Positive electrode material of lithium ion battery and preparation method thereof

A lithium-ion battery, cathode material technology, applied in battery electrodes, secondary batteries, circuits, etc., can solve problems such as safety hazards, cycle life, etc., and achieve the effects of inhibiting battery flatulence, improving electronic conductivity, and stabilizing lattice structure

Active Publication Date: 2015-09-30
QINGHAI CONTEMPORARY AMPEREX TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In view of this, it is necessary to provide a modification method, which combines the advantages of doping and coating, and at the same time constructs a special multi-layer coating structure, which can improve the LiMn x Fe 1-x PO 4 The electrochemical performance of the material can solve the safety hazards and cycle life problems caused by the dissolution of manganese and iron elements in the material, and this modification method can significantly reduce the production cost of the material. The prepared LiMn x Fe 1-x PO 4 The material has excellent low-temperature electrochemical performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Positive electrode material of lithium ion battery and preparation method thereof
  • Positive electrode material of lithium ion battery and preparation method thereof
  • Positive electrode material of lithium ion battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] In the first step, Lithium hydroxide, manganese sulfate, ferrous sulfate, phosphoric acid, cetyltrimethyl Ammonium bromide, use deionized water to dissolve lithium hydroxide and prepare a 2.5mol / L aqueous solution, add manganese sulfate, ferrous sulfate, and phosphoric acid to the reactor with a reflux device, then add deionized water to the reactor and stir Dissolve to form solution I, keep the total concentration of Mn and Fe in solution I at 1.8mol / L, add ethylene glycol into the reactor according to the total volume of deionized water in solution I: the total volume of ethylene glycol is 1:1, Then add cetyltrimethylammonium bromide, slowly add lithium hydroxide solution in the reactor under continuous stirring, then add 2.5mol / L NaOH solution in the mixture until the pH value of the mixed solution is adjusted to 8.0, Formation of mixture II;

[0028] In the second step, place the reactor in an oil bath at a temperature of 160°C and turn on the condensing reflux dev...

Embodiment 2～23

[0031] The chemical formula of the obtained target product, the type of raw material, the pH value of the liquid phase system, the calcination temperature and time and other process parameters are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a positive electrode material of a lithium ion battery. The chemical formula of the positive electrode material is Li(1-a)NaaMnxFe(1-x)PO4(MeFy)b(C)c, wherein a is more than 0 and smaller than or equal to 0.08, b is more than 0 and smaller than 0.15, c is more than 0 and smaller than 1.5, b+c is smaller than 1.5, x is more than or equal to 0.1 and smaller than or equal to 0.9, MeFy is at least one of AlF3, TiF4, MgF2, ZrF4, MoF6 and NbF4; the positive electrode material is of a core-shell structure, and sequentially comprises a Na<+> bulk phase doped Li(1-a)NaaMnxFe(1-x)PO4 inner core layer, a middle transitional layer containing metal fluoride MeFy, and a carbon coverage layer positioned on the surface. The invention also provides a preparation method of the positive electrode material. According to the positive electrode material, the electric conductivity is improved, the bloating of the positive electrode material is effectively inhibited, the cycle life of the battery is prolonged, and the high-temperature storage property of the battery is improved.

Description

technical field [0001] The invention belongs to the technical field of lithium ion batteries, and in particular relates to a lithium ion battery cathode material modified lithium manganese iron phosphate and a preparation method thereof. Background technique [0002] Lithium iron manganese phosphate (LiMn x Fe 1-x PO 4 ), as a cathode material for lithium-ion batteries, has a wide range of applications in the electric vehicle (EV) and energy storage system (ESS) markets. LiMn x Fe 1-x PO 4 It can provide higher working potential and higher discharge capacity, and has the advantages of low price, environmental friendliness, abundant raw materials, good thermal stability, and high safety, and has been recognized by the market. But LiMn x Fe 1-x PO 4 The extremely low intrinsic electronic conductivity and lithium ion diffusion rate affect its electrochemical performance, which hinders its commercial application. Therefore, increasing the LiMn x Fe 1-x PO 4 The elec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/58H01M4/62
CPCH01M4/5825H01M4/62H01M4/624H01M4/625H01M4/628H01M10/0525Y02E60/10
Inventor 吴关
Owner QINGHAI CONTEMPORARY AMPEREX TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com