Wear-resistant and mildewproof non-stick pan coating

A non-stick pan and coating technology, applied in coatings, anti-corrosion coatings, anti-fouling/underwater coatings, etc., can solve problems such as poor strength of PTFE coatings, reduced non-stick performance, and easy peeling off, etc., to achieve Improves steam penetration resistance, inhibits high temperature degradation, and stabilizes chemical properties

Active Publication Date: 2015-12-02
NINGBO GRAMMY KITCHENWARE
View PDF4 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the current mainstream non-stick pans in the market rely on spraying a layer of polyfluororesin non-stick coating on the surface, relying on its strong hydrophobicity and low friction coefficient to achieve non-stick food. It can indeed satisfy people's cooking needs. There is no requirement for food to stick to the pan during the process, but it also has many defects
First of all, the strength of the PTFE coating is poor, it is easy to fall off and damage, and it will soften during cooking, so you can only use a wooden spatula, and you can't cook hard food; at the same time, this kind of non-stick pan is not suitable for cooking Acidic food, otherwise it will affect the service life of the non-stick pan; in addition, the service temperature of the PTFE coating generally cannot exceed 250°C, it is difficult for people to strictly control it when using it, and it is easy to be damaged by dry burning
There has always been controversy over whether PTFE-coated non-stick pans are harmful to human health during use, and disputes continue to arise; and once the non-stick coating falls off, the non-stick performance will be greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant and mildewproof non-stick pan coating
  • Wear-resistant and mildewproof non-stick pan coating
  • Wear-resistant and mildewproof non-stick pan coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A wear-resistant, anti-mildew and non-stick pan coating comprises a primer and a surface layer; the primer is composed of the following raw materials in parts by weight:

[0024]

[0025] Described surface coating is made up of the raw material of following parts by weight:

[0026]

[0027]

[0028] Wherein, the modified polyvinylidene fluoride resin is composed of acrylic acid-based resin, polyvinylidene fluoride resin, methyl methacrylate, and acrylic acid. The high temperature resistant pigment is enamel black. The acrylic-containing resin is composed of methyl methacrylate, methacrylic acid, acrylic acid, ethylhexyl acrylate and methacrylamide.

Embodiment 2

[0030] A wear-resistant, anti-mildew and non-stick pan coating comprises a primer and a surface layer; the primer is composed of the following raw materials in parts by weight:

[0031]

[0032] Described surface coating is made up of the raw material of following parts by weight:

[0033]

[0034]

[0035] Wherein, the modified polyvinylidene fluoride resin is composed of acrylic acid-based resin, polyvinylidene fluoride resin, methyl methacrylate, and acrylic acid. The high temperature resistant pigment is enamel black. The acrylic-containing resin is composed of methyl methacrylate, methacrylic acid, acrylic acid, ethylhexyl acrylate and methacrylamide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a wear-resistant and mildewproof non-stick pan coating. The coating comprises a bottom layer and a surface layer; The bottom layer consists of the following materials in parts by weight: polyimide resin, modified polyvinylidene fluoride resin, a high-temperature-resistant pigment filler, modified polyorganosiloxane polymer, polyetheretherketone PEEK and graphite. The surface layer consists of the following materials in parts by weight: polytetrafluoroethylene resin, phenylene sulfide, acrylate rubber latex, epoxy accelerated resin, a catalyst, fumed silica, nano silver and the like. The wear-resistant and mildewproof non-stick pan coating prepared in the invention is chemically stable at the cooking temperature and does not generate hazardous substance PFOA. The coating has relatively great hardness and the damages of spatulas or spoons to the surface coating of the non-stick pan can be avoided. The non-stick pan prepared from the coating has low cost and a long service life.

Description

technical field [0001] The invention relates to cooking utensils, in particular to a wear-resistant, mildew-proof and non-stick pan coating. Background technique [0002] People have been using traditional metal pans (cast iron, stainless steel, aluminum and aluminum alloys) to cook food for a long time, but the phenomenon of food sticking to the pan often occurs during the cooking process. This not only destroys the appearance of the food, but also the food that sticks to the pan is prone to scorching, and even produces harmful substances, which will affect human health. In addition, it also increases the difficulty of cleaning the cooking utensils, which brings inconvenience to cooking. Therefore, since the invention of the non-stick pan, it has been prepared because it is easy to clean, can easily fry and fry food without sticking to the pan, can minimize oil fume, and meets the needs of modern people's pursuit of green food, low fat, and low calories. Loved by the publ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D179/08C09D183/04C09D161/16C09D127/18C09D181/02C09D133/12C09D151/00C09D7/12C09D5/08C09D5/14A47J36/04
Inventor 肖彬彭彩佑王高林
Owner NINGBO GRAMMY KITCHENWARE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products