Bicomponent silicofluoride acrylic polyurethane coating as well as preparation and application methods thereof

A technology of acrylic polyurethane and fluorine siliconization, which is applied in polyurea/polyurethane coatings, coatings, devices for coating liquid on surfaces, etc.

Active Publication Date: 2014-09-03
广东惠电科技发展有限公司
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to aim at the deficiencies of the prior art, to provide a two-component fluorosilicified acrylic polyurethane coating and its preparation and application method. Anti-aging, anti-scratch, anti-corrosion, anti-discoloration, anti-pollution and other characteristics, when used in conjunction with other excellent primers and primers, it can achieve excellent long-term protection performance on steel structures and long-term protection life up to 30 years

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bicomponent silicofluoride acrylic polyurethane coating as well as preparation and application methods thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] A two-component fluorosiliconized acrylic polyurethane coating of this embodiment includes component A and component B, and the mass ratio of component A to component B is 3:1;

[0085] Component A comprises the following raw materials in parts by weight:

[0086] Hydroxy acrylic resin 50 parts

[0087] Solvent 24 parts

[0088] Fluoride powder 1 part

[0089] Pigment 22 parts

[0090] High hardness oxide 1 part

[0091] Auxiliary 2 parts

[0092] Part B includes the following raw materials in parts by weight:

[0093] Blocked isocyanate curing agent 50 parts

[0094] Solvent 50 parts

[0095] Wherein, the hydroxyacrylic resin is a hydroxyacrylate copolymer with a solid content of 59% and a specific gravity of 0.95g / cm 3 , the viscosity is 5500cp (25°C), the acid value is 5mgKOH / g (100%), and the hydroxyl value is 53mgKOH / g.

[0096] Wherein, the solvent is dehydrated xylene, anhydrous butyl ester, ethylene glycol ethyl ether acetate, dimethyl nylonate, dimethy...

Embodiment 2

[0122] A two-component fluorosiliconized acrylic polyurethane coating of this embodiment comprises component A and component B, and the mass ratio of component A and component B is 3.5:1;

[0123] Component A comprises the following raw materials in parts by weight:

[0124] Hydroxy acrylic resin 55 parts

[0125] Solvent 20 parts

[0126] Fluoride powder 2 parts

[0127] Pigment 18 parts

[0128] High hardness oxide 3 parts

[0129] Auxiliary 2 parts

[0130] Part B includes the following raw materials in parts by weight:

[0131] 60 parts of blocked isocyanate curing agent

[0132] Solvent 40 parts

[0133] Wherein, the hydroxyacrylic resin is a hydroxyacrylate copolymer with a solid content of 60% and a specific gravity of 1 g / cm 3 , the viscosity is 5800cp (25°C), the acid value is 7mgKOH / g (100%), and the hydroxyl value is 54mgKOH / g.

[0134] Wherein, the solvent in the described component A and component B includes the following raw materials in weight percentag...

Embodiment 3

[0167] A two-component fluorosiliconized acrylic polyurethane coating of this embodiment comprises component A and component B, and the mass ratio of component A and component B is 4:1;

[0168] Component A comprises the following raw materials in parts by weight:

[0169] Hydroxy acrylic resin 60 parts

[0170] 18 parts of solvent

[0171] Fluorine-containing fine powder 0.5 parts

[0172] Pigment 15 parts

[0173] High hardness oxide 1.5 parts

[0174] Auxiliary 5 parts

[0175] Part B includes the following raw materials in parts by weight:

[0176] 65 parts of blocked isocyanate curing agent

[0177] Solvent 35 parts

[0178] Wherein, the hydroxyacrylic resin is a hydroxyacrylate copolymer with a solid content of 60% and a specific gravity of 1.01g / cm 3 , the viscosity is 6000cp (25°C), the acid value is 9mgKOH / g (100%), and the hydroxyl value is 55mgKOH / g.

[0179] Wherein, the solvent in the described component A and component B includes the following raw materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of protection coatings and in particular relates to a bicomponent silicofluoride acrylic polyurethane coating. The coating comprises a first component and a second component, wherein the mass ratio of the first component to the second component is (3 : 1) to (5 : 1); the first component comprises the following raw materials by weight parts: 50-70 parts of hydroxy acrylic resin, 15-24 parts of a solvent, 0.1-3 parts of fluorine-containing micropowder, 10-25 parts of a pigment, 1-3 parts of high-hardness oxide and 2-5 parts of aids; the second component comprises the following raw materials in parts by weight: 50-80 parts of a closed isocyanate curing agent and 20-50 parts of a solvent. According to the coating, the capability of protecting a steel structure can be improved; the coating has the characteristics of good ageing resistance, scratch resistance, corrosion prevention, color change prevention, pollution prevention and the like, and can achieve a very good long-acting protection effect on the steel structure by combination with other base paint and intermediate paint with excellent performance; and the protection life can be 30 years.

Description

Technical field [0001] The present invention involves the field of protective coating technology, especially a dual -component of fluorine siliconized acrylic polyurethane coatings. Background technique [0002] With the increasingly widespread application of steel structure, the protection of steel structure has also received more and more attention.At present, the study of anti -corrosion of steel structure engineering at home and abroad has done a lot of work, such as a high coatings with high corrosion fillers (such as zinc powder, cloud iron powder, aluminum powder) as a protective coating, or by corrosion corrosion.The primer and closed paint constitute a composite protective coating. These measures have a certain effect on the protection of the steel structure, but they also expose some problems.For example, when a layer of zinc -rich paint or high zinc paint is preserved to protect the steel structure, the surface treatment of the substrate is high, and the zinc -rich coa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04B05D7/14B05D3/12B05D3/02
Inventor 刘奖生李泳锋雷辉斌
Owner 广东惠电科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com