Electrode plate solidification technology for lead-acid battery

A lead-acid battery and electrode plate curing technology, used in lead-acid battery electrodes, electrode manufacturing, electrode heat treatment, etc., can solve problems such as low service life, and achieve the effect of improving floating charge life and high initial capacity.

Active Publication Date: 2014-07-23
CHAOWEI POWER CO LTD
View PDF7 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to provide a battery that is suitable for charging and discharging cycles at various ambient temperatures and has a high cycle life for lead-acid batteries in order to solve the defects of early attenuation and low service life of the existing lead-acid batteries for communication. plate curing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of pole plate curing process suitable for lead-acid batteries, the curing process includes a moisturizing stage, a heat preservation curing stage and a drying stage; wherein, the relative humidity of the moisturizing stage is 98-100%; the moisturizing stage includes the following steps: temperature 40 ℃, relative Humidity 98-100%, curing time 12h; temperature 75°C, relative humidity 98-100%, curing time 12h;

[0027] The heat preservation and curing stage includes the following steps: 1) The temperature is 50°C, the relative humidity is 90%, the curing time is 10 hours, and water vapor containing 0.1% ozone is introduced;

[0028] 2) The temperature is 50°C, the relative humidity is 80%, the curing time is 6 hours, and the water vapor with a mass fraction of 0.3% ozone is introduced;

[0029] 3) The temperature is 50°C, the relative humidity is 70%, the curing time is 8 hours, and the water vapor with a mass fraction of 0.5% ozone is introduced;

[0030] In the ...

Embodiment 2

[0034] A kind of plate curing process suitable for lead-acid batteries, said curing process includes a moisturizing stage, a heat preservation curing stage and a drying stage; wherein, the relative humidity of the moisturizing stage is 98-100%; the moisturizing stage includes the following steps: temperature 42 ℃, relative Humidity 98-100%, curing time 12h; temperature 80 ℃, relative humidity 98-100%, curing time 12h;

[0035] The heat preservation and curing stage includes the following steps: 1) The temperature is 53°C, the relative humidity is 90%, the curing time is 11 hours, and water vapor containing 0.1% ozone is introduced;

[0036] 2) The temperature is 52°C, the relative humidity is 80%, the curing time is 7 hours, and the water vapor with a mass fraction of 0.5% ozone is introduced;

[0037] 3) The temperature is 52°C, the relative humidity is 70%, the curing time is 9h, and the water vapor with a mass fraction of 0.15% ozone is introduced;

[0038] In the drying s...

Embodiment 3

[0042] A kind of plate curing process suitable for lead-acid batteries, the curing process includes a moisturizing stage, a heat preservation curing stage and a drying stage; wherein, the relative humidity of the moisturizing stage is 98-100%; the moisturizing stage includes the following steps: temperature 45 ℃, relative Humidity 98-100%, curing time 12h; temperature 85℃, relative humidity 98-100%, curing time 12h;

[0043] The heat preservation and curing stage includes the following steps: 1) The temperature is 54°C, the relative humidity is 90%, the curing time is 12 hours, and water vapor containing 0.5% ozone is introduced;

[0044] 2) The temperature is 54°C, the relative humidity is 80%, the curing time is 8h, and the water vapor containing 0.25% ozone is passed through;

[0045] 3) The temperature is 54°C, the relative humidity is 70%, the curing time is 10h, and the water vapor with a mass fraction of 0.5% ozone is introduced;

[0046] In the drying stage, the tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an electrode plate solidification technology for lead-acid battery. The solidification technology comprises a moisture retention phase, a thermal insulation solidification phase, and a drying phase. In the moisture retention phase, a low-temperature solidification treatment is carried out at first, the temperature in the low-temperature solidification treatment is 40 to 45 DEG C, then a high-temperature solidification treatment is carried out, and the temperature in the high temperature solidification treatment is 75 to 85 DEG C. In the thermal insulation solidification phase, the relative humidity is gradually reduced during the solidification process. Electrode plates that are produced through the solidification technology are assembled into batteries. The floating charging resistant performance of the battery is prominently improved, and thus the service life of the battery is prolonged. The primary capacity of the battery is large, and the service life is 5 years or more. The electrode plate solidification technology is an ideal solidification mode for lead-acid battery for communication.

Description

technical field [0001] The invention relates to the field of accumulators, in particular to a curing process for polar plates suitable for lead-acid accumulators which improves the service life of the lead-acid accumulators. [0002] Background technique [0003] Lead-acid battery (Lead-acid battery) electrodes are mainly made of lead and its oxides, and the electrolyte is a battery of sulfuric acid solution. Since the French G.Plante invented the lead-acid battery in 1859, it has experienced nearly 150 years of development. Great progress has been made, whether it is in transportation, communication, electric power, military or in various economic fields of navigation and aviation, lead-acid batteries have played an indispensable and important role. In recent years, with the acceleration of urbanization and the expansion of city limits, the traffic flow has increased dramatically. Although automobiles and other means of transportation are developing rapidly, due to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/20H01M4/21
CPCH01M4/0471H01M4/20H01M4/21Y02E60/10
Inventor 杨绍坡张森
Owner CHAOWEI POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com