Positive photoresist-based nickel positive mold production method

A technology of positive photoresist and photoresist, which is applied in the direction of microlithography exposure equipment, photosensitive material processing, photolithography process exposure device, etc., which can solve the problem of edge warping, difficult deglue process, and low photolithography preparation efficiency And other issues

Active Publication Date: 2015-05-06
北京同方光盘股份有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The embodiment of the present invention provides a method for making a positive photoresist-based nickel positive mold, which solves the problems of low photolithography preparation efficiency, difficult desmearing process, and edge warping

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Positive photoresist-based nickel positive mold production method
  • Positive photoresist-based nickel positive mold production method
  • Positive photoresist-based nickel positive mold production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In order to make the object, technical solution and advantages of the present invention clearer, the specific embodiments of the present invention will be further described in detail below in conjunction with the accompanying drawings.

[0026] Below to figure 1 As an example to describe in detail the positive photoresist-based nickel positive mold manufacturing method provided by the embodiment of the present invention, figure 1 The flow chart of the positive photoresist-based nickel positive mold manufacturing method provided by the embodiment of the present invention; figure 2 The schematic flow chart of the positive photoresist-based nickel positive mold manufacturing method provided by the embodiment of the present invention; image 3 A schematic diagram of the production scene of a positive photoresist-based nickel positive mold provided by the embodiment of the present invention. Such as figure 1 , 2 As shown in and 3, the method includes the following steps...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Draft angleaaaaaaaaaa
Login to View More

Abstract

The embodiment of the invention relates to a positive photoresist-based nickel positive mold production method. The method comprises the following steps: evenly spin-coating the front side of a substrate with a positive photoresist; exposing the positive photoresist of the substrate by utilizing a negative mask plate of a target pattern, and developing to obtain the patterned photoresist; splash-plating chromium on the substrate with the patterned photoresist, to form a uniform chromium layer pattern; performing tackifier hexamethyldisilazane evaporation on the chromium layer pattern so as to enhance the adhesiveness of the chromium layer pattern and the photoresist, and evenly spin-coating the chromium layer pattern with the positive photoresist; exposing the photoresist on the chromium layer pattern on the substrate by utilizing the chromium layer pattern, and developing to obtain the photoresist of the chromium layer pattern; performing surface metallization on the photoresist of the chromium layer pattern; and performing metal nickel positive mold electroforming on the photoresist of the metalized the chromium layer pattern, to obtain the nickel positive mold. For the nickel positive mold, the production technology is simple and convenient, the photoresist removal is convenient, and the upwarping edges of the nickel positive mold can be avoided.

Description

technical field [0001] The invention relates to the field of microfluidic chip preparation, in particular to a method for manufacturing a positive photoresist-based nickel positive mold. Background technique [0002] Lithography technology is widely used in the field of microfluidic chip preparation. The quality of lithography directly affects the quality of the metal positive mold and its microfluidic chip. Optimizing and adjusting the lithography process and methods is crucial to improving product quality. role. Therefore, optimizing and adjusting the photolithography process is particularly important for the precise and rapid preparation of microfluidic chips. Due to the existence of light diffraction and other phenomena in thick photoresist lithography technology, the angle α between the photoresist pattern and the substrate is not equal to 90°. If the angle α between the photoresist pattern and the substrate is not greater than 90°, the photoresist The side wall of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G03F7/20G03F7/42
Inventor 郭哲刘祝凯宋娇阳许斌
Owner 北京同方光盘股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com