, soft and plump feel

Active Publication Date: 2016-07-20
NANTONG JINSHAIDA SPECIAL FAB CO LTD
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

High shrinkage and reduced shape stability after moisture absorption affect the performance of modal fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The width of the grey fabric of satin weave fabric is 108 inches, the yarn count is 60s×60s, and the density is 182×118 threads / inch;

[0015] A production method of pure white modal wide suede fabric, including light singeing → enzymatic desizing of jigger dyeing machine → boiling and bleaching of Bugong tea saponin in jigger dyeing machine → drying → raising → shrink-proof finishing → tentering → Mechanical pre-shrinking→inspect the packaging; when the bog tea saponin is boiled and bleached, the composition of the boiling and bleaching liquid is: bog tea saponin 4% (owf), efficient refining agent TF-125T5g / L, hydrogen peroxide (100%) 2.5~ 2.8g / L, oxygen bleaching stabilizer TF-122B1~1.3g / L, bath ratio 2:1; scouring and bleaching process: 1 channel in greenhouse → 4 channels at 95~98℃→4 channels at 95~98℃ hot water→70 ~80℃ hot water wash 2 times→cold water wash 2 times.

[0016] When raising, the front of the fabric is raised six times, the cylinder speed is 75rpm, the clo...

Embodiment 2

[0020] The width of the grey fabric of satin weave fabric is 108 inches, the yarn count is 40s×40s, and the density is 144×90 threads / inch.

[0021] A production method of pure white modal wide suede fabric, including light singeing → enzymatic desizing of jigger dyeing machine → boiling and bleaching of Bugong tea saponin in jigger dyeing machine → drying → raising → shrink-proof finishing → tentering → Mechanical pre-shrinking→inspect packaging; when Bogong tea saponin is boiled and bleached, the composition of the boiling and bleaching liquid is: Bogong tea saponin 4% (owf), efficient refining agent TF-125T5g / L, hydrogen peroxide (100%) 2.8~ 3g / L, oxygen bleaching stabilizer TF-122B 1.3~1.5g / L, bath ratio 2:1; scouring and bleaching process: 1 channel in the greenhouse→4 channels at 95~98℃→4 channels in hot water at 95~98℃→ 70~80℃ hot water wash 2 times→cold water wash 2 times.

[0022] When raising the fabric, the front side of the fabric is raised four times, the cylinder spe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
reflectanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pure-white modal wide pile fabric and a production method thereof.The technical process includes: slight singeing, enzyme desizing by a dye jigger, Bu-gong tea saponin scouring and bleaching by the dye jigger, drying, napping, anti-shrinking finishing, tentering, mechanical pre-shrinking, and inspecting and packaging.The front of this fabric is provided with a layer of loose piles, and after weft-wise washing, the fabric is -3% to +1.0% in size variation rate, > / =82% in reflectivity and > / =260 N in breaking strength.The process is simple, operating is convenient, and the product has excellent properties.

Description

Technical field [0001] The invention relates to a production method of pure white modal wide suede fabric. Background technique [0002] Modal fiber is a high wet modulus regenerated cellulose fiber that combines the luxurious texture of natural fiber with the practicality of synthetic fiber. It has the softness of cotton, the luster of silk, the smoothness of linen, and its water absorption and air permeability are better than cotton. Its dry strength is close to polyester, and its wet strength is higher than ordinary viscose. The wide suede fabric is used for bedding, has a pleasant soft touch feeling and excellent durability, and can increase the warm touch in winter. However, since the moisture absorption capacity of modal fiber is 50% higher than that of cotton fiber, the shrinkage rate of modal fiber fabric is relatively large, and the shape stability after moisture absorption also decreases. The FZ / T14013-2009 "Modal Fiber Printing and Dyeing Fabric" standard stipulates ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D03D13/00D06C9/00D06B3/32D06C3/00D06B9/00D03D15/225
CPCD03D13/00D03D15/00D06B3/32D06B9/00D06C3/00D06C9/00
Inventor 欧卫国薛鹏飞王月华徐建华葛忠平杨莹莹黄颖杨静新
Owner NANTONG JINSHAIDA SPECIAL FAB CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com