Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Waste glass-containing thermos bottle blank material

A waste glass and thermos bottle technology, applied in the field of glass materials, can solve the problems of not being able to adapt to the boiling water environment for a long time, poor thermal stability, and low mechanical strength, so as to accelerate the elimination of air bubbles, lower the melting temperature, and improve the quality of glass. Effect

Active Publication Date: 2014-09-10
济宁高新科达科技项目服务有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional thermos bottle preform is made of silicon dioxide as the main material and mixed with several oxides. The mechanical strength is not high, which makes it easier to break during use and transportation, resulting in waste of resources. Some thermal stability Not strong, unable to adapt to boiling water environment for a long time, not only easy to break, but also may damage personal safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A thermos bottle preform material made of waste glass, which is composed of the following raw materials in parts by weight (kg):

[0025] Waste glass 50, silica powder 30, calcite 15, potassium oxide 6, sodium phosphate 2, calcium oxide 6, lithium carbonate 4, aluminum oxide 3, zirconium oxide 2, aluminum carbonate 1, composite clarification aid 1;

[0026] Described composite clarification aid is made up of the following raw materials of weight part:

[0027] Fly ash 30, sodium carbonate 14, bone char 1, barium nitrate 7, 50% sulfuric acid 100, zinc oxide 0.8;

[0028] (1) After the fly ash is calcined at high temperature, the iron is removed, so that the component content in the selected fly ash is

[0029] 50%≤SiO2 2 ≤70%, 30%≤AL2O3≤40%, the balance is calcium oxide, magnesium oxide, sodium oxide, potassium oxide, etc.;

[0030] (2) Mix and grind the above-mentioned fly ash and sodium carbonate, put it into a muffle furnace for calcination at 850°C for 2 hours, ta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a waste glass-containing thermos bottle blank material. The waste glass-containing thermos bottle blank material comprises, by weight, 50-60 parts of waste glass, 20-30 parts of silica powder, 10-15 parts of calcite, 6-7 parts of potassium oxide, 2-3 parts of sodium phosphate, 5-6 parts of calcium oxide, 4-5 parts of lithium carbonate, 3-4 parts of alumina, 1-2 parts of zirconia, 1-2 parts of aluminum carbonate, and 1-2 parts of a compound clarifier aid. The utilization of cullet as a primary production material realizes the full use of municipal wastes and improves the environment; and the preheating of the cullet and the mixing of the preheated cullet with other materials greatly decrease the melting temperature of glass, improve the melting rate, reduce energy consumption, achieve a very good clarified effect, improve the quality of glass.

Description

technical field [0001] The invention mainly relates to a thermos bottle preform material made of waste glass, which belongs to the field of glass materials. Background technique [0002] The traditional thermos bottle preform is made of silicon dioxide as the main material and mixed with several oxides. The mechanical strength is not high, which makes it easier to break during use and transportation, resulting in waste of resources. Some thermal stability Not strong, unable to adapt to the boiling water environment for a long time, not only easy to break, but also may damage personal safety. Contents of the invention [0003] The purpose of the present invention is to provide a thermos bottle preform material made of waste glass. [0004] The present invention is achieved through the following technical solutions: [0005] A thermos bottle preform material made of waste glass, which is composed of the following raw materials in parts by weight: [0006] Waste glass 50-6...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/02C03C1/00
Inventor 薛宗洪
Owner 济宁高新科达科技项目服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com