Method for making conductive fabric through polyaniline-triggered chemical slivering

A conductive fabric, chemical silver plating technology, applied in the direction of plant fibers, animal fibers, textiles and paper, can solve the problems of environmental pollution, tin poisonous and harmful, high cost, etc., to reduce environmental pollution, good electrical conductivity, strong bonding high degree of effect

Inactive Publication Date: 2015-03-25
DONGHUA UNIV
View PDF8 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, tin protochloride is poisonous and harmful, and will pollute the environment; palladium salt belongs to noble metal, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making conductive fabric through polyaniline-triggered chemical slivering
  • Method for making conductive fabric through polyaniline-triggered chemical slivering
  • Method for making conductive fabric through polyaniline-triggered chemical slivering

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) prepare the mixed solution of aniline and protonic acid, wherein aniline 0.2mol / L, hydrochloric acid 0.4mol / L, put into fabric and soak for 40min, then add ammonium persulfate, make the ammonium persulfate concentration in the solution be 0.2mol / L, Polymerize for 2h, take out and wash with water.

[0032] (2) Prepare a silver nitrate solution with a concentration of 8g / L, dip the fabric with a layer of polyaniline at 20°C for 2 hours, take it out, wash it with water, and dry it in the air.

[0033] (3) First prepare silver ammonia solution: 10g / L AgNO 3 , add ammonia water dropwise until clarified; then prepare reducing solution: glucose 20g / L, tartaric acid 0.05g / L, ethanol 100mL / L, ethylenediamine 10mL / L.

[0034] Mix the silver ammonia solution and the reducing solution at a volume ratio of 1:2 to prepare an electroless silver plating solution. Immerse the fabric, perform chemical silver plating at 40°C, apply plating for 60 minutes, wash with water, and dry to...

Embodiment 2

[0040] (1) prepare the mixed solution of aniline and protonic acid, wherein aniline 0.3mol / L, hydrochloric acid 0.6mol / L, put into fabric dipping 30min, then add ammonium persulfate, make the ammonium persulfate concentration in the solution be 0.3mol / L, Polymerize for 2h, take out and wash with water.

[0041] (2) Prepare a silver nitrate solution with a concentration of 10 g / L, dip the fabric with a layer of polyaniline at 50° C. for 3 hours, take it out, wash it with water, and dry it in the air.

[0042] (3) First prepare silver ammonia solution: 10g / L AgNO 3 , add ammonia water dropwise until clarified; then prepare reducing solution: glucose 20g / L, tartaric acid 0.05g / L, ethanol 100mL / L, ethylenediamine 10mL / L.

[0043] Mix the silver ammonia solution and the reducing solution at a volume ratio of 1:3 to prepare an electroless silver plating solution. Immerse the fabric, perform chemical silver plating at 40°C, apply plating for 50 minutes, wash with water, and dry to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for making conductive fabric through polyaniline-triggered chemical slivering. Fabric is soaked in a mixed solution of aniline and protonic acid, ammonium persulfate is added to the mixed solution, a reaction is carried out for 2-10 hours, and then the processed fabric is obtained after washing; the processed fabric is soaked in a silver nitrate solution, washed, dried, and then soaked in a silvering solution for being silvered for 30-60 min at the temperature of 30-40 DEG C, then the processed fabric is washed and dried, and finally the conductive fabric is obtained. According to the method, the process conditions of sensitization and activation are omitted, polyaniline and silver nitrate replace stannous chloride and palladium chloride high in price, cost is lowered, and environment pollution is reduced. The conductive fabric obtained through the method is good in conductivity, the binding strength of metal and fabric is high, the electromagnetic shielding performance is excellent, and the conductive fabric has an antistatic function, an antibacterial function and the like.

Description

technical field [0001] The invention belongs to the field of preparation of conductive fabrics, in particular to a method for preparing conductive fabrics using polyaniline to trigger chemical silver plating. Background technique [0002] With the development of science and technology, electronic technology products have penetrated into all aspects of people's life and production. In order to improve the efficiency of use, the transmission power is often larger and larger, and the problem of electromagnetic radiation also follows. Anti-electromagnetic radiation fabrics are mainly Electromagnetic waves are shielded by reflection loss and absorption loss. The reflection method is mainly realized by the metal layer on the surface of the fabric, and the absorption method is mainly realized by high molecular conductive polymer. The processing method combining conductive polymers and metal conductive layers will be more advantageous. The conductive textiles prepared by this method...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/61D06M11/83D06M101/34D06M101/32D06M101/28D06M101/06D06M101/12D06M101/10
Inventor 俞丹穆世鹏饶竹君田魏成刘玲玲王炜
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com