Preparation method for architectural decoration flambe art ceramic tile

A technology for architectural decoration and artistic ceramics, applied in the field of ceramics, can solve the problems of unfavorable development and high energy consumption, and achieve the effects of reducing firing costs, obvious economic benefits, and shortening firing time

Inactive Publication Date: 2016-02-10
SICHUAN BAITA XINLIANXING CERAMIC GROUP
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using the traditional crystallization kiln-changing glaze process, the energy consumption is high, and it is not conducive to the development of architectural decorative kiln-changing art ceramic tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for architectural decoration flambe art ceramic tile
  • Preparation method for architectural decoration flambe art ceramic tile
  • Preparation method for architectural decoration flambe art ceramic tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] A method for preparing architectural decorative kiln art ceramics, comprising the following steps:

[0062] A. Ingredients: Weigh the green body raw materials according to weight percentage, and the green body raw materials are composed of the following weight percentage components:

[0063] Kaolin 10%

[0064] Weathered sand 7%

[0065] Potassium feldspar 28%

[0066] Low fire clay 32%

[0067] Refined white sand 12%

[0068] Waste base powder 4%

[0069] Black talc 7%.

[0070] B. Pulping: Weigh the raw materials according to the ratio in A, and put them into the ball mill to grind the mixed raw materials according to the ratio of material: ball: water = 1:2:0.35; after ball milling, the 250-mesh sieve sieve balance is 1.2~ 1.7% slurry.

[0071] C. Powder making: the slurry obtained in step B is made into powder through a spray dryer, and then aged for 2 to 3 days.

[0072] D. Press molding: press the aged powder obtained in step C into brick adobe.

[0073] ...

Embodiment 2

[0100] The blank is composed of the following components by weight: 15% kaolin, 12% weathered sand, 35% potassium feldspar, 22% low-fired clay, and 7% refined white sand. Waste base powder 7%, black talc 2%;

[0101] The bottom glaze is composed of the following components by weight: 19% potassium feldspar, 10% porcelain sand, 10% kaolin, 5% zinc oxide, 10% calcined talc, 15% barium carbonate, 8% dolomite, and 11% calcium carbonate , calcium phosphate 10%, alumina 2%

[0102] The surface glaze is composed of the following components by weight: potassium feldspar 23%, porcelain sand 5%, kaolin 10%, zinc oxide 17%, calcined talc 10%, zirconium silicate 10%, titanium oxide 18%, glass powder 5% %, cobalt oxide 2%.

[0103] Other steps are the same as in Embodiment 1.

Embodiment 3

[0105] The blank is composed of the following components by weight: 12% kaolin, 10% weathered sand, 30% potassium feldspar, 28% low-fired clay, and 9% refined white sand. Waste base powder 6%, black talc 5%;

[0106] The bottom glaze is composed of the following raw materials in weight percentage: albite 16%, porcelain sand 15%, kaolin 7.5%, zinc oxide 6.5%, calcined talc 7.5%, barium carbonate 16%, dolomite 7%, calcium carbonate 16%, Calcium phosphate 5%, alumina 3.5%;

[0107] The surface glaze is composed of the following raw materials in weight percentage: 22% albite feldspar, 8% porcelain sand, 8% kaolin; 22% zinc oxide; 5% calcined talc; 15% titanium oxide, 12% zirconium silicate, and 8% glass powder , coloring agent 1.2%.

[0108] Other steps are the same as in Embodiment 1.

[0109] The crystal flower detection of kiln-changing art ceramic tiles is shown in the attached figure.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for an architectural decoration flambe art ceramic tile. Ground coat is prepared from, by weight, 14%-19% of potassium feldspar+albite, 10%-15% of porcelain sand, 5%-10% of kaolin, 5%-12% of zinc oxide, 5%-10% of calcined talc, 15%-20% of barium carbonate, 3%-8% of dolomite, 11%-16% of calcium carbonate, 3%-10% of calcium phosphate and 2%-7% of aluminum oxide. Cover glaze is prepared from, by weight, 16%-23% of feldspar+albite, 5%-10% of porcelain sand, 5%-10% of kaolin, 17%-23% of zinc oxide, 5%-10% of calcined talc, 10%-16% of zirconium silicate, 14%-18% of titanium oxide, 5%-10% of glass dust and 1%-2% of colorant. The architectural decoration flambe art ceramic tile is formed through the steps of burdening, pulping, powder making, press forming, drying, ground coat sprinkling, cover glaze sprinkling, firing, fine trimming packaging and the like. The apparent size of snowflake-shaped crystal patterns ranges from 3 mm to 6 mm, and the maximum apparent size of cotton-shaped crystal patterns can reach about 20 mm. Low-temperature rapid sintering of flambe art ceramic is achieved, firing cost is reduced, and energy saving, consumption reduction and emission reduction are achieved.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a method for preparing kiln-transformed art ceramic bricks for architectural devices. Background technique [0002] Kiln-changing glaze is an art of water, earth and fire. As a treasure in ancient Chinese ceramic art, it is deeply loved by people, and crystal kiln-changing glaze products are the best in kiln-changing. However, traditional crystalline kiln-changing glaze products are high-temperature and slow-fired products, and their production costs are very high. It is very difficult to survive, and it is difficult to realize industrialized mass production. Therefore, although crystallized kiln-changed glaze has preliminary development in modern handicrafts and daily-use porcelain, the development of kiln-changed glaze in the direction of architectural ceramic wall and floor tiles is almost blank. The firing time of traditional crystal kiln-changing glaze art products is at l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/86C04B35/622
Inventor 廖咏康
Owner SICHUAN BAITA XINLIANXING CERAMIC GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com