Abrasion-proof sheet metal and preparation method thereof

A technology of metal sheet and high temperature resistance, which is applied in the field of wear-resistant materials production, can solve the problems of poor oxidation resistance, high friction loss, multiple fragmentation, etc., and achieve the effect of improving impact value, long life and good wear resistance

Inactive Publication Date: 2016-04-20
安徽创新电磁离合器有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] However, traditional wear-resistant metals cannot adapt well to this harsh grinding environment. Especially in high-temperature environments, they are prone to high friction loss, multiple deformations, and multiple breakages, which have a great impact on their service life. In order to adapt to this harsh working condition and achieve a better grinding effect, it is necessary to find a high temperature resistant, strong impact resistant, strong corrosion resistant, etc., and the existing wear-resistant metal sheets generally have poor oxidation resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A wear-resistant metal sheet, the components and weight percentages are: C: 2.85%, Si: 0.47%, Mn: 0.34%, Mu: 0.2%, Cr: 11.5%, S: 0.018%, P: ≤0.025% , Mo: 0.9%, V: 0.09%, Ti: 0.3%, Cu: 0.5%; the balance is Fe.

[0024] The preparation method comprises the following steps:

[0025] 1. Raw materials are smelted at a temperature of 1490°C;

[0026] 2. Constant temperature pouring, the pouring temperature is 1440°C;

[0027] 3. Heat treatment: first heat at 700°C for 7 hours, then raise the temperature to 960°C, quench in 110°C quenching oil for 7 minutes, and temper at 330°C for 8 hours.

[0028] This technical solution: HRC: 60~60; impact value: ≥6.5J / c㎡; falling ball impact fatigue life ≥40,000 times; strong corrosion resistance, ultra-high temperature resistance.

[0029] It can be seen from the above that the metal sheet meets the performance requirements in all aspects.

Embodiment 2

[0031] A wear-resistant metal sheet, the components and weight percentages are: C: 2.22%, Si: 0.45%, Mn: 0.57%, Mu: 0.4%, Cr: 12.0%, S: 0.012%, P: ≤0.025% , Mo: 1.2%, V: 0.08%, Ti: 0.5%, Cu: 0.7%; the balance is Fe.

[0032] The preparation method comprises the following steps:

[0033] 1. Raw materials are smelted at a temperature of 1550°C;

[0034] 2. Constant temperature pouring, the pouring temperature is 1500℃;

[0035] 3. Heat treatment: first heat at 710°C for 8 hours, then raise the temperature to 980°C, quench in quenching oil at 130°C for 11 minutes, and temper at 350°C for 8 hours.

[0036] This technical solution: HRC: 61~62; impact value: ≥6.8J / c㎡; falling ball impact fatigue life ≥40,000 times; strong corrosion resistance, ultra-high temperature resistance.

[0037] It can be seen from the above that the metal sheet has reached the performance requirements in all aspects

Embodiment 3

[0039] A wear-resistant metal sheet, the components and weight percentages are: C: 2.15%, Si: 0.45%, Mn: 0.60%, Mu: 0.6%, Cr: 13.5%, S: 0.014%, P: ≤0.024% , Mo: 1.4%, V: 0.10%, Ti: 0.5%, Cu: 0.8%; the balance is Fe.

[0040] The preparation method comprises the following steps:

[0041] 1. Raw materials are smelted at a temperature of 1550°C;

[0042] 2. Constant temperature pouring, the pouring temperature is 1500℃;

[0043] 3. Heat treatment: first heat at 720°C for 10 hours, then raise the temperature to 990°C, quench in 140°C quenching oil for 15 minutes, and temper at 380°C for 10 hours.

[0044] This technical solution: HRC: 63~65; impact value: ≥7.0J / c㎡; falling ball impact fatigue life ≥40,000 times; strong corrosion resistance, super high temperature resistance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides abrasion-proof sheet metal and a preparation method thereof, and relate to the technical field of production of abrasion-proof materials. The abrasion-proof sheet metal is prepared from the following components in percentage:1.9-3.1% of C, 0.4-0.6% of Si, 0.2-0.8% of Mn, 0.2-0.6% of Mu,11.5-13.5% of Cr, S which is smaller than or equal to 0.10%, P which is smaller than or equal to 0.10%, 0.5-1.5% of Mo, 0.05-0.15% of V, 0.1-1.0% of Ti, 0.3-1.0% of Cu, and the balance being Fe. The preparation method comprises the following steps of melting raw materials; performing constant-temperature pouring; performing heat treatment, heating the sheet metal shaped through pouring for 3-5 hours at the temperature of 700-720 DEG C, performing warming until the temperature is 800-900 DEG C, performing quenching in quenching oil for 7-10 minutes at the temperature of 90-100 DEG C, and then performing tempering for 6-10 hours at the temperature of 300-350 DEG C; and performing heat treatment once again, putting the sheet metal obtained after the heat treatment in high-temperature-resistant silicone oil for soaking for 3-5 hours, fishing out the sheet metal, and removing external silicone oil. The abrasion-proof sheet metal disclosed by the invention is impact-resistant, long in service life, and good in abrasion resistance, so that the abrasion-proof sheet metal can be used in serious environment, and can resist strong corrosion and ultrahigh temperature.

Description

Technical field: [0001] The invention relates to the technical field of wear-resistant material production, in particular to a wear-resistant metal sheet and a preparation method thereof. Background technique: [0002] However, traditional wear-resistant metals cannot adapt well to this harsh grinding environment. Especially in high-temperature environments, they are prone to high friction loss, multiple deformations, and multiple breakages, which have a great impact on their service life. In order to adapt to this harsh working condition and achieve a better grinding effect, it is necessary to find a high temperature resistant, strong impact resistant, strong corrosion resistant, etc., and the existing wear-resistant metal sheets generally have poor oxidation resistance. Invention content: [0003] The technical problem to be solved by the present invention is to provide a wear-resistant metal sheet with impact resistance, high temperature resistance, corrosion resistance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/22C22C38/60C22C38/24C22C38/28C22C38/20C22C38/02C22C38/04C21D1/18C21D6/00
CPCC22C38/22C21D1/18C21D6/002C21D6/005C21D6/008C22C38/002C22C38/02C22C38/04C22C38/20C22C38/24C22C38/28C22C38/60
Inventor 阮社良
Owner 安徽创新电磁离合器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com