Organic multi-pore supported catalyst as well as synthesis method and application thereof

A supported catalyst, hierarchical pore technology, applied in the preparation of organic compounds, organic compound/hydride/coordination complex catalysts, organic chemistry, etc., can solve the problems of backward research, lack of synthesis mechanism and preparation method, etc. , to achieve the effect of good universality, excellent multi-channel connectivity, and controllable size

Inactive Publication Date: 2016-05-25
EAST CHINA NORMAL UNIVERSITY
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the research on organic hierarchical porous polymers is still in its infancy, and the research is relatively backward, and a general synthesis mechanism and preparation method have not yet been formed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic multi-pore supported catalyst as well as synthesis method and application thereof
  • Organic multi-pore supported catalyst as well as synthesis method and application thereof
  • Organic multi-pore supported catalyst as well as synthesis method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Embodiment 1 The synthesis of the precursor of organic hierarchical porous loaded organic amine catalyst

[0064] (a) Synthesis of PGM main chain:

[0065] Glycidyl methacrylate (2ml), azobisisobutyronitrile (AIBN, 2.4mg), RAFT reagent (36mg), and benzene (2ml) were added to the reaction test tube, and the reaction was sealed at 60°C after removing oxygen. After the reaction, it was precipitated in methanol. Dichloromethane dissolved. NMR results showed that its degree of polymerization was 250.

[0066] (b) Hydrolysis of the PGM backbone:

[0067] The main chain (1 g) synthesized in step 1 was dissolved in tetrahydrofuran (THF, 20 ml), glacial acetic acid (40 ml), and 60 ml of water was slowly added at 60°C. Reacted for 24h, and precipitated in ether after the reaction. dissolved in methanol.

[0068] (c) Synthesis of P(GM-g-LA):

[0069] Dissolve 50mg of hydrolyzed PGM in 5ml of dry N,N-dimethylformamide, add 1620mg of recrystallized D,L-lactide, and then add 4...

Embodiment 2

[0076] Synthesis of embodiment 2 organic hierarchical porous supported organic amine catalyst

[0077] In a round-bottomed flask, 70 mg of P(GM-g-LA-g-TBOCa-g-St) prepared in Example 1 was dissolved in dry 7 ml of 1,2-dichloroethane, and after deoxygenation, 133 uL ( 1.5mmol) of dimethyl formal and 243mg (6mmol) of ferric chloride were reacted at 80°C for 14h. After the end, the obtained insoluble solid was washed with water and methanol respectively until the supernatant was colorless. Disperse the insoluble solid in 6ml 1,4-dioxane, add 0.6ml HCl solution, and react at room temperature for 12h. After the end, the insoluble solids were washed with water and methanol respectively until the supernatant was neutral. Dry in vacuum at 50°C for 24h. Figure 5 Infrared schematic diagram showing the process of cross-linking hydrolysis of organic hierarchical porous supported catalyst, compared with (A), 1758cm in (C) -1 The carbonyl characteristic peak of polylactic acid disappear...

Embodiment 3

[0078] Example 3 Catalysts of organic hierarchically porous loaded organic amines (amino groups) and organic small molecule catalysts (n-butylamine) catalyze the reaction of benzaldehyde and ethyl cyanoacetate in catalytic toluene solution

[0079] In a reaction flask, 5 mg of the organic hierarchically porous supported catalyst loaded with amino groups was dispersed and dissolved in 2.3 ml of toluene, and 17.5 ul (0.17 mmol) of benzaldehyde and 74 ul (0.68 mmol) of ethyl cyanoacetate were added. React at 80°C for 45min. The reaction solution was obtained by centrifugation, and the GC-MS result showed that the conversion rate of benzaldehyde was 97% after 15min, as figure 1 as shown in a.

[0080] Described reaction is shown in following reaction formula (II):

[0081]

[0082] Benzaldehyde (0.17mmol), ethyl cyanoacetate (0.68mmol) and organic hierarchically porous supported catalyst (30mg) were reacted in toluene (2.3ml) at 80°C for 45min.

[0083] In a reaction flask,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an organic multi-pore supported catalyst as well as a synthesis method and application thereof. The synthesis method comprises the following steps: firstly, synthesizing a precursor of the organic multi-pore supported catalyst, namely (2-acrylamido-ethyl) tert-butyl carbamate-modifying core-shell polylactic acid-polystyrene bottle brush macromolecules; then carrying out a friedel-crafts hyper-crosslinking reaction on the precursor by taking dimethoxymethane as a crosslinking agent and anhydrous ferric chloride as a catalyst; then carrying out hydrolysis to remove cores and deprotection to synthesize the organic multi-pore supported catalyst, namely the organic multi-pore supported catalyst loaded with organic amine. The invention further provides the application of the organic multi-pore supported catalyst loaded with organic amine in a catalytic Knoevenagel condensation reaction.

Description

technical field [0001] The invention belongs to the technical field of polymer synthesis, relates to the technical field of polymer-loaded catalysts, in particular to the synthesis and application of a catalyst for organic hierarchical porous-loaded organic amines used to catalyze oil-soluble organic reactions. Background technique [0002] Solid-phase (heterogeneous) catalysts have been widely used in typical organic reactions such as oxidation, reduction, and addition in recent years. Among them, the supported solid base has attracted more and more attention in organic synthesis due to its outstanding advantages, such as high activity, high selectivity, less side reactions, high yield, and can avoid the reaction under homogeneous conditions. Mixture; to overcome the defect that small molecule catalysts are unstable and cause increased by-products; easy to operate, easy to post-treat, the catalyst can be recovered by simple centrifugation or filtration, and can be recycled ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J31/06B01J35/10C07C253/30C07C255/41C07D307/54C07C255/34C07C255/37C08G83/00
CPCC07C253/30C07D307/54C08G83/005B01J31/06B01J35/618B01J35/617B01J35/638C07C255/41C07C255/34C07C255/37
Inventor 黄琨张慧熊林峰何紫东钟爱青周铭洪
Owner EAST CHINA NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com