A kind of yttrium lithium fluoride nanocomposite material and its preparation method and application in photodynamic therapy

A nano-composite material and technology of the composite material are applied in the field of photosensitizer-coupled rare-earth doped yttrium-lithium fluoride nano-composite materials and their preparation, and can solve the problems of unfavorable wide application, low efficiency of nano-particle sensitizer photosensitizer, low yield and the like

Active Publication Date: 2016-04-27
FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the method of combining photosensitizers with nanomaterials is mainly to encapsulate photosensitizers with polymers or absorb photosensitizers with silica. Although the above methods can well couple photosensitizers with nanomaterials, the nanoparticles sensitize photosensitizers after coupling. The efficiency of the agent is low, and the method is complicated and the yield is low, which is not conducive to the wide application in the future

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of yttrium lithium fluoride nanocomposite material and its preparation method and application in photodynamic therapy
  • A kind of yttrium lithium fluoride nanocomposite material and its preparation method and application in photodynamic therapy
  • A kind of yttrium lithium fluoride nanocomposite material and its preparation method and application in photodynamic therapy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0085] Embodiment 1: ZnPc-COOH coupling 8-nmLiYF 4 : Preparation of 0.20Yb / 0.02Er Nanocrystals

[0086] First weigh 0.1430gCF 3 COOLi, 0.3860gY (CF 3 COO) 3 ,0.1132gYb(CF 3 COO) 3 and 0.0112gEr(CF 3 COO)3 To a three-hole flask, then add 8mL oleic acid and 6mL oleylamine solvent. Then pass in N 2 Under certain conditions, the temperature was raised to 100°C and kept for 10 minutes to dissolve the solid reactants until transparent, and then heated to 320°C for 1 hour. After cooling down to room temperature, add 20mL ethanol to precipitate, centrifuge, and wash to obtain 8nm oil-soluble LiYF 4 : 0.20Yb / 0.02Er nanocrystal. Disperse the nanocrystals in 15mL hydrochloric acid aqueous solution (0.1M) and sonicate for 15min, centrifuge to redisperse the obtained precipitate in dimethylformamide, add 3mgZnPc-COOH and stir for 1h, centrifuge to obtain the precipitate, disperse in water, add After 20mg of PVP was stirred overnight, the precipitate obtained by centrifugation was...

Embodiment 2

[0087] Embodiment 2: ZnPc-COOH coupling 25-nmLiYF 4 : Preparation of 0.20Yb / 0.02Er Nanocrystals

[0088] First weigh 0.1430gCF 3 COOLi, 0.3860gY (CF 3 COO) 3 ,0.1132gYb(CF 3 COO) 3 and 0.0112gEr(CF 3 COO) 3 To a three-hole flask, and then add 8mL oleic acid, 4mL oleylamine solvent. Then pass in N 2 Under certain conditions, the temperature was raised to 100°C and kept for 10 minutes to dissolve the solid reactants until transparent, and then heated to 320°C for 1 hour. After cooling down to room temperature, add 20mL ethanol to precipitate, centrifuge, and wash to obtain 20nm oil-soluble LiYF 4 : 0.20Yb / 0.02Er nanocrystal. Disperse the nanocrystals in 15mL hydrochloric acid aqueous solution (0.1M) and sonicate for 15min, centrifuge to redisperse the precipitate obtained in dimethylformamide, add 3mgZnPc-COOH and stir for 1h, then disperse the precipitate obtained by centrifugation in water, add 20mgPVP After stirring overnight, the precipitate obtained by centrifuga...

Embodiment 3

[0089] Embodiment 3: ZnPc-COOH coupling 50-nmLiYF 4 : Preparation of 0.20Yb / 0.02Er Nanocrystals

[0090] First weigh 0.1430gCF 3 COOLi, 0.3860gY (CF 3 COO) 3 ,0.1132gYb(CF 3 COO) 3 and 0.0112gEr(CF 3 COO) 3 To a three-hole flask, then add 8mL oleic acid and 2mL oleylamine solvent. Then pass in N 2 Under certain conditions, the temperature was raised to 100°C and kept for 10 minutes to dissolve the solid reactants until transparent, and then heated to 320°C for 1 hour. After cooling down to room temperature, add 20mL ethanol to precipitate, centrifuge, and wash to obtain 50nm oil-soluble LiYF 4 : 0.20Yb / 0.02Er nanocrystal. Disperse the nanocrystals in 15mL hydrochloric acid aqueous solution (0.1M) and sonicate for 15min, then redisperse the precipitate obtained by centrifugation in dimethylformamide, add 3mgZnPc-COOH and stir for 1h, centrifuge to disperse the precipitate in water, add 20mgPVP and stir After overnight, the precipitate obtained by centrifugation was w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a photosensitizer coupled rare earth-doped LiAF4 nanocomposite material, its preparation method, and its application in the photodynamic therapy. The above photosensitizer coupled nanomaterial emits strong visible light under the irradiation of 980nm laser, and can sensitize the photosensitizer to generate singlet oxygen, so the nanomaterial can be used in the up-conversion photodynamic therapy. The method has the advantages of simplicity and high yield, the prepared nanomaterial has the advantages of good water solubility, excellent luminescence performance and high singlet oxygen yield, and the singlet oxygen can well kill cancer cells, so the nanomaterial can be applied in the diagnosis and treatment field of tumor diseases.

Description

technical field [0001] The invention relates to the field of rare earth doped nanocomposite materials, in particular to a photosensitizer coupled rare earth doped yttrium lithium fluoride nanocomposite material, a preparation method thereof and an application in the field of photodynamic therapy. Background technique [0002] In recent years, rare earth-doped upconversion nanomaterials have made great progress in controllable preparation, optical properties, and biological applications, but their combination with traditional photosensitizers as a new generation of photodynamic therapy materials has not attracted people's attention until recent years. focus on. Compared with the traditional photosensitizer materials excited by ultraviolet-visible light, due to the influence of the penetration depth of the excitation light source, they are greatly limited in the photodynamic therapy of some related tumors. The near-infrared-excited upconversion luminescent material combined w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/85A61K41/00A61P35/00
Inventor 陈学元王蒙陈卓郑伟
Owner FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap