Modified PVC sheet

A sheet and modification technology, applied in the field of polymer modified materials, can solve the problems of breakage, easy rupture of PVC sheets, and easy aging, and achieve the effects of easy molding process, not easy to break, and not easy to age.

Inactive Publication Date: 2015-04-29
DONGGUAN PENGQI PLASTIC
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the chemical structural characteristics of PVC itself and small molecule processing aids such as plasticizers and lubricants in the products are easy to migrate to the surface, the current plastic-absorbing (plastic-absorbing board is PVC, also known as high molecular polymer) packaging materials are prone to appear. In the case of damage, especially when the temperature is low, the PVC sheet is easy to break and age

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified PVC sheet
  • Modified PVC sheet
  • Modified PVC sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The invention provides a kind of preparation method of PVC modified sheet, comprises the following steps:

[0032] (1), prepare raw material, its composition and parts by weight are:

[0033]

[0034] (2) Add the dried raw materials into the mixer, mix and stir at high speed for 5 to 10 minutes, mixing sequence: powdery PVC plastic, plasticizer, stabilizer, internal and external lubricants, processing aids, Pigments, tougheners, reinforcing agents; high-speed mixing to obtain premixes;

[0035] (3) Cool the premix to 45-55°C;

[0036] (4) Extrusion: Add the premixed material after cooling in step (3) into the extruder through the feeder, extrude through the extruder, and then shape it through a mold;

[0037] Described extruder processing technique is as follows:

[0038] The extruder is provided with five temperature control zones, wherein the temperature of the first temperature control zone is 150-170°C, the temperature of the second temperature control zone is...

Embodiment 2

[0045] (1) Prepare raw materials according to the following formula: 100 parts of PVC powder, 3.5 parts of dioctyl terephthalate (DOTP), 0.6 parts of n-butyl stearate, 0.3 parts of methyl hydrogen sulfate, 3.5 parts of polyethylene, acrylate 1.2 parts of resin (ACR resin), 2.2 parts of methyl tin mercaptide, 0.2 parts of pigment, 5.5 parts of methacrylic acid (MBS resin);

[0046] Drying of raw materials: drying at 115°C for 2.5 hours, then set aside;

[0047] (2) Add the dried raw materials into the mixer, mix and stir at high speed for 8 minutes, mixing order: powdery PVC plastic, dioctyl terephthalate (DOTP), methyl tin mercaptide, polyethylene , methyl hydrogen sulfate, acrylate resin (ACR resin), pigment, polyethylene, methacrylic acid (MBS resin); high-speed mixing to obtain a premix;

[0048] (3), the premix is ​​cooled to 48°C;

[0049] (4) Extrusion: Add the premixed material after cooling in step (3) into the extruder through the feeder, extrude through the extrude...

Embodiment 3

[0056] (1) Prepare raw materials according to the following formula: 107 parts of PVC powder, 4.3 parts of dioctyl terephthalate (DOTP), 0.8 part of n-butyl stearate, 0.5 part of phenyl acetate, 4.5 parts of polyethylene, acrylate resin (ACR resin) 1.9 parts, mercaptan methyl tin 2.8 parts, pigment 0.4 parts, methacrylic acid (MBS resin) 6.5 parts;

[0057] Drying of raw materials: drying at 122°C for 3.5 hours, set aside;

[0058] (2) Add the dried raw materials into the mixer, mix and stir at high speed for 6 minutes, mixing sequence: powdery PVC plastic (polyvinyl chloride resin), plasticizer, stabilizer, internal and external slip agent, Processing aids, pigments, tougheners, reinforcing agents; high-speed mixing to obtain premixes;

[0059] (3), the premix is ​​cooled to 50°C;

[0060] (4) Extrusion: Add the premixed material after cooling in step (3) into the extruder through the feeder, extrude through the extruder, and then shape it through a mold;

[0061] Describe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified PVC sheet. The toughness, strength and tensile property of a PVC sheet are improved, and the weather resistance of the sheet can be greatly improved. The sheet comprises the following raw materials in parts by weight: 110 parts of PVC powder, 5 parts of a plasticizer, 1 part of an internal lubricant, 0.6 part of an external lubricant, 5 parts of a toughening agent, 2 parts of a processing agent, 3 parts of a stabilizer, 0.5 part of a pigment and 7 parts of a reinforcing agent. The product has the advantages of higher physical properties and mechanical properties, lightweight, high easiness in forming, simple process, low cost and the like.

Description

technical field [0001] The present invention relates to a polymer modified material, and more specifically relates to a weather-resistant PVC sheet product. Background technique [0002] Polyvinyl chloride resin (PVC) is one of the earliest general-purpose resins that achieved industrialization and has a large output. It occupies an undoubted important position in material engineering. The global annual output of PVC is second only to polyethylene. Applied in all fields of production and life. PVC has excellent properties such as flame retardancy, corrosion resistance, insulation, and wear resistance. It is an important thermoplastic with low price and wide source of raw materials. [0003] Among them, PVC sheet is an important product in PVC products. It has good mechanical properties and transparency, and is widely used in the fields of medicine, food, and packaging. It not only meets the requirements of product mechanics and flame retardancy, but also increases Improve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08L9/02C08L51/04C08K5/12C08K5/101C08K5/58
CPCC08L27/06C08L2205/035
Inventor 张学军李明何富荣
Owner DONGGUAN PENGQI PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More