Preparation method of blocked organosilicone waterborne polyurethane anti-fluffing-and-pilling agent

A pilling agent, silicone water-based technology, applied in the field of preparation of anti-pilling agent, can solve the problems of modified polyurethane such as limited adaptability, easy yellowing, affecting hand feel, etc., to improve hand feel and water resistance, and not easy to yellow change, obvious effect

Inactive Publication Date: 2016-06-22
南通曙光染织有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Purpose of the invention: In order to overcome the limitations of the adaptability of the modified polyurethane prepared by the prior art, which affects the hand feeling, stability and easy yellowing, the invention provides a block organosilicon water-based polyurethane anti-pilling agent and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of blocked organosilicone waterborne polyurethane anti-fluffing-and-pilling agent
  • Preparation method of blocked organosilicone waterborne polyurethane anti-fluffing-and-pilling agent
  • Preparation method of blocked organosilicone waterborne polyurethane anti-fluffing-and-pilling agent

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0036] A block organosilicon water-based polyurethane anti-pilling agent, the block organosilicon water-based polyurethane anti-pilling agent is composed of the following components in parts by weight: hydroxyl-terminated silicone oil: 20 parts, Isophor Ketone diisocyanate: 7 parts, dimethylolpropionic acid: 1.5 parts, 1,4-butanediol: 0.2 parts, dibutyltin dilaurate: 0.20 parts, triethylamine: 1 part, acetone: 10 parts , water: 90 parts.

[0037] A preparation method according to the described block organosilicon water-based polyurethane anti-pilling agent, adding the dehydrated hydroxyl-terminated silicone oil, dibutyltin dilaurate and isophorone diisocyanate into the reaction kettle, Heating and reacting for 1 hour, then adding dimethylol propionic acid and 1,4-butanediol, reacting for 1.5 hours; adding an appropriate amount of acetone to adjust the viscosity, adding triethylamine to neutralize after cooling down, stirring rapidly for 30 minutes, and finally adding water for...

specific Embodiment 2

[0042] A block organosilicon water-based polyurethane anti-pilling agent, the block organosilicon water-based polyurethane anti-pilling agent is composed of the following components in parts by weight: hydroxyl-terminated silicone oil: 30 parts, Isophor Ketone diisocyanate: 15 parts, dimethylolpropionic acid: 2.5 parts, 1,4-butanediol: 0.5 parts, dibutyltin dilaurate: 0.24 parts, triethylamine: 2 parts, acetone: 20 parts , water: 120 parts.

[0043] A preparation method according to the described block organosilicon water-based polyurethane anti-pilling agent, adding the dehydrated hydroxyl-terminated silicone oil, dibutyltin dilaurate and isophorone diisocyanate into the reaction kettle, Heating and reacting for 1 hour, then adding dimethylol propionic acid and 1,4-butanediol, reacting for 1.5 hours; adding an appropriate amount of acetone to adjust the viscosity, adding triethylamine to neutralize after cooling down, stirring rapidly for 30 minutes, and finally adding water ...

specific Embodiment 3

[0048] A block organosilicon water-based polyurethane anti-pilling agent, the block organosilicon water-based polyurethane anti-pilling agent is composed of the following components in parts by weight: hydroxyl-terminated silicone oil: 27 parts, Isophor Ketone diisocyanate: 12 parts, dimethylolpropionic acid: 1.9 parts, 1,4-butanediol: 0.3 parts, dibutyltin dilaurate: 0.22 parts, triethylamine: 1.4 parts, acetone: 17 parts , water: 107 parts.

[0049] A preparation method according to the described block organosilicon water-based polyurethane anti-pilling agent, adding the dehydrated hydroxyl-terminated silicone oil, dibutyltin dilaurate and isophorone diisocyanate into the reaction kettle, Heating and reacting for 1 hour, then adding dimethylol propionic acid and 1,4-butanediol, reacting for 1.5 hours; adding an appropriate amount of acetone to adjust the viscosity, adding triethylamine to neutralize after cooling down, stirring rapidly for 30 minutes, and finally adding wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a blocked organosilicone waterborne polyurethane anti-fluffing-and-pilling agent. The preparation method includes following steps: preparing terminated hydrogen group modified silicone oil; preparing terminated hydroxyl blocked silicone oil; preparing the blocked organosilicone waterborne polyurethane anti-fluffing-and-pilling agent. The preparation method is simple in process, and the agent prepared by the method is high in film forming strength, compactness and continuity; fabric finished by using the agent is not clammy and free of adhesion with a roller in the process of application, anti-fluffing-and-pilling effect is improved obviously, and the fabric after being finished is good in hand feeling.

Description

technical field [0001] The invention relates to a preparation method of an anti-pilling agent, in particular to a preparation method of a block organosilicon water-based polyurethane anti-pilling agent. The block organosilicon water-based polyurethane anti-pilling agent is mainly used for wool, Anti-pilling finishing of cashmere fabrics, polyester, cotton knitted fabrics and their blended fabrics. Background technique [0002] Polyurethane (referred to as PU), that is, polyurethane, is a polymer compound containing -NHCOO- unit structure. In 1937, German chemist Otto Bayer prepared polyurethane by the addition of isocyanate and active hydrogen compound, thus laying the foundation of polyurethane chemistry. In the 1950s, solvent-based polyurethane coatings were first applied in the dyeing and finishing industry in Europe. With the enhancement of people's awareness of environmental protection, water-based polyurethane has gradually replaced solvent-based polyurethane in rece...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/75C08G18/65C08G18/61C08G18/34C08G18/32D06M15/564D06M101/12D06M101/32D06M101/06
CPCC08G18/755C08G18/0823C08G18/3206C08G18/348C08G18/61C08G18/6511C08G18/6541D06M15/564D06M2101/06D06M2101/12D06M2101/32D06M2200/25D06M2200/35D06M2200/50
Inventor 王海峰叶伟管永华贾维妮武迪张晓玲
Owner 南通曙光染织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com