Preparation method of foam ceramic of silicon nitride and silicon carbide combined with titanium carbide

A foamed ceramic and silicon carbide technology, applied in the fields of silicon carbide combined with titanium carbide foamed ceramics and silicon nitride, can solve the problems of low operating temperature, inability to meet the continuous casting of large special steel castings, poor thermal shock resistance, etc. Improved, light weight, excellent thermal shock resistance

Inactive Publication Date: 2015-01-28
SHANDONG UNIV OF TECH
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently used alumina foam ceramics and silicon carbide foam ceramics generally have problems such as low service temperature and poor thermal shock resistance, which cannot meet the needs of continuous casting of large special steel castings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Mix TiC, silicon micropowder, and phenolic resin in a ratio of 40:40:20 by weight and add 0.1wt% hydroxypropyl methylcellulose solution 40wt% to make a ceramic slurry, and then impregnate the ceramic slurry On the polyurethane foam, after drying, in a nitrogen atmosphere, the temperature is slowly raised at a temperature of 300°C to 1450°C for 20 hours, kept at a temperature of 1450°C for 5 hours, and then kept at a temperature of 1700°C for 20 minutes to form a combination of silicon nitride and silicon carbide. Titanium carbide foam ceramics.

[0011] The purity of the batching raw materials used in the experiment is industrial pure.

Embodiment 2

[0013] Mix TiC, silicon micropowder, and phenolic resin in a weight ratio of 60:25:15 and add 0.2wt% hydroxypropyl methylcellulose solution 50wt% to make a ceramic slurry, and then impregnate the ceramic slurry On the polyurethane foam, after drying, in a nitrogen atmosphere, the temperature is slowly raised at a temperature of 300°C to 1450°C for 60 hours, kept at 1450°C for 8 hours, and then kept at a temperature of 1730°C for 70 minutes to form a combination of silicon nitride and silicon carbide. Titanium carbide foam ceramics.

[0014] The purity of the batching raw materials used in the experiment is industrial pure.

Embodiment 3

[0016] Mix TiC, silicon micropowder, and phenolic resin in a weight ratio of 88:10:2 and add 0.3wt% hydroxypropyl methylcellulose solution 60wt% to make a ceramic slurry, and then impregnate the ceramic slurry On the polyurethane foam, after drying, in a nitrogen atmosphere, the temperature is slowly raised for 100 hours at a temperature of 300 ° C ~ 1450 ° C, kept at 1450 ° C for 10 hours, and then kept at a temperature of 1750 ° C for 120 minutes to form a combination of silicon nitride and silicon carbide. Titanium carbide foam ceramics.

[0017] The purity of the batching raw materials used in the experiment is industrial pure.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of foam ceramic of silicon nitride and silicon carbide combined with titanium carbide. The preparation method is characterized by comprising the following steps: uniformly mixing TiC, silicon micropowder, and phenolic resin in addition to a hydroxypropyl methyl cellulose solution to prepare ceramic slurry; then, impregnating polyurethane foam with the ceramic slurry; and drying and firing in a nitrogen atmosphere to obtain the foam ceramic of silicon nitride and silicon carbide combined with titanium carbide. The foam ceramic of silicon nitride and silicon carbide combined with titanium carbide provided by the invention is uniform in microstructure, high in strength and uniform in size of pore and avoids residues of carbon and free silicon, so that the strength, high-temperature resistance and heat impact resistance of the ceramic are greatly improved.

Description

technical field [0001] The invention relates to silicon nitride, silicon carbide and titanium carbide foam ceramics, belonging to the technical field of porous ceramic preparation. Background technique [0002] Silicon nitride, silicon carbide and titanium carbide composite ceramics are structural ceramic materials with low expansion, corrosion resistance, high strength and high temperature resistance. Silicon nitride, silicon carbide and titanium carbide foam ceramics are mainly used as molten steel filter elements in steel casting and other industries for large special steel castings. The currently used alumina foam ceramics and silicon carbide foam ceramics generally have problems such as low service temperature and poor thermal shock resistance, which cannot meet the needs of continuous casting of large special steel castings. Contents of the invention [0003] The object of the present invention is to provide a kind of preparation method of silicon nitride, silicon c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/06C04B35/56C04B35/622
Inventor 唐竹兴
Owner SHANDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com