A chromium-free passivating agent after metal plating with hydrophobic surface performance

A chromium-free passivation and metal plating technology, applied in the direction of metal material coating process, can solve the problems of use limitation, chromium ion environment and human harm, and achieve the effect of preventing corrosion, low cost and improving corrosion resistance

Active Publication Date: 2017-12-15
WUXI EPIC TECH
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because chromium ions are extremely harmful to the environment and the human body, their use is restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A chromium-free passivating agent after metal plating with hydrophobic surface performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Use deionized water to prepare a passivator with a sodium silicate concentration of 0.5g / L, a methyltrimethoxysilane coupling agent concentration of 0.1-0.5g / L, and a nano-titanium dioxide concentration of 0.2g / L, and adjust the pH to 12 , to obtain passivator 1.

Embodiment 2

[0025] Use deionized water to prepare sodium silicate with a concentration of 5g / L, the concentration of methyltrimethoxysilane coupling agent and alcohol amine titanate coupling agent with a concentration of 0.8-1.2g / L, and the concentration of silicone defoamer with a concentration of 2g / L. L, the passivating agent whose concentration of nano-titanium dioxide and nano-silicon dioxide is 0.01g / L, the pH is adjusted to be 10, and the passivating agent 2 is obtained.

Embodiment 3

[0027] Use deionized water to prepare lithium silicate with a concentration of 15g / L, γ-aminopropyltriethoxysilane coupling agent and alcoholamine titanate coupling agent with a concentration of 2-5g / L, and a nano-silica concentration of 0.5g / L, organic silicon defoamer and C7-9 alcohol polyoxyethylene ether penetrating agent concentration of 3g / L passivating agent, adjust pH to 10, to obtain passivating agent 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

A chromium-free passivator with a hydrophobic surface property for plated metal, comprising: 0.5-30 g / L of silicate, 0.01-1 g / L of a nanometer material, and 0.1-10 g / L of one or more of a silane coupling agent, a titanate coupling agent, and a water-based wax emulsion. Also disclosed is a method for passivating plated metal by using a passivator.

Description

technical field [0001] The invention relates to a protective agent after plating on metal surfaces and a using method thereof, in particular to a chromium-free passivating agent after metal plating with hydrophobic surface performance. Background technique [0002] After metal plating, it is usually passivated to improve its corrosion resistance. The traditional passivation treatment method usually uses the oxidation of hexavalent or trivalent chromium ions to form a dense oxide film on the surface of the coating, that is, the passivation film, which can prevent the metal from contacting with corrosive media such as water and oxygen in the air. So as to achieve the role of anti-corrosion. Because chromium ions are extremely harmful to the environment and the human body, their use is limited. In January 2003, with the passage of the ROHS Directive, which prohibits the use of chromate-passivated galvanized steel sheets in electronic and electrical products exported to the EU...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/60
CPCC23C22/60
Inventor 尤为
Owner WUXI EPIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com