Polyacrylate UV adhesive and preparation method thereof

A polyacrylate and stabilizer technology, applied in the direction of ester copolymer adhesives, adhesive types, fibrous fillers, etc., can solve problems such as poor wear resistance, achieve improved wear resistance, enhanced compatibility, Reduce the effect of agglomeration

Inactive Publication Date: 2016-02-10
SUZHOU GAIDE FINE MATERIALS CO LTD
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the UV curable pressure-sensitive adhesive prepared by the invention has the same disadvantage of poor abrasion resistance as the existing polyacrylate UV adhesive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of polyacrylate UV adhesive, by weight, is made of following components: polyacrylate 55 parts, ETPTA 10 parts, HMPF 7 parts, phenolic stabilizer 1.2 parts, methacrylic acid phosphate 2.5 parts, organic pigment 1.4 parts 2.5 parts of hydrogenated castor oil, 1.8 parts of polydimethylsiloxane, 2.5 parts of zinc oxide, 5 parts of PTFE, and 2.5 parts of chromium oxide.

[0026] The steps of its preparation method are as follows:

[0027] (1) Dissolve stearic acid in toluene and disperse evenly, move to a constant temperature oil bath and heat to 90°C, add chromium oxide, stir and react at 400rpm for 50 minutes, move to an ultrasonic disperser for ultrasonic dispersion for 30 minutes, take out Afterwards, suction filtration, repeated washing with distilled water to remove unreacted stearic acid and toluene, drying in a blower dryer at 90°C for 5 hours, and grinding to obtain modified chromium oxide for future use;

[0028] (2) Add polyacrylate to the stirring tank, ...

Embodiment 2

[0030] A kind of polyacrylate UV glue, by weight, is made of following components: polyacrylate 70 parts, ETPTA 15 parts, HMPF 2 parts, phenolic stabilizer 1.8 parts, methacrylate phosphate 3.5 parts, organic pigment 1.6 parts 2.8 parts of fumed silica, 1.6 parts of polydimethylsiloxane, 2 parts of zinc oxide, 7 parts of PTFE, and 4.5 parts of chromium oxide.

[0031] Its preparation method is the same as Example 1.

Embodiment 3

[0033] A kind of polyacrylate UV glue, by weight, is made up of following components: polyacrylate 72 parts, ETPTA 14 parts, HMPF 3 parts, phenolic stabilizer 1 part, methacrylate phosphate 3 parts, organic pigment 1.8 3 parts, hydrogenated castor oil 3 parts, polydimethylsiloxane 1.5 parts, zinc oxide 3 parts, PTFE 7.5 parts, chromium oxide 4 parts.

[0034] Its preparation method is the same as Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polyacrylate UV adhesive. The polyacrylate UV adhesive is prepared from, by weight, 50-72 parts of polyacrylate, 10-15 parts of reactive diluents, 2-7 parts of photoinitiator, 1-2 parts of stabilizer, 2-4 parts of adhesive force enhancer, 1-2 parts of pigment, 2-3 parts of thixotropic agent, 1-2 parts of flatting agent, 1-3 parts of age resister, 5-8 parts of PTFE and 2-5 parts of chromic oxide. The invention further provides a preparation method of the polyacrylate UV adhesive. The polyacrylate UV adhesive has good wear resistance.

Description

Technical field: [0001] The invention relates to a UV glue, in particular to a polyacrylate UV glue and a preparation method thereof. Background technique: [0002] UV glue, also known as shadowless glue, photosensitive glue, and ultraviolet light curing glue, is a type of adhesive that must be cured by ultraviolet light. It can be used as an adhesive or as a glue for paints, coatings, inks, etc. Material use. UV is the abbreviation of UltravioletRays in English, that is, ultraviolet light. Ultraviolet rays are invisible to the naked eye and are a section of electromagnetic radiation other than visible light. The wavelength range is generally 110-400nm. The principle of UV glue curing is that the photoinitiator (or photosensitizer) in the UV curing material absorbs ultraviolet light under the irradiation of ultraviolet light to generate active free radicals or cations, triggering monomer polymerization and crosslinking chemical reactions, so that the adhesive Converts from...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J133/08C09J127/18C09J11/04C09J11/06C09C1/34C09C3/08
Inventor 李晓明
Owner SUZHOU GAIDE FINE MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com