Vinylon/polyester oil harness string production process and product thereof

A production process and silk thread technology, which is applied in the production process and product field of polyester oil through thread, can solve the problems of fabric warp defects, breakage of the thread, large stretching of the thread, etc., and achieve enhanced breaking strength and friction coefficient. The effect of improving and reducing the expansion rate

Inactive Publication Date: 2015-11-18
安徽创星实业有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The product is in the weaving factory, due to the large amount of expansion and contraction of the harness, it affects the normal production
Especially in the season when the air humidity is high, the expansion and contraction of the harness becomes larger, seriously reducing the weaving efficiency of the loom, and it is easier to cause warp defects of the fabric, and even the breakage of the harness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A production process of polyester oil through thread, comprising the following steps:

[0025] 1) For the yarn, two 333dtex-420dtex polyester filaments and two 29.5tex vinylon stretch-cut yarns are combined into one strand;

[0026] 2) Pre-twist, twist direction Z, number of strands twist is twist / 100㎝, twist with 1 strand that has been merged, and the twist is 360;

[0027] 3) Double twisting, twisting direction S, number of strands and twisting twist / 100㎝, synthesize 3 strands with the first twisting, and then twisting, the twisting degree is 180-270;

[0028] 4) The strands with a good twist of 180-270 are wound into stranded wires by a yarn reeling machine;

[0029] 5) Sizing and dyeing in the slurry pool, the concentration of the slurry is 20%, and the dyestuff is 0.0010-0.0020% of the total slurry, and they are put together to adjust the slurry;

[0030] 6) Put the stranded wire into the adjusted slurry, soaking time is 60 minutes;

[0031] 7) Sizing the polyes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a vinylon / polyester oil harness string production process and a product thereof. The production process comprises the following steps: 1) plying; 2) first twisting; 3) second twisting; 4) winding the plied yarn, which is formed after second twisting and the twisting degree of which is 180-270, by a yarn reeler to form a stranded yarn; 5) carrying out size mixing in a pulp chest; 6) putting the stranded yarn into the mixed size; 7) removing 60-70% of the size in the vinylon / polyester stranded yarn, which is sized, by a dehydrator; 8) carrying out drafting and setting for 15-25 minutes by a yarn waxing machine on the sized stranded yarn; 9) carrying out drying on the stranded yarn obtained through first drafting and setting, the humidity being lower than 3%, and the wax temperature being 90-130 DEG C; and 10) putting the dried stranded yarn into a wax bucket and lifting the stranded yarn after being soaked for 5-10 minutes, and then, carrying out second drafting and setting by the yarn waxing machine. The breaking strength of the vinylon / polyester oil harness string provided in the invention is obviously improved; the ratio of expansion and contraction thereof is reduced; and the friction coefficient is improved by 30%-60%.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a production process and a product of a polyester oil through silk thread. Background technique [0002] At present, the weaving width of the jacquard loom is increasing, which puts forward higher requirements for the harness. Therefore, the development of a harness with high strength and low stretching rate is already the best way to ensure that the shed of the jacquard loom is clear and weaves smoothly. An urgent need. At the same time, the high-strength, low-stretch harness can effectively reduce the warp defects of the fabric. [0003] At present, the polyester thread made by common methods has low tensile breaking strength. The expansion and contraction of the harness is relatively large under a small load. When the product is in the weaving factory, due to the large amount of expansion and contraction of the harness, the normal production is affected. Espec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/04D02G3/26D06B21/00D06P3/82D06P1/52D06M13/02D06M13/188D06M101/32D06M101/24
Inventor 刘克祥
Owner 安徽创星实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products