A kind of nb-si system material microstructure corrosion agent and electrolytic corrosion method

A technology of microstructure and corrosive agent, applied in the field of metallographic analysis in physical metallurgy, can solve the problems of wasting manpower and material resources, unable to distinguish alloys, corrosion well, etc., and achieve the effect of improving convenience

Active Publication Date: 2017-11-21
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the Nb-Si series material is a new type of structural material, and its composition phase is completely different from the existing mature system materials, such as steel, aluminum alloy, titanium alloy, superalloy, etc., using the existing corrosive agent, for Nb -The composition phase of Si-based materials can produce corrosion, resulting in more false images. The composition phase of the alloy cannot be well resolved by optical microscope observation. It is necessary to use the backscattered electron imaging function of the scanning electron microscope for observation. In large-size samples There are certain limitations in multi-regional observation, and a lot of manpower and material resources are wasted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nb-si system material microstructure corrosion agent and electrolytic corrosion method
  • A kind of nb-si system material microstructure corrosion agent and electrolytic corrosion method
  • A kind of nb-si system material microstructure corrosion agent and electrolytic corrosion method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Prepare the Nb-Si series material microstructure sample according to the following steps:

[0023] 1) Corrosive agent configuration: measure 1ml H with graduated cylinder 3 PO4 and 99ml H 2 O, first the measured H 2 O was placed in a glass beaker, and then the measured H 3 Pour PO4 into the beaker and stir with a glass rod for about 30s;

[0024] 2) Polish the Nb-22Ti-16Si-3Cr-3Al-2Hf material sample prepared by vacuum non-consumable arc melting, and connect it to a DC power supply XD173A-120 with a rated working voltage of 120V and a rated working current of 3A through a wire The anode of the stainless steel plate is connected to the cathode of the power supply through a wire, and the polished surface of the Nb-22Ti-16Si-3Cr-3Al-2Hf sample is kept opposite to the stainless steel plate, but cannot be contacted;

[0025] 3) Turn on the switch of the DC power supply, quickly adjust the voltage to 80V, observe the change of the current, and turn off the DC power switch...

Embodiment 2

[0029] Prepare the Nb-Si series material microstructure sample according to the following steps:

[0030] 1) Corrosive agent configuration: measure 1ml H with graduated cylinder 3 PO4 and 99ml H 2 O, first the measured H 2 O was placed in a glass beaker, and then the measured H 3 Pour PO4 into the beaker and stir with a glass rod for about 30s;

[0031] 2) Polish the crystallization front sample of Nb-20Ti-16Si-3Cr-3Al-2Hf material directional solidified in an electromagnetic cold crucible, and connect it to the DC power supply XD173A-120 with a rated working voltage of 120V and a rated working current of 3A through a wire Anode, the stainless steel plate is connected to the cathode of the power supply through a wire, and the polished surface of the Nb-22Ti-16Si-3Cr-3Al-2Hf sample is kept opposite to the stainless steel plate, but cannot be contacted;

[0032] 3) Turn on the switch of the DC power supply, quickly adjust the voltage to 70V, observe the change of the current...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to an etchant and an electrolytic corrosion method for preparing Nb-Si series material microstructure samples, and belongs to the field of metallographic analysis in physical metallurgy. The present invention uses a solution with a volume content of 98% H3PO4:H2O=1:99 as the etchant, uses the polished Nb-Si material as the anode, and stainless steel as the cathode, and conducts electrolytic corrosion through a DC power supply to prepare the Nb-Si system. The material microstructure observes the sample, so that the composition phase and microstructure morphology of the Nb-Si series material can be analyzed conveniently and quickly through an optical microscope.

Description

technical field [0001] The invention belongs to the field of metallographic analysis in physical metallurgy, and relates to an etchant and an electrolytic corrosion method for preparing Nb-Si series material microstructure samples. Background technique [0002] The increase of the thrust-to-weight ratio of gas turbine engines strongly depends on the increase of the inlet temperature before the high-pressure turbine. The temperature at the front inlet of the new-generation engine with a thrust-to-weight ratio of 15-20 is as high as 2100-2200K. Considering the cooling effect of the air-cooling structure of the blade itself and the heat insulation effect of the thermal barrier coating, the temperature bearing between the guide of the high-pressure turbine and the working blade itself The capacity must reach above 1150°C, which greatly exceeds the limit temperature bearing capacity of current nickel-based high-temperature metal materials (working temperature does not exceed 1120...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25F3/08G01N1/32
Inventor 康永旺李明郭丰伟
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap