A kind of internalization of lead calcium into colloidal electrolyte

A colloidal electrolyte, internalization technology, applied in the direction of lead-acid batteries, electrolyte immobilization/gelation, etc., can solve the problems of capacity attenuation, short deep cycle life, softening and falling off of positive active materials, etc., to slow down softening and falling off, Improve the service life of deep cycle and improve the effect of initial capacity fading effect

Active Publication Date: 2016-04-06
江苏海宝电池科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the above-mentioned problems of lead-calcium internalization battery capacity decay in the initial stage (the first 50 cycles), the positive active material softens and falls off, and the deep cycle life is short, the present invention provides a long-life lead-calcium internalization colloidal electrolyte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of lead calcium internalized into a colloidal electrolyte, the weight percentage of each component is: meteorological silica: 1.5%, sodium silicate: 0.5%, anhydrous sodium sulfate: 1.5%, stannous sulfate: 0.1%, carboxymethyl Sodium cellulose (CMC): 0.08%, bismuth trioxide: 0.1%, phosphoric acid: 0.8%, sulfuric acid: 34%, and the rest is water.

Embodiment 2

[0021] A kind of lead calcium internalized into a colloidal electrolyte, the weight percentage of each component is: meteorological silica: 0.8%, sodium silicate: 1.5%, anhydrous sodium sulfate: 1.2%, stannous sulfate: 0.15%, carboxymethyl Sodium cellulose (CMC): 0.1%, bismuth trioxide: 0.2%, phosphoric acid: 0.8%, sulfuric acid: 34%, and the rest is water.

Embodiment 3

[0023] A kind of lead calcium internalized into a colloidal electrolyte, the weight percentage of each component is: meteorological silica: 3.5%, sodium silicate: 1.3%, anhydrous sodium sulfate: 1.8%, stannous sulfate: 0.2%, carboxymethyl Sodium cellulose (CMC): 0.05%, bismuth trioxide: 0.3%, phosphoric acid: 0.8%, sulfuric acid: 35.5%, and the rest is water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a lead-calcium formation colloid electrolyte which is composed of the following components in percentage by weight: 0.8-5% of gas-phase silicon dioxide, 0.1-2% of sodium silicate, 1-2% of anhydrous sodium sulfate, 0.1-0.5% of stannous sulfate, 0.05-0.5% of sodium carboxymethyl cellulose, 0.02-0.5% of bismuth trioxide, 0.2-3% of phosphoric acid, 28-38% of sulfuric acid and the balance of water. When being used for preparing a lead-calcium formation battery, the colloid electrolyte improves the early capacity attenuation effect of the lead-calcium formation battery, decelerates the softening shedding of the active substances at the positive pole, and prolongs the deep cycle service life of the battery.

Description

technical field [0001] The invention relates to a colloidal electrolytic solution formed by internalizing lead and calcium. Background technique [0002] Since the country canceled the production of lead-antimony-cadmium lead-acid batteries at the end of 2013, most lead-acid battery manufacturers have changed from lead-antimony-cadmium externalization to lead-calcium internalization batteries to comply with the requirements of national policies. Although the lead-calcium battery overcomes the problem of fast grid corrosion in the lead-antimony-cadmium battery, it also has the disadvantages of rapid initial (first 50 cycles) capacity decay, short life, and easy softening and falling off of the active material, especially when the battery is deep Discharge, prompting a sharp decline in battery life. Therefore, it is necessary to provide a new technical solution to solve the above problems. Contents of the invention [0003] In order to solve the problems of capacity decay ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/08
CPCH01M10/10H01M2300/0085Y02E60/10
Inventor 沈维新
Owner 江苏海宝电池科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap