A kind of double network cross-linked epoxy resin and preparation method thereof

A technology of epoxy resin and double network, which is applied in the preparation of double network cross-linked epoxy resin and the field of double network cross-linked epoxy resin. Good combustion performance and the effect of inhibiting chain segment movement

Active Publication Date: 2016-09-14
ANHUI SHANFU NEW MATERIAL TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, simply introducing rigid groups into the molecular structure of epoxy resin, although the large-sized rigid groups can inhibit the thermal movement of molecules, the relatively loose cross-linking structure still limits the further improvement of heat resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of double network cross-linked epoxy resin and preparation method thereof
  • A kind of double network cross-linked epoxy resin and preparation method thereof
  • A kind of double network cross-linked epoxy resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Add 320 g of 5-amino-1-naphthol and 200 g of xylene into a 1000 mL four-necked flask equipped with a mechanical stirrer, a thermometer, a reflux condenser and a nitrogen introduction device, slowly raise the temperature of the oil bath to 125 ° C, and wait for 5- After amino-1-naphthol was completely dissolved, 240 g of maleimide was dissolved in 280 g of xylene, and slowly added dropwise to the reaction system. After 2 hours of addition, the reaction temperature was controlled at 125° C., and the reaction was continued for 6 hours. After completion of the reaction, cool down and distill off the solvent and excess water under reduced pressure to obtain a yellow semi-solid product. Add 140 g of the obtained yellow semi-solid product and 200 g of methyl isobutyl ketone into a 500 ml four-necked flask equipped with a mechanical stirrer, a thermometer, a reflux condenser and a nitrogen introduction device, react at 120 ° C for 8 h, cool and distill under reduced pressure to ...

Embodiment 2

[0026] Add 45 g of 5-amino-1-naphthol and 80 g of xylene into a 250 mL four-necked flask equipped with a mechanical stirrer, a thermometer, a reflux condenser, and a nitrogen introduction device, and slowly raise the temperature of the oil bath to 115° C., and wait for 5- After amino-1-naphthol was completely dissolved, 35 g of maleimide was dissolved in 80 g of xylene, and slowly added dropwise to the reaction system. After 2 hours of addition, the reaction temperature was controlled at 115° C., and the reaction was continued for 3 hours. After the reaction was completed, it was cooled and the solvent and excess water were distilled off under reduced pressure to obtain a yellow viscous product. Add 14 g of the obtained yellow viscous product and 20 g of methyl isobutyl ketone into a 100 ml four-necked flask equipped with a mechanical stirrer, a thermometer, a reflux condenser and a nitrogen introduction device, react at 120 ° C for 8 h, cool and distill under reduced pressure ...

Embodiment 3

[0029] Add 4500 g of 5-amino-1-naphthol and 8000 g of xylene in the 25L enamel reactor equipped with electric heating oil bath jacket, mechanical stirring, thermometer, reflux condenser and nitrogen gas introduction device, slowly raise the oil bath temperature to 125°C, after 5-amino-1-naphthol is completely dissolved, dissolve 3800 g of maleimide in 8000 g of xylene, and slowly add it dropwise to the reaction system. After 2 hours of feeding, the reaction temperature is controlled at 125°C, continue Reaction 2h. After the reaction was completed, it was cooled and the solvent and excess water were distilled off under reduced pressure to obtain a yellow viscous product. Add 1400g of the obtained yellow viscous product and 2000g of methyl isobutyl ketone into a 10L enamel reactor equipped with an electric heating oil bath jacket, mechanical stirring, thermometer, reflux condenser and nitrogen introduction device, and react at 120°C for 6h, then cool The solvent and excess wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a double network cross-linked epoxy resin, which uses maleimide and 5-amino-1-naphthol as main raw materials to synthesize 5-maleimide-1-naphthol, and then The resulting 5-maleimido-1-naphthol is reacted with paraformaldehyde, epichlorohydrin and sodium hydroxide to obtain a double network cross-linked epoxy resin. The obtained epoxy resin contains epoxy groups and maleimide groups, which can form double crosslinked networks of epoxy ring opening and imide polymerization during the crosslinking and curing process. The obtained cured product has excellent flame retardancy, It has good heat resistance and can be used as the matrix of high-performance composite materials used in high-temperature environments.

Description

technical field [0001] The invention belongs to the technical field of epoxy resins, and in particular relates to a double network cross-linked epoxy resin. At the same time, the invention also relates to a preparation method of the double network cross-linked epoxy resin. Background technique [0002] Epoxy resin is an important thermosetting resin and one of the most widely used materials in general polymer composite materials. Epoxy resin not only has good bonding properties, coating properties, mechanical properties, wear resistance and electrical insulation properties, but also has stable chemical properties, good corrosion resistance, good thermal stability, low shrinkage, and easy processing and molding , Low price. Epoxy resin is an important thermosetting resin with excellent adhesive properties, wear resistance, mechanical properties, electrical insulation properties, chemical stability, high and low temperature resistance, low shrinkage, easy processing and low ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G59/02
Inventor 任华包秀群叶琳张淑贞
Owner ANHUI SHANFU NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com