Halogen-free flame-retardant environment-friendly covered polyolefin yarn fabric and preparation method thereof

A technology of polyolefin and covered yarn, which is applied in the field of fabrics to achieve the effects of increased air permeability, improved flame retardancy, high heat resistance and barrier properties

Inactive Publication Date: 2014-12-24
NINGBO XIANFENG NEW MATERIAL
View PDF16 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The present invention aims at the defects existing in the existing PVC substrate-coated yarn fabric products, and provides a polyolefin-coated yarn fabric which is halogen-free, flame-retardant, environmentally friendly and has excellent comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free flame-retardant environment-friendly covered polyolefin yarn fabric and preparation method thereof
  • Halogen-free flame-retardant environment-friendly covered polyolefin yarn fabric and preparation method thereof
  • Halogen-free flame-retardant environment-friendly covered polyolefin yarn fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Choose 220D polyester fiber.

[0064] According to the following parts by weight, the halogen-free flame-retardant environment-friendly polyolefin clad composite material is prepared:

[0065]HDPE: 50 parts

[0066] Ethylene-vinyl acetate copolymer: 8 parts

[0067] Halogen-free flame retardant: 20 parts

[0068] Zinc borate: 7 parts

[0069] Flame retardant synergist: 3 parts

[0070] Flow modifier: 10 parts

[0071] Compatibilizer: 3 parts

[0072] Lubricant: 1.5 parts

[0073] Anti-ultraviolet agent: 0.3 parts

[0074] Antioxidant: 0.3 parts

[0075] The compatibilizer is a maleic anhydride grafted high-density polyethylene copolymer, and the maleic anhydride grafting rate in the copolymer is 2%; the vinyl acetate content in the ethylene-vinyl acetate copolymer is 25%.

[0076] The above materials are mixed in a low mixer at 40-50°C for 5-10 minutes, and then put into a parallel co-rotating twin-screw machine for extrusion and granulation. The granulation te...

Embodiment 2

[0082] Choose 250D polyester fiber.

[0083] According to the following parts by weight, the halogen-free flame-retardant environment-friendly polyolefin clad composite material is prepared:

[0084] HDPE: 55 parts

[0085] Ethylene-vinyl acetate copolymer: 10 parts

[0086] Halogen-free flame retardant: 25 parts

[0087] Zinc borate: 6 parts

[0088] Flame retardant synergist: 3 parts

[0089] Flow modifier: 15 parts

[0090] Compatibilizer: 3 parts

[0091] Lubricant: 1.5 parts

[0092] Anti-ultraviolet agent: 0.3 parts

[0093] Antioxidant: 0.3 parts

[0094] The compatibilizer is a maleic anhydride grafted high-density polyethylene copolymer, and the maleic anhydride grafting rate in the copolymer is 2%; the vinyl acetate content in the ethylene-vinyl acetate copolymer is 30%.

[0095] According to the processing technology of Example 1, a halogen-free flame-retardant and environmentally friendly polyolefin covered yarn fabric was prepared, with the difference tha...

Embodiment 3

[0097] Choose 220D polyester fiber.

[0098] According to the following parts by weight, the halogen-free flame-retardant environment-friendly polyolefin clad composite material is prepared:

[0099] HDPE: 50 parts

[0100] Ethylene-vinyl acetate copolymer: 8 parts

[0101] Halogen-free flame retardant: 20 parts

[0102] Zinc borate: 7 parts

[0103] Flame retardant synergist: 5 parts

[0104] Flow modifier: 10 parts

[0105] Compatibilizer: 5 parts

[0106] Lubricant: 1.5 parts

[0107] Anti-ultraviolet agent: 0.3 parts

[0108] Antioxidant: 0.3 parts

[0109] The compatibilizer is ethylene-vinyl acetate copolymer grafted with maleic anhydride, and the grafting rate of maleic anhydride in the copolymer is 1.5%; the content of vinyl acetate in the ethylene-vinyl acetate copolymer is 25%.

[0110] Subsequent fabric preparation process is the same as in Example 1. The main physical properties of the obtained halogen-free flame-retardant and environmentally friendly pol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a halogen-free flame-retardant environment-friendly covered polyolefin yarn fabric and a preparation method thereof. The fabric is formed by weaving covered threads and has warp and weft structures; the covered threads comprise polyester fibers and halogen-free flame-retardant environment-friendly polyolefin composite materials covering the surfaces of the polyester fibers; the covered threads are 0.3-0.4 millimeter in diameter, rectangular or square gaps are reserved between the warp structures and the weft structures, and the aperture ratio is 2 to 10 percent; the halogen-free flame-retardant environment-friendly covered polyolefin yarn fabric is 0.55-0.75mm in total thickness and 350-420g / m<2>. The invention also provides a preparation method for the fabric. The fabric has the characteristics of sunshading, ultraviolet resistance, flame retardancy, high color fastness and the like of similar PVC (polyvinyl chloride) substrate fabrics, and also has the advantages of no halogen, environment friendliness, low smoke density during combustion, high self-cleaning property, high chemical stability, light weight, high air permeability and the like.

Description

technical field [0001] The invention relates to a fabric, in particular to a halogen-free flame-retardant and environment-friendly polyolefin coated yarn fabric and a preparation method thereof. Background technique [0002] Covered yarn fabric is a kind of fabric obtained by weaving fiber threads obtained by covering the surface of fibers (polyester, polypropylene, glass fiber, etc.) with plastic. At present, most of the fiber threads used in traditional covered yarn fabrics on the market are polyvinyl chloride (PVC) coated polyester fibers, which are mainly used in the building sunshade industry. PVC is a widely used general-purpose high-halogen polymer plastic with excellent processing performance. Its high halogen content makes it have good flame retardant performance, but its harm to the environment is also huge: halogen is soluble in water, in the air Combining with water vapor in the medium will form acid rain; in the process of injection molding or high temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D02G3/44D02G3/36D02G3/04D06C7/02C08L23/08C08L23/06C08K13/02D01F6/92D03D15/283D03D15/292D03D15/513
Inventor 熊圣东潘祥江俞月卫周乾坤张洪翔
Owner NINGBO XIANFENG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com