UV (Ultraviolet) cured primer having flame-retarding effect and preparation method thereof

A nano-silica, raw material technology, applied in the direction of fire-resistant coatings, coatings, etc., can solve the problems of poor adhesion and impact resistance, reduce production costs, poor coating flexibility, etc., achieve good sandability, good flame retardant Effect, good adhesion effect

Inactive Publication Date: 2014-06-04
WUHU EDISON AUTOMATION EQUIP
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current UV curing materials are various, but there are still some problems to varying degrees. The existing UV curing coatings have a large shrinkage rate after photocuring and produce shrinkage stress, resulting in brittleness of the coating film, adhesion and impact resistance. Poor, poor flexibility and low hardness of the coating film, no corrosion resistance, easy yellowing and aging, etc. These series of problems need to be continuously improved for different purposes, reduce production costs, and expand uses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] specific implementation plan

[0014] The present invention will be described in detail below through specific examples.

[0015] A UV curable primer with flame retardant effect, prepared from the following raw materials in parts by weight (kg): acrylic resin 50, N-acryloylmorpholine 8, acrylate-2-hydroxyethyl ester 7, 1-hydroxy ring Hexyl phenyl ketone 4, ethylene glycol ether 11, allyl glycidyl ether 9, methyl ethyl ketone 3, benzyltrimethylammonium tribromide 1, polydimethylsiloxane 1, brown corundum powder 5 , aluminum hydroxide 3, auxiliary agent 4;

[0016] The auxiliary agent is made of the following raw materials in parts by weight (kg): barite 10, bamboo charcoal 5, nano silicon dioxide 5, epoxy soybean oil 1, lemon essential oil 0.1, lauric acid methacrylate 4, acrylic acid Hydroxyethyl ester 3, silane coupling agent KH560 2, hydroxyethyl methacrylate 20; the preparation method is to put barite in a calciner and calcinate at 520-540°C for 3-4 hours, take it ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a UV (Ultraviolet) cured primer having a flame-retarding effect. The UV cured primer is characterized by being prepared from the following raw materials in parts by weight: 50-55 parts of acrylic resin, 8-11 parts of N-acryloylmorpholine, 7-10 parts of 2-hydroxyethyl acrylate, 4-6 parts of 1-hydroxycyclohexyl phenyl ketone, 11-13 parts of glycol ether, 9-10 parts of allyl glycidyl ether, 3-5 parts of butanone, 1-2 parts of benzyltrimethylammonium tribromide, 1-2 parts of polydimethylsiloxane, 5-7 parts of brown fused alumina powder, 3-4 parts of aluminum hydroxide and 4-5 parts of aid. The coating is added with the aluminum hydroxide, so that a good flame-retarding effect is achieved; the aid is added, so that high levelling property, uniform coating, good coating of devices, excellent airtightness and high rubbing property are realized. The prepared coating has excellent water resistance, hot water resistance, drug resistance, bonding property and toughness, and is suitable to be taken as a primer.

Description

technical field [0001] The invention relates to a coating and a preparation method thereof, in particular to a UV curable primer with a flame-retardant effect and a preparation method thereof. Background technique [0002] UV curing coatings have become a relatively mature technology, especially with the improvement of people's awareness of environmental protection, production and researchers pay more attention to the development and application of UV curing coatings. UV curing coating is a kind of green and environment-friendly coating, which fully complies with the "4E" principle. Generally, the energy consumption of UV curing is 1 / 5 of that of thermal curing, and UV curing coating contains less volatile components and less pollution. It is most attractive to researchers. And the developer's advantage is that UV curing coatings can reduce raw material consumption, which is beneficial to reduce economic costs. [0003] The current UV curing materials are various, but there...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/02C09D4/06C09D5/18C09D7/12
Inventor 汤广顺
Owner WUHU EDISON AUTOMATION EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products