Winter paste mixing process for container formation battery plate

A battery plate, internalization technology, applied in battery electrodes, lead-acid batteries, lead-acid battery construction, etc., can solve the problem of unstable performance of lead paste, and achieve the effect of good initial capacity and long life

Active Publication Date: 2014-07-23
CHAOWEI POWER CO LTD
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problem of unstable performance of the prepared lead paste due to the neglect of environmental factors in the current internalized battery plate paste process, and to provide a winter paste process for internally formed battery plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of internalization into battery polar plate winter paste process, specifically comprises the following steps:

[0028] 1) Material preparation: according to the formula, add the corresponding materials to the lead powder metering bucket, sulfuric acid metering barrel, and water metering barrel respectively; the specific gravity of the sulfuric acid used at 25°C is 1.35-1.45g / cm 3 , the water level is deionized water.

[0029] 2) Adding lead: First, add the auxiliary materials measured according to the formula into the paste pot, then add the measured lead powder into the paste pot during continuous stirring, and continue to dry mix for 8 minutes after adding the lead powder;

[0030] 3) Add water: Then, add measured water into the paste pot during the continuous stirring process, and the adding process lasts for 2 minutes. When ≤20°C, preheat the temperature of the water to 50°C;

[0031] 4) Adding acid: Add the measured sulfuric acid evenly into the paste pot ...

Embodiment 2

[0034] A kind of internalization into battery polar plate winter paste process, specifically comprises the following steps:

[0035] 1) Material preparation: according to the formula, add the corresponding materials to the lead powder metering bucket, sulfuric acid metering barrel, and water metering barrel respectively; the specific gravity of the sulfuric acid used at 25°C is 1.35-1.45g / cm 3 , the water level is deionized water.

[0036] 2) Adding lead: First, add the auxiliary materials measured according to the formula into the paste pot, then add the measured lead powder into the paste pot during continuous stirring, and continue to dry mix for 10 minutes after adding the lead powder;

[0037] 3) Add water: Then, add measured water into the mixing paste pot during the continuous stirring process, and the adding process lasts for 1 minute, add water and then stir for 7 minutes, and add all the water according to the amount of water used, when the ambient temperature When ...

Embodiment 3

[0041] A kind of internalization into battery polar plate winter paste process, specifically comprises the following steps:

[0042] 1) Material preparation: according to the formula, add the corresponding materials to the lead powder metering bucket, sulfuric acid metering barrel, and water metering barrel respectively; the specific gravity of the sulfuric acid used at 25°C is 1.35-1.45g / cm 3 , the water level is deionized water.

[0043] 2) Adding lead: First, add the auxiliary materials measured according to the formula into the mixing paste pot, then add the measured lead powder into the mixing paste pot during the continuous stirring process, and continue to dry mix for 9 minutes after adding the lead powder;

[0044] 3) Add water: Then, add measured water into the paste pot during the continuous stirring process, and the adding process lasts for 1-2 minutes, add water and then stir for 6 minutes, and add all the water according to the amount of water used, when When the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the lead battery manufacturing field, in particular to a winter paste mixing process for a container formation battery plate. The process specifically includes the steps of: adding corresponding materials into a lead powder measuring hopper, a sulfuric acid measuring barrel and a water measuring barrel respectively according to the formula measurement; adding auxiliary materials into a paste mixing pot according to the formula measurement, then adding well measured lead powder into the paste mixing pot during continuous stirring, then further conducting dry stirring for 8-10min; adding water into the paste mixing pot in the continuous stirring process, and keeping the adding process duration at 1-2min, then conducting stirring for another 5-7min, adding all the water according to a use amount, and when the environment temperature is lower than or equal to 20DEG C, pre-heating the water to 30-50DEG C; adding well measured acid into the paste mixing pot in the continuous stirring process, and keeping the adding process last for 13-15min, and when the environmental temperature is lower than or equal to 20DEG C, pre-heating sulfuric acid to 20-40DEG C; at the same time controlling the temperature in the paste mixing pot lower than or equal to 60DEG C; at the end of acid adding, further conducting stirring for 10-25min, testing the diachylon apparent density, and discharging the diachylon from the pot when the apparent density reaches the standard.

Description

technical field [0001] The invention relates to the field of lead battery manufacturing, and specifically relates to a process of internalizing battery pole plates and mixing paste in winter. Background technique [0002] Lead paste is the matrix of the active material of the pole plate. It is a paste-like substance with certain plasticity formed by mechanical stirring and mixing of lead powder with a certain degree of oxidation and apparent density, water and sulfuric acid solution. The role of lead paste in lead-acid batteries is mainly to provide and store the substances required for electrochemical reactions. Lead paste is a plastic substance mixed with lead powder, water, sulfuric acid and additives. Its properties are mainly manifested in the apparent density and consistency of lead paste. Therefore, the prepared lead paste should have good plasticity, so that the lead paste can be easily bonded to the grid when coating the board, and can be evenly coated and filled w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M10/12
CPCH01M4/57H01M10/12Y02E60/10Y02P70/50
Inventor 张森
Owner CHAOWEI POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com