A kind of pasty water-based release agent and its preparation method and application method

A release agent, water-based technology, applied in coatings and other directions, can solve problems such as the decline of rubber properties, and achieve the effects of good lubricity, high colloid content, and good thixotropic effect.

Active Publication Date: 2018-04-27
江苏益路昇新材料有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims at the problems that the powdery solid, liquid and suspension rubber release agents cannot completely solve the problem of adhesion of the laminated sheets after the rubber material is kneaded or banburyed, and that the performance of the rubber in the subsequent processing is reduced due to the addition of the release agent, etc., and provides a A paste-like water-based rubber release agent and its preparation method and application method, mainly using inorganic powder, adding surfactants, thixotropic agents, defoamers, water, etc., to make an environmentally friendly release agent with good stability, dispersibility and isolation effect Type water-based rubber release agent, applied to the isolation of rubber sheets for mastication or kneading

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pasty water-based release agent and its preparation method and application method
  • A kind of pasty water-based release agent and its preparation method and application method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) The mass-number ratio of each component prepared by paste-like water-based rubber release agent is: 0.1 part of sodium oleate (industrial grade, commercially available, the same below), 0.5 part of OP-4, 1.0 part of OP-7, 1.0 part of OP-7, -10 4.0 parts (OP-4, OP-7, OP-10 are all provided by Jiangsu Haian Petrochemical Plant, the same below), diatomite (325 mesh, provided by Lingshou County Longtong Building Materials Factory, the same below) 2.0 parts , active ZnO (provided by HX-5 Copper Anode Chemical Factory, the same below) 0.5 parts, TiO 2 (rutile type, 325 mesh, commercially available, the same below) 0.5 part, bisphenol A polyoxyethylene ether (BPE-20, provided by Jiangsu Haian Petrochemical Factory, the same below) 1 part, sodium bentonite (natural grade, 325 10 parts of the mixture (the mass ratio of bentonite to silica is 10:1, the same below) and polyether Modified silicone oil (ZBH-207, provided by Qingdao Zhongbao Chemical Co., Ltd., the same below) 0...

Embodiment 2

[0038] (1) The mass-number ratio of each component prepared by the pasty water-based rubber release agent is: 0.5 part of sodium oleate, 0.5 part of sodium linoleate (industrial grade, commercially available, the same below), 0.5 part of OP-10, Ultrafine CaCO 3 Powder (CL-8030, 3000 mesh, provided by Hunan Chenglu Jufeng New Material Co., Ltd., the same below) 9 parts, diatomaceous earth 2.0 parts, active ZnO 0.5 part, TiO 2 0.5 parts, 2 parts of bisphenol A polyoxyethylene ether, 5 parts of a mixture of sodium bentonite and fumed silica, 0.5 parts of polyether modified silicone oil, and 90 parts of deionized water.

[0039] (2) Preparation method of water-based paste rubber release agent: Mix deionized water at 20-50°C with surfactants such as sodium oleate, sodium linoleate, and OP-10, stir and dissolve; add ultra-fine CaCO 3 , diatomaceous earth, active ZnO, TiO 2 Wait for inorganic powder, and add polyether modified silicone oil defoamer dropwise; speed up the stirring s...

Embodiment 3

[0044] (1) The mass-number ratio of each component prepared by paste water-based rubber release agent is: 0.5 part of sodium linoleate, 1.0 part of OP-4, 1.0 part of OP-7, 1.0 part of OP-10, superfine CaCO 3 6.0 parts of powder, 5.0 parts of diatomaceous earth, 0.5 parts of active ZnO, TiO 2 0.5 parts, 0.8 parts of bisphenol A polyoxyethylene ether, 8 parts of a mixture of sodium bentonite and fumed silica, 0.2 parts of polyether modified silicone oil, and 100 parts of deionized water.

[0045] (2) Preparation method of water-based paste rubber release agent: mix deionized water at 20-50°C with sodium linoleate, OP-4, OP-7, OP-10 and other surfactants, stir and dissolve; add super Fine CaCO 3 , diatomaceous earth, active ZnO, TiO 2 Wait for inorganic powder, and add polyether modified silicone oil dropwise; increase the stirring speed, add the mixture of sodium bentonite and fumed white carbon black in batches, then add bisphenol A polyoxyethylene ether, fully stir and grind...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
porosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a paste-like water-based rubber release agent and its preparation method and application method. Its components include 3-15 parts of inorganic powder additives, 0.1-1.0 parts of anionic surfactant, and 0.5-1.0 parts of anionic surfactant in parts by mass. 5.5 parts of nonionic surfactant, 5-10 parts of thixotropic agent, 0.2-2.0 parts of thickener, 0.1-0.5 parts of defoamer, 60-100 parts of deionized water. Mix water and surfactant, stir to dissolve, add inorganic powder additives, add defoamer dropwise, add thixotropic agent and thickener in batches, stir well and grind until homogeneous to obtain the release agent. When in use, make an aqueous solution at a mass ratio of 1:3 to 15, add it to the water cooling tank of the film, the film is cooled by water while the release agent is applied, and it can be stacked after air drying on the hanging rod. The invention is easily soluble in water, non-toxic, tasteless, simple in process and low in cost, and basically has no influence on the subsequent processing performance of rubber.

Description

technical field [0001] The invention relates to a paste-like water-based rubber release agent, in particular to one used to prevent natural rubber, synthetic rubber and their blended rubbers from sticking during storage and transportation after mastication, mixing or final kneading. The preparation method and application method of the pasty water-based rubber release agent. Background technique [0002] In the production and processing process of rubber products, the rubber material is stacked and parked after kneading or banburying. Due to the high self-adhesiveness of the film, and under the action of layer-by-layer pressure, the film is prone to layer-by-layer adhesion, which seriously affects subsequent processing and use. Therefore, before the rubber is transported and stacked for storage, polyethylene plastic film or a layer of release agent is used on the film to achieve isolation and prevent the films from sticking to each other. Due to the mixing of polyethylene f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/04C08L21/00
Inventor 陈正年张克杰张声春陈鹏徐建华徐颖弘詹纯金
Owner 江苏益路昇新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap