Blended regenerating cotton yarns capable of improving ultraviolet ray resistance, and preparation method thereof

A kind of recycled cotton yarn, anti-ultraviolet technology, used in melt spinning, rayon manufacturing, textiles and papermaking, etc., can solve the problems of low moisture regain, poor aging resistance, etc., achieve good elasticity, improve product quality, and enhance the effect of strength

Inactive Publication Date: 2015-10-07
SHUNTIAN SPINNING LIMITED
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polypropylene fiber is light in weight, high in strength, good in elasticity, wear-resistant and corrosion-resistant, has electrical insulation and warmth retention properties, low moisture regain, low price, and good chemical resistance. It is widely used in the field of decorative fabrics, but due to The poor heat resistance and aging resistance of polypropylene fiber limit its application in the field of clothing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] specific implementation plan

[0015] The present invention will be described in detail below through specific examples.

[0016] A blended regenerated cotton yarn capable of improving UV resistance, prepared from the following raw materials in parts by weight (kg): waste cotton fabric 40, cotton yarn scraps 15, phosphate starch 2, pectin 1.5, pure acrylic emulsion 6, lauryl alcohol Sodium polyoxyethylene ether sulfate 0.5, polypropylene 39, nano-zinc oxide 3, liquid paraffin 12, nano-titanium dioxide 9, carboxymethyl cellulose 1.5, glyceryl stearate 1, appropriate amount of water;

[0017] A kind of blended regenerated cotton yarn that can improve the anti-ultraviolet performance of the present invention is made by the following specific steps:

[0018] (1) Add phosphate starch to 30 times the amount of water, then heat and swell to form a viscous slurry, then add pectin, continue stirring, and then add half the amount of nano-titanium dioxide, pure acrylic emulsion, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses blended regenerating cotton yarns capable of improving ultraviolet ray resistance, wherein the blended regenerating cotton yarns are characterized in that the blended regenerating cotton yarns are prepared from the following raw materials by weight: 40-43 parts of waste cotton fabric, 15-17 parts of cotton yarn leftover, 2-2.5 parts of phosphoric ester starch, 1.5-2 parts of pectin, 6-8 parts of pure acrylic emulsion, 0.5-0.7 part of dodecanol polyoxyethylene ether sodium sulfate, 39-44 parts of polypropylene, 3-5 parts of nanometer zinc oxide, 12-14 parts of liquid paraffin, 9-10 parts of nanometer titanium dioxide, 1.5-2 parts of carboxymethyl cellulose, 1-2 parts of glyceryl stearate, and a proper amount of water. According to the present invention, the waste cotton fabric is used to regenerate the fibers, and the obtained fibers and the surface modified polypropylene short fibers are subjected to drawing and blending to obtain the blended regenerating cotton yarns of the present invention, such that the characteristics of various fibers are neutralized, the disadvantage of poor sunscreen property of the cotton fibers and the polypropylene fibers are overcome, characteristics of strength enhancing, good elasticity, wear resistance, corrosion resistance, good warm keeping and product quality improving are provided, and the waste cotton regeneration is adopted so as to save the cost.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a blended regenerated cotton yarn capable of improving anti-ultraviolet performance and a preparation method thereof. Background technique [0002] With the rapid increase of the global population, all countries in the world will control the use of cultivated land, and the planting of cotton, hemp, and mulberry trees for sericulture will be restricted, and the traditional cotton textile raw materials will be subject to multiple constraints. Relevant data show that in 2010, the amount of leftover materials and other raw materials used in domestic recycled cotton yarns can reach about 3 million tons in total. It is estimated that 50% of the cotton is recycled yarn, and the cotton output per mu is 200 kg, which is equivalent to the output of more than 7 million mu of cotton fields. Regenerated yarn not only realizes the recycling of resources, saves limited resources, but also sol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/46D01F2/00D01F1/10D01D5/08D06M15/09D06M101/20
Inventor 刘勇
Owner SHUNTIAN SPINNING LIMITED
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products