A kind of modified fluorine rubber compound and preparation method thereof

A technology for modifying fluororubber and mixing rubber, applied in the field of material science and engineering, can solve the problems of complex synthesis process of perfluoroether rubber, inability to meet requirements and high production cost, and achieve excellent resistance to alcohol fuel and chemical media, Reduced low temperature performance, affordable effect

Active Publication Date: 2015-12-02
ZHONGHAO CHENGUANG RES INST OF CHEMICALINDUSTRY CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the complexity of the synthesis process of perfluoroether rubber and the high production cost, how to prepare perfluoroether rubber with excellent properties such as high heat resistance, cold resistance, low permeability and fuel resistance has long been a problem in our country. A technical problem for R&D personnel in related technical fields
At present, the technology of perfluoroether rubber in our country has not yet been overcome, and it can only be satisfied by imports, and the price is quite expensive, so it cannot replace the existing ordinary fluororubber varieties.
The adjustment of the formula can not meet the requirements. Because of this, on the basis of ensuring excellent physical properties and processing performance, the low temperature and alcohol fuel oil of the rubber compound can be improved by adjusting the raw rubber in the fluorine compound rubber and the formula system. , chemical properties, to meet the needs of all walks of life is extremely necessary

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified fluorine rubber compound and preparation method thereof
  • A kind of modified fluorine rubber compound and preparation method thereof
  • A kind of modified fluorine rubber compound and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Preparation of Embodiment 1 Fluorine Rubber Compound (1)

[0044] The formulation of fluororubber compound with low temperature resistance and chemical medium is as follows.

[0045] Modified binary fluororubber (REM260) 100

[0046] Magnesium Oxide 4

[0047] calcium hydroxide 5

[0048] Carbon black filler 20

[0049] Calcium Fluoride 10

[0050] Release agent 1.5

[0051] Bisphenol AF2.0

[0052] Benzyl triphenyl phosphorus chloride 0.4

[0053] Modified diatomaceous earth 5

[0054] dual 2.51.0

[0055] TAIC2.0

[0056] The above-mentioned release agent is WS280.

[0057] The above-mentioned modified diatomite is obtained by physically treating diatomite and silica with an aminosilane coupling agent containing four functional groups.

Embodiment 2

[0058] Preparation of embodiment 2 fluorine rubber compound (2)

[0059] The formulation of fluororubber compound with low temperature resistance and chemical medium is as follows.

[0060] Modified binary fluororubber (REM260) 100

[0061] Magnesium Oxide 6

[0062] calcium hydroxide 7

[0063] Carbon black filler 25

[0064] Calcium Fluoride 20

[0065] Release Agent 2.0

[0066] Bisphenol AF2.2

[0067] Benzyl triphenyl phosphorus chloride 0.5

[0068] Modified diatomaceous earth 7

[0069] Dual 2.51.2

[0070] TAIC2.4

[0071] The above-mentioned release agent is Rhine Powder

[0072] The above-mentioned modified diatomite is obtained by physical treatment of diatomite and silica powder through aminosilane coupling agent containing four functional groups.

Embodiment 3

[0073] Preparation of Embodiment 3 Fluorine Rubber Compound (3)

[0074] The formulation of fluororubber compound with low temperature resistance and chemical medium is as follows.

[0075] Modified binary fluororubber (REM260) 100

[0076] Magnesium oxide 7

[0077] calcium hydroxide 8

[0078] Carbon black filler 30

[0079] Calcium Fluoride 30

[0080] Release agent 3.0

[0081] Bisphenol AF2.5

[0082] Benzyl triphenyl phosphorus chloride 0.6

[0083] Modified diatomaceous earth 7

[0084] double 2.51.5

[0085] TAIC2.8

[0086] The above mold release agent is obtained by mixing Rhine powder and WS280 in 1:1 parts by weight.

[0087] The above-mentioned modified diatomite is obtained by physical treatment of silica and silica powder through aminosilane coupling agent containing four functional groups.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
specific surface areaaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention provides a modified fluororubber rubber compound and a preparation method thereof. The fluororubber takes modified binary fluororubber as a raw material; meanwhile, two vulcanization agent manners including a bisphenol vulcanization system and a peroxide vulcanization system are combined to carry out vulcanization; an auxiliary agent is increased and matched, and is mixed with the material to prepare the modified fluororubber rubber compound. The modified fluororubber rubber compound has excellent high heat resistance, cold resistance, low permeability and fuel oil resistance, and is applicable to industries including aerospace, aviation, cars, metallurgy, petrochemical engineering, electronics and the like; the performance on a sealing application is not too low and a problem caused by that an application environment is changed is not caused; the modified fluororubber rubber compound can be used as the first choice of a sealing material.

Description

technical field [0001] The invention relates to the technical field of material science and engineering, in particular to an improved fluorine rubber compound with low temperature resistance and chemical substances and a preparation method thereof. Background technique [0002] Fluorine rubber is a new type of polymer material, which has excellent heat resistance, medium resistance and oil resistance, as well as good physical and mechanical properties, electrical insulation and radiation resistance, etc., known as the "King of Rubber". [0003] 60-70% of fluorine rubber is used in the automobile industry. Nowadays, with the development of light weight, high performance and low fuel consumption of automobiles, green fuels containing alcohol and ether are widely used in automobiles, and the emission standards of motor vehicles are continuously improved. The demand for high-performance fluorine compounds is strong. However, due to the limitation of existing materials in the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/12C08K13/06C08K9/00C08K3/34C08K3/22C08K3/04C08K5/13C08K5/14C08K3/16C08J3/24
Inventor 邢华艳张建新刘斌
Owner ZHONGHAO CHENGUANG RES INST OF CHEMICALINDUSTRY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com