Chassis armored coating and preparation method thereof

An armor and coating technology, applied in anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., to achieve the effects of good weather resistance, good adhesion and low thermal conductivity

Active Publication Date: 2014-05-21
QINGDAO AIR NEW MATERIALS
View PDF6 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of this invention is to provide a kind of chassis armor coating and preparation method thereof, to solve the problems existing in the above-mentioned existing bituminous coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chassis armored coating and preparation method thereof
  • Chassis armored coating and preparation method thereof
  • Chassis armored coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The preparation technology in the embodiment of the present invention is as follows:

[0034] (1) Preparation of aqueous mixture:

[0035] At room temperature, mix water-based emulsion, 1 / 2 of water, 1 / 2 of defoamer, all antifreeze, wetting agent, dispersant, preservative, antifungal agent, flame retardant, and rust inhibitor according to weight Mix evenly, then add thixotropic agent and paint film anti-cracking agent in turn and stir evenly to obtain an aqueous mixed solution.

[0036] 2) Filler addition and paint mixing:

[0037] Add all functional fillers, film-forming aids, and 1 / 2 defoamer to the above-mentioned aqueous mixture according to the weight ratio, stir and mix at a high speed, then add the remaining 1 / 2 of water, and finally add an appropriate amount of thickener Adjust viscosity. Among them, the order of antifreeze, flame retardant, and rust inhibitor can be interchanged, otherwise it will cause demulsification and gel phenomenon.

Embodiment 1

[0040] A kind of chassis armor coating of the present embodiment, with aqueous emulsion as main agent; With expanded perlite, expanded vermiculite, talcum powder, kaolin, calcium carbonate, flaky mica powder, hollow microspheres as functional filler; Silicon is used as a thixotropic agent; wood fiber is used as an anti-cracking agent for the paint film; and an appropriate amount of halogen-free environmentally friendly flame retardant aluminum hydroxide, dispersant, wetting agent, anti-corrosion and anti-mold agent, rust inhibitor, flame retardant, etc. are added Various additives for water-based coatings, the main components are proportioned according to the following weight ratio: 30 parts of water-based pure acrylic emulsion; 15 parts of mica powder, 10 parts of hollow glass microspheres, 10 parts of kaolin, 10 parts of calcium carbonate; 1.0 parts of thixotropic 0.5 parts of anti-cracking agent; 5 parts of halogen-free environmentally friendly flame retardant; 5 parts of co...

Embodiment 2

[0050]A kind of chassis armor coating of the present embodiment, with aqueous emulsion as main agent; With expanded perlite, expanded vermiculite, talcum powder, kaolin, calcium carbonate, flaky mica powder, hollow microspheres as functional filler; Silicon is used as a thixotropic agent; wood fiber is used as an anti-cracking agent for the paint film; and an appropriate amount of halogen-free environmentally friendly flame retardant aluminum hydroxide, dispersant, wetting agent, anti-corrosion and anti-mold agent, rust inhibitor, flame retardant, etc. are added Various additives for water-based coatings, the main components are proportioned according to the following weight ratio: 20 parts of water-based pure acrylic emulsion, 20 parts of styrene-acrylic emulsion; 10 parts of mica powder, 5 parts of hollow glass microspheres, 10 parts of expanded perlite, 10 parts 0.5 parts of thixotropic agent; 0.8 parts of anti-cracking agent; 10 parts of halogen-free environmental protectio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
solid contentaaaaaaaaaa
Login to View More

Abstract

The invention discloses a chassis armored coating. The chassis armored coating comprises the following main components in parts by weight: 30-50 parts of waterborne emulsion, 37-60 parts of functional filler, 5-15 parts of coalescing agent, 0.5-1.0 part of dispersant, 0.5-1.5 parts of wetting agent, 0.5-1.0 part of antiseptic mildewproof agent, 0.5-1.0 part of defoaming agent, 0.5-1.0 part of anti-rust agent, 5-20 parts of flame retardant, 0.5-1.0 part of thixotropic agent, 0.5-1.0 of anti-cracking agent, 0.5-1.0 part of thickening agent, 2.0-5.0 parts of antifreeze and 5-15 parts of water. The invention aslo discloses a preparation method of the chassis armored coating. The chassis armored coating uses the water as a dispersion medium, is safe and environmentally-friendly and has excellent corrosion resistance and good solvent resistance and machine oil resistance; a paint film formed by the chassis armored coating has low coefficient of heat conductivity and good thermal insulation property; when the dry film is 2mm, the sound insulation property can reach 30dB.

Description

technical field [0001] The invention relates to the field of vehicle protective coatings, in particular to a chassis armor coating used for vehicle chassis and a preparation method thereof. Background technique [0002] Chassis armor can effectively protect the vehicle chassis from being hit by road sand and gravel, prevent slight dragging friction; prevent acid, alkali, and salt from corroding the chassis iron plate; prevent chassis screws from loosening; reduce noise transmission during driving, increase Driving tranquility; preventing the heat conduction of the chassis iron plate, so that the cab is warm in winter and cool in summer. At present, the chassis armor on the market is mainly various asphalt coatings. Although asphalt coatings have excellent anti-corrosion properties, their shortcomings are also obvious. The main manifestations are: (1) Asphalt is easy to drip when the temperature of the bottom of the vehicle is high in summer. Harmful gas infiltrates into the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D125/14C09D133/04C09D183/04C09D175/04C09D7/12C09D5/08
Inventor 郭焱矫伟李永岗王桂刚王伟
Owner QINGDAO AIR NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com